US4199614A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Transparent colored magnetic materials and electrostatographic process
Assignee: Xerox Corp
•
Filing: 1976-08-02
•
Granted: 1980-04-22
•
Expires: 1996-08-02
Abstract
Abstract Transparent colored materials having low bulk densities and high magnetic permeabilities are obtained by encasing silicaceous particles in a sheath of magnetic or magnetically-attractable metal, which are then heat-treated. The magnetic composite particles are prepared by the solution phase thermal decomposition of transition metal carbonyls in the presence of the silicaceous particles with a suitable suspending medium. Air and moisture are excluded from the reaction vessel and the contents are heated with agitation so that the carbonyl boils and the mixture is refluxed until the temperature rises to that of the suspending medium whereupon coating of the silicaceous particles with elemental metal is complete. The mixture is cooled, the beads washed, air-dried, and recovered. The metal coated particles are then heated in an ambient atmosphere for between about 2 to about 120 minutes at a temperature of from between about 50° C. and 700° C. Particles having transparency, color, and magnetism in the same body are obtained.
Inventors
- 👤 Ronald F. Ziolo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 15:06
CPC Classifications
G; G03; G03G; G03G9/00; G03G9/08; G03G9/083; G03G9/0837; G03G9/0825; G03G9/0831; G03G9/0832; G03G9/0833; G03G9/0839; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10S430/00; Y10S430/001; Y10S430/104; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2996
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
102 words
A magnetically-responsive composite particle having an average particle diameter of from between about 10 microns and about 850 microns, said particle comprising a porous silicaceous matrix impregnated with a magnetic or magnetically-attractable transition metal comprising a fine dispersion of ferrimagnetic γ-Fe 2 O 3 throughout said silicaceous matrix, said composite particle having been heated in an ambient atmosphere for between about 2 minutes and about 120 minutes at a temperature of from between about 50° C. and about 700° C. whereby said composite particle is characterized as colored and transparent in the wavelength region of from about 5,000 to about 8,000 Angstroms.
Claim 2
Dependent Claim
102 words
A magnetically-responsive composite particle having an average particle diameter of from between about 10 microns and about 850 microns, said particle comprising a porous silicaceous matrix impregnated with a magnetic or magnetically-attractable transition metal comprising a fine dispersion of ferrimagnetic γ-Fe 2 O 3 throughout said silicaceous matrix, said composite particle having been heated in an ambient atmosphere for between about 2 minutes and about 120 minutes at a temperature of from between about 50° C. and about 700° C. whereby said composite particle is characterized as colored and transparent in the wavelength region of from about 5,000 to about 8,000 Angstroms.
Claim 3
Dependent Claim
29 words
A magnetically-responsive composite particle in accordance with claim 1 wherein said dispersion of ferrimagnetic γ-Fe 2 O 3 comprises crystallites ranging in size of up to about 200 Angstroms.
Claim 4
Dependent Claim
141 words
An electrostatographic magnetic imaging process comprising the steps of providing an electrostatographic imaging member having a recording surface, forming an electrostatic latent image on said recording surface, and contacting said electrostatic latent image with a magnetically-responsive composite particle having an average particle diameter of from between about 10 microns and about 850 microns, said particle comprising a porous silicaceous matrix impregnated with a magnetic or magnetically-attractable transition metal, said composite particle having been heated in an ambient atmosphere for between about 2 minutes and about 120 minutes at a temperature of from between about 50° C. and about 700° C. whereby said composite particle is characterized as colored and transparent in the wavelength region of from about 5,000 to about 8,000 Angstroms, whereby said particle is attracted to and deposited on said recording surface in conformance with said electrostatic latent image.
Claim 5
Dependent Claim
141 words
An electrostatographic magnetic imaging process comprising the steps of providing an electrostatographic imaging member having a recording surface, forming an electrostatic latent image on said recording surface, and contacting said electrostatic latent image with a magnetically-responsive composite particle having an average particle diameter of from between about 10 microns and about 850 microns, said particle comprising a porous silicaceous matrix impregnated with a magnetic or magnetically-attractable transition metal, said composite particle having been heated in an ambient atmosphere for between about 2 minutes and about 120 minutes at a temperature of from between about 50° C. and about 700° C. whereby said composite particle is characterized as colored and transparent in the wavelength region of from about 5,000 to about 8,000 Angstroms, whereby said particle is attracted to and deposited on said recording surface in conformance with said electrostatic latent image.
Claim 6
Dependent Claim
143 words
An electrostatographic magnetic imaging process comprising the steps of providing an electrostatographic imaging member having a recording surface, forming an electrostatic latent image on said recording surface, and contacting said electrostatic latent image with a magnetically-responsive composite particle having an average particle diameter of from between about 10 microns and about 850 microns, said particle comprising a core of a silicaceous material encased in a sheath of a magnetic metal, said composite particle having been heated in an ambient atmosphere for between about 2 minutes and about 120 minutes at a temperature of from between about 50° C. and about 700° C. whereby said composite particle is characterized as colored and transparent in the wavelength region of from about 5,000 to about 8,000 Angstroms, whereby said particle is attracted to and deposited on said recording surface in conformance with said electrostatic latent image.
Claim 7
Dependent Claim
143 words
An electrostatographic magnetic imaging process comprising the steps of providing an electrostatographic imaging member having a recording surface, forming an electrostatic latent image on said recording surface, and contacting said electrostatic latent image with a magnetically-responsive composite particle having an average particle diameter of from between about 10 microns and about 850 microns, said particle comprising a core of a silicaceous material encased in a sheath of a magnetic metal, said composite particle having been heated in an ambient atmosphere for between about 2 minutes and about 120 minutes at a temperature of from between about 50° C. and about 700° C. whereby said composite particle is characterized as colored and transparent in the wavelength region of from about 5,000 to about 8,000 Angstroms, whereby said particle is attracted to and deposited on said recording surface in conformance with said electrostatic latent image.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-22 | 1983-10-22 | 1984-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-22 | 1987-10-22 | 1988-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-22 | 1991-10-22 | 1992-04-22 | $7700.00 | Window Closed / Lapsed |