Plasma arc production of silicon nitride
Assignee: Westinghouse Electric Corp
•
Filing: 1974-03-11
•
Granted: 1980-06-03
•
Expires: 1994-03-11
Abstract
Abstract This is a method of producing silicon nitride in a plasma arc furnace utilizing silicon metal or silicon dioxide as a starting material. When silicon metal is used it is reacted directly with a nitrogen bearing gas to produce silicon nitride. When silicon dioxide is used a two-step process is performed wherein the silicon dioxide is first reacted with hydrogen to produce silicon monoxide gas and water and thereafter the silicon monoxide gas is reacted with hydrogen and nitrogen to produce silicon nitride and water.
Inventors
- 👤 II Francis J. Harvey
- 👤 Raymond J. Bratton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:52
CPC Classifications
C; C01; C01B; C01B21/00; C01B21/06; C01B21/068; C01B21/0682; B; B82; B82Y; B82Y30/00; C01P; C01P2004/00; C01P2004/60; C01P2004/64; C01P2006/00; C01P2006/12
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
211 words
A method of forming particulate silicon nitride comprising the steps of: providing a plasma arc heater having a high heat reaction section and a low heat reaction section, introducing particulate silicon dioxide and a hydrogen containing gas into the high heat section of the plasma arc heater, the hydrogen functioning to sustain the plasma and react with the silicon dioxide, controlling the flow of hydrogen within the plasma arc heater to provide a temperature above 2500° K., said temperature being sufficient to cause a reaction between the silicon dioxide and at least a part of the hydrogen to form reaction products including silicon monoxide, transferring the reaction products including silicon monoxide and unreacted hydrogen to the low heat reaction section of the plasma arc heater, introducing a nitrogen containing gas into the low heat reaction section, and controlling the nitrogen containing gas flow to provide a temperature within the low heat reaction section to below 2170° K., said temperature being sufficient to cause a reaction between the hydrogen and the silicon monoxide and at least a portion of the nitrogen to form particulate silicon nitride within the low heat reaction section, said silicon nitride characterized by a fine and uniform particle size suitable for use in the production of sintered articles.
Claim 2
Independent Claim
211 words
A method of forming particulate silicon nitride comprising the steps of: providing a plasma arc heater having a high heat reaction section and a low heat reaction section, introducing particulate silicon dioxide and a hydrogen containing gas into the high heat section of the plasma arc heater, the hydrogen functioning to sustain the plasma and react with the silicon dioxide, controlling the flow of hydrogen within the plasma arc heater to provide a temperature above 2500° K., said temperature being sufficient to cause a reaction between the silicon dioxide and at least a part of the hydrogen to form reaction products including silicon monoxide, transferring the reaction products including silicon monoxide and unreacted hydrogen to the low heat reaction section of the plasma arc heater, introducing a nitrogen containing gas into the low heat reaction section, and controlling the nitrogen containing gas flow to provide a temperature within the low heat reaction section to below 2170° K., said temperature being sufficient to cause a reaction between the hydrogen and the silicon monoxide and at least a portion of the nitrogen to form particulate silicon nitride within the low heat reaction section, said silicon nitride characterized by a fine and uniform particle size suitable for use in the production of sintered articles.
Claim 3
Dependent Claim
25 words
The invention as defined in claim 1 wherein the temperature in the lower heat reaction section is controlled to produce a temperature below 1600° K.
Claim 4
Dependent Claim
28 words
The invention as defined in claim 1 wherein the gas introduced in the high heat reaction section is hydrogen gas in excess of the amount needed for reaction.
Claim 5
Dependent Claim
21 words
The invention as defined in claim 1 wherein the nitrogen bearing gas introduced into the lower heat reaction section is nitrogen.
Claim 6
Independent Claim
103 words
A method of forming particulate silicon nitride comprising the steps of: providing a plasma arc heater having a heat reaction section, introducing into the arc heater reaction section a mixture of particulate silicon metal and a nitrogen bearing gas, controlling the temperature of the reaction section to heat the mixture to between 1683° K. and 2170° K. to liquefy the particles of silicon and reacting the liquefied particles of silicon metal with the nitrogen to form particulate silicon nitride within the reaction section, said silicon nitride characterized by a fine and uniform particle size suitable for use in the production of sintered articles.
Claim 7
Independent Claim
103 words
A method of forming particulate silicon nitride comprising the steps of: providing a plasma arc heater having a heat reaction section, introducing into the arc heater reaction section a mixture of particulate silicon metal and a nitrogen bearing gas, controlling the temperature of the reaction section to heat the mixture to between 1683° K. and 2170° K. to liquefy the particles of silicon and reacting the liquefied particles of silicon metal with the nitrogen to form particulate silicon nitride within the reaction section, said silicon nitride characterized by a fine and uniform particle size suitable for use in the production of sintered articles.
Claim 8
Dependent Claim
16 words
The invention as defined in claim 5 wherein the nitrogen bearing gas in N 2 .
Claim 9
Dependent Claim
22 words
The method of claim 5 wherein the average particle size of the solid, particulate silicon metal is less than about 8 microns.
Claim 10
Dependent Claim
39 words
The method of claim 1 including the step of introducing a hydrogen containing gas into the low heat reaction section, said hydrogen containing gas being in addition to the unreacted hydrogen transferred thereto from the high heat reaction section.
Claim 11
Dependent Claim
37 words
The method of claim 1 including the step of adding a reductant selected from the group consisting of magnesium, aluminum, and calcium with the silicon dioxide prior to the reaction between the silicon dioxide and the hydrogen.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-06-03 | 1983-12-03 | 1984-06-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-06-03 | 1987-12-03 | 1988-06-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-06-03 | 1991-12-03 | 1992-06-03 | $7700.00 | Window Closed / Lapsed |