Neutron absorbing article and method for manufacture thereof
Assignee: Standard Oil Co
•
Filing: 1978-01-17
•
Granted: 1980-08-19
•
Expires: 1998-01-17
Abstract
Abstract A composite, neutron absorbing, coated article, suitable for installation in storage racks for spent nuclear fuel and for other neutron absorbing applications, includes a backing member, preferably of flexible material such as woven fiberglass cloth, a synthetic organic polymeric coating or a plurality of such coatings on the backing member, preferably of cured phenolic resin, such as phenol formaldehyde or trimethylolphenol formaldehyde and boron carbide particles held to the backing member by the cured coating or a plurality of such coatings. Also within the invention is a method for the manufacture of the neutron absorbing coated article and the use of such an article. In a preferred method the backing member is first coated on both sides thereof with a filling coating of thermosettable liquid phenolic resin, which is then partially cured to solid state, one side of the backing member is then coated with a mixture of thermosettable liquid resin and finely divided boron carbide particles and the resin is partially cured to solid state, the other side is coated with a similar mixture, larger boron carbide particles are applied to it and the resin is partially cured to solid state, such side of the article is coated with thermosettable liquid phenolic resin, the resin is partially cured to solid state and such resin, including previously applied partially cured resins, is cured to final cross-linked and permanently set form.
Inventors
- 👤 Carl H. McMurtry
- 👤 Robert G. Naum
- 👤 Paul F. Forsyth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:31
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/88; B29C70/02; B29C70/021; B29C70/025; G; G21; G21F; G21F1/00; G21F1/12
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
109 words
A composite, neutron absorbing, coated article comprising a backing member of woven fiberglass cloth, a trimethylol phenol formaldehyde polymer coating or a plurality of such coatings on said cloth and boron carbide particles held to said backing member by said coating or plurality of said coatings, which boron carbide particles are partially uncoated by said coating or coatings and project past said coating or coatings in a direction or directions opposite to that or those of the backing member and are of sizes in the No. 60 to 400 sieve range and in which article the B 10 loading is in the range of 0.001 to 0.1 g./sq. cm.
Claim 2
Dependent Claim
109 words
A composite, neutron absorbing, coated article comprising a backing member of woven fiberglass cloth, a trimethylol phenol formaldehyde polymer coating or a plurality of such coatings on said cloth and boron carbide particles held to said backing member by said coating or plurality of said coatings, which boron carbide particles are partially uncoated by said coating or coatings and project past said coating or coatings in a direction or directions opposite to that or those of the backing member and are of sizes in the No. 60 to 400 sieve range and in which article the B 10 loading is in the range of 0.001 to 0.1 g./sq. cm.
Claim 3
Dependent Claim
85 words
A composite, neutron absorbing, coated article comprising a backing member having a coating on one side thereof of phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 60 to 400 sieve range and held to the backing member by such polymer and on the other side having a coating of phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 170 to 400 sieve range and held to the backing member by such polymer.
Claim 4
Dependent Claim
85 words
A composite, neutron absorbing, coated article comprising a backing member having a coating on one side thereof of phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 60 to 400 sieve range and held to the backing member by such polymer and on the other side having a coating of phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 170 to 400 sieve range and held to the backing member by such polymer.
Claim 5
Dependent Claim
41 words
A neutron absorbing article according to claim 2 wherein the backing member is a woven fiberglass cloth, the phenolic resin is a trimethylol phenol formaldehyde polymer and the B 10 loading is in the range of 0.005 to 0.03 g./sq. cm.
Claim 6
Dependent Claim
63 words
A composite, neutron absorbing, coated article which is from 1 to 7 mm. thick and comprises a backing member of fiberglass cloth, a synthetic organic polymeric coating of cured phenol formaldehyde type resin on a surface thereof and boron carbide particles of particle sizes in the No. 10 to No. 400 sieve range held to said fiberglass cloth backing member by said coating.
Claim 7
Dependent Claim
63 words
A composite, neutron absorbing, coated article which is from 1 to 7 mm. thick and comprises a backing member of fiberglass cloth, a synthetic organic polymeric coating of cured phenol formaldehyde type resin on a surface thereof and boron carbide particles of particle sizes in the No. 10 to No. 400 sieve range held to said fiberglass cloth backing member by said coating.
Claim 8
Dependent Claim
38 words
A neutron absorbing article according to claim 4 wherein the backing member is a woven fiberglass cloth, the article is from 1 to 4 mm. thick and the B 10 concentration is from 0.001 to 0.1 g./sq. cm.
Claim 9
Dependent Claim
36 words
A neutron absorbing article according to claim 5 wherein the woven fiberglass cloth is of a thickness in the range of 0.1 to 2 mm. and the weight thereof is from 50 to 2,000 g./sq. m.
Claim 10
Dependent Claim
36 words
A neutron absorbing article according to claim 6 wherein the phenolic resin is a trimethylol phenol formaldehyde polymer and the B 10 loading of the article is in the range of 0.005 to 0.03 g./sq. cm.
Claim 11
Dependent Claim
45 words
A neutron absorbing article according to claim 4 wherein the boron carbide particles held to the fiberglass backing member by the phenol formaldehyde polymer are partially uncoated by said polymer and project past said coating in a direction opposite to that of the backing member.
Claim 12
Dependent Claim
121 words
A shield or container for absorbing neutrons emitted by nuclear materials which comprises means for holding a nuclear material, means for holding neutron absorbing material or materials in position about said nuclear material and a composite, neutron absorbing, coated article or a plurality of such articles held in such means in position about the nuclear material, said neutron absorbing article comprising a backing member of fiberglass cloth, a coating of phenol formaldehyde polymer on a surface of said backing member and boron carbide particles held to said backing member by said coating, which particles are of sizes in the No. 10 to No. 400 sieve range and which articles are of a thickness in the range of 1 to 7 mm.
Claim 13
Dependent Claim
121 words
A shield or container for absorbing neutrons emitted by nuclear materials which comprises means for holding a nuclear material, means for holding neutron absorbing material or materials in position about said nuclear material and a composite, neutron absorbing, coated article or a plurality of such articles held in such means in position about the nuclear material, said neutron absorbing article comprising a backing member of fiberglass cloth, a coating of phenol formaldehyde polymer on a surface of said backing member and boron carbide particles held to said backing member by said coating, which particles are of sizes in the No. 10 to No. 400 sieve range and which articles are of a thickness in the range of 1 to 7 mm.
Claim 14
Dependent Claim
176 words
A composite, neutron absorbing coated article from 1 to 7 mm. thick and of a B 10 concentration from 0.001 to 0.1 g./sq. cm. comprising a thin and substantially flat woven fiberglass cloth backing member, a phenol formaldehyde type of polymeric coating on the backing member and boron carbide particles of particle sizes in the No. 10 to No. 400 sieve range held to the backing member by cured phenol formaldehyde type polymer, wherein the cloth is of a thickness in the range of 0.1 to 2 mm. and a weight from 50 to 2,000 g./sq. m., the backing member has a filling coating of phenolic polymer on both sides thereof, over said filling coating, on one side thereof, has a coating of the same phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 60 to 400 sieve range and on the other side has a coating of the same phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 170 to 400 sieve range.
Claim 15
Dependent Claim
176 words
A composite, neutron absorbing coated article from 1 to 7 mm. thick and of a B 10 concentration from 0.001 to 0.1 g./sq. cm. comprising a thin and substantially flat woven fiberglass cloth backing member, a phenol formaldehyde type of polymeric coating on the backing member and boron carbide particles of particle sizes in the No. 10 to No. 400 sieve range held to the backing member by cured phenol formaldehyde type polymer, wherein the cloth is of a thickness in the range of 0.1 to 2 mm. and a weight from 50 to 2,000 g./sq. m., the backing member has a filling coating of phenolic polymer on both sides thereof, over said filling coating, on one side thereof, has a coating of the same phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 60 to 400 sieve range and on the other side has a coating of the same phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 170 to 400 sieve range.
Claim 16
Dependent Claim
27 words
A neutron absorbing article according to claim 10 with the coarse side coated with phenolic polymer, which is co-cured with the other coatings of such phenolic polymer.
Claim 17
Dependent Claim
39 words
A neutron absorbing article according to claim 11 wherein the B 10 loading is in the range of 0.005 to 0.03 g./sq. cm. and the weight of the article is in the range of 100 to 5,000 g./sq. m.
Claim 18
Dependent Claim
86 words
A neutron absorbing article according to claim 12 wherein the phenol formaldehyde type polymer is a trimethylol phenol formaldehyde polymer. thereof, over said filling coating, on one side thereof, has a coating of the same phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 60 to 400 sieve range and on the other side has a coating of the same phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 170 to 400 sieve range.
Claim 19
Dependent Claim
218 words
A composite, neutron absorbing, coated article comprising a thin and substantially flat cloth backing member, a phenol formaldehyde type polymeric coating on the backing member and boron carbide particles of particle sizes in the No. 10 to 400 sieve range held in place on the backing member by cured phenol formaldehyde type polymer, which neutron absorbing article is 1 to 7 mm. thick, with a B 10 concentration from 0.005 to 0.03 g./sq. cm. and weighs in the range of 100 to 5,000 g./sq. m., wherein the woven cloth material is of a thickness in the range of 0.1 to 2 mm. and the weight thereof is from 100 to 2,000 g./sq. m., the cloth backing member has a filling coating of phenolic polymer on both sides thereof and over said filling coating, on one side thereof, has a coating of the same phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 10 to 400 range and on the other side has a coating of phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 170 to 400 sieve range and wherein such No. 10 to 400 sieve coating is further coated with the same phenolic polymer which is co-cured with the other coatings of such polymer.
Claim 20
Dependent Claim
218 words
A composite, neutron absorbing, coated article comprising a thin and substantially flat cloth backing member, a phenol formaldehyde type polymeric coating on the backing member and boron carbide particles of particle sizes in the No. 10 to 400 sieve range held in place on the backing member by cured phenol formaldehyde type polymer, which neutron absorbing article is 1 to 7 mm. thick, with a B 10 concentration from 0.005 to 0.03 g./sq. cm. and weighs in the range of 100 to 5,000 g./sq. m., wherein the woven cloth material is of a thickness in the range of 0.1 to 2 mm. and the weight thereof is from 100 to 2,000 g./sq. m., the cloth backing member has a filling coating of phenolic polymer on both sides thereof and over said filling coating, on one side thereof, has a coating of the same phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 10 to 400 range and on the other side has a coating of phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 170 to 400 sieve range and wherein such No. 10 to 400 sieve coating is further coated with the same phenolic polymer which is co-cured with the other coatings of such polymer.
Claim 21
Dependent Claim
54 words
A neutron absorbing article according to claim 14 wherein the boron carbide particles held to the backing member by the synthetic organic polymeric coating or a plurality of said coatings include boron carbide particles partially uncoated by said coating and projecting past said coating in a direction opposite to that of the backing member.
Claim 22
Dependent Claim
69 words
A neutron absorbing article according to claim 14 wherein the backing member has a coating on one side thereof of phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 60 to 400 sieve range and on the other side has a coating of phenolic polymer with boron carbide particles evenly distributed therein of particle sizes in the No. 170 to 400 sieve range.
References Cited (Backward Citations)
US1609682A
Cited
US2796411A
Cited
US2796529A
Cited
US2991368A
Cited
DE2037514A1
Cited
DE2263676A1
Cited
US4027377A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-08-19 | 1984-02-18 | 1984-08-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-08-19 | 1988-02-18 | 1988-08-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-08-19 | 1992-02-18 | 1992-08-19 | $7700.00 | Window Closed / Lapsed |