Assignee: Motorola Solutions Inc
•
Filing: 1978-06-05
•
Granted: 1980-05-06
•
Expires: 1998-06-05
Abstract
Abstract A method for removing photoresist from a substrate. A substrate to be stripped of photoresist is placed in a metal substrate holder or boat which is subsequently loaded into a plasma reactor. The holder is placed in contact with one electrode of the plasma reactor. The plasma reactor is evacuated and a hydrogen bearing gas is injected into the reactor at a rate to maintain the pressure between 0.1 and 10 Torr. The photoresist coated substrate is heated to a temperature between 100° C. and 225° C. Power is applied to the plasma reactor to create a hydrogen plasma which reacts with and removes the photoresist. During the removal operation the reflected power from the reactor is monitored to detect the end point of the plasma-photoresist reaction.
Inventors
- 👤 Frederick J. Robinson
- 👤 Clarence J. Tracy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:30
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/26; G03F7/42; G03F7/427; H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/286; H10P50/287
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
109 words
A method for removing a photoresist coating from a substrate which comprises the steps of: placing said substrate coated with said photoresist in a metal holder; placing said metal holder and said substrate in a plasma reactor, said metal holder in electrical contact with an electrode of said plasma reactor; heating said substrate; injecting a hydrogen bearing gas into said plasma reactor; applying power to said plasma reactor to create a plasma therein, a portion of said power being reflected from said reactor, said plasma reacting with and removing said photoresist from said substrate, and monitoring said reflected power from said reactor to detect the removing of the photoresist.
Claim 2
Independent Claim
109 words
A method for removing a photoresist coating from a substrate which comprises the steps of: placing said substrate coated with said photoresist in a metal holder; placing said metal holder and said substrate in a plasma reactor, said metal holder in electrical contact with an electrode of said plasma reactor; heating said substrate; injecting a hydrogen bearing gas into said plasma reactor; applying power to said plasma reactor to create a plasma therein, a portion of said power being reflected from said reactor, said plasma reacting with and removing said photoresist from said substrate, and monitoring said reflected power from said reactor to detect the removing of the photoresist.
Claim 3
Dependent Claim
21 words
The method of claim 1 wherein said substrates are heated to a temperature between about 100° C. and about 225° C.
Claim 4
Dependent Claim
14 words
The method of claim 1 wherein said hydrogen bearing gas is substantially pure hydrogen.
Claim 5
Dependent Claim
26 words
The method of claim 1 wherein said hydrogen bearing gas is injected to maintain a pressure within said plasma reactor between about 0.1 and 10.0 Torr.
Claim 6
Dependent Claim
18 words
The method of claim 4 wherein said pressure is maintained at between about 0.2 and about 1.5 Torr.
Claim 7
Independent Claim
132 words
A method for removing photoresist from a substrate which comprises the steps of: placing said substrate coated with photoresist in a metal substrate holder; placing said holder and said substrate in a plasma reactor, said holder contacting an electrode of said plasma reactor; evacuating said plasma reactor; injecting a hydrogen bearing gas into said plasma reactor to maintain a pressure in said reactor between 0.1 and 10.0 Torr; heating said substrate coated with photoresist to a temperature between about 100° C. and about 225° C.; applying power to said plasma reactor to create a hydrogen plasma therein, a portion of said power being reflected from said reactor, and said hydrogen plasma reacting with and removing said photoresist; and monitoring said reflected power from said reactor to detect the removing of said photoresist.
Claim 8
Independent Claim
132 words
A method for removing photoresist from a substrate which comprises the steps of: placing said substrate coated with photoresist in a metal substrate holder; placing said holder and said substrate in a plasma reactor, said holder contacting an electrode of said plasma reactor; evacuating said plasma reactor; injecting a hydrogen bearing gas into said plasma reactor to maintain a pressure in said reactor between 0.1 and 10.0 Torr; heating said substrate coated with photoresist to a temperature between about 100° C. and about 225° C.; applying power to said plasma reactor to create a hydrogen plasma therein, a portion of said power being reflected from said reactor, and said hydrogen plasma reacting with and removing said photoresist; and monitoring said reflected power from said reactor to detect the removing of said photoresist.
Claim 9
Dependent Claim
28 words
The method of claim 6 further comprising the step of terminating said reacting of said plasma with said photoresist in response to said monitoring of said reflected power.
References Cited (Backward Citations)
US3837856A
Cited
US3705055A
Cited
US3890176A
Cited
US4115184A
Cited
US4134817A
Cited
US4142107A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-05-06 | 1983-11-05 | 1984-05-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-05-06 | 1987-11-05 | 1988-05-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-05-06 | 1991-11-05 | 1992-05-06 | $7700.00 | Window Closed / Lapsed |