Process for the preparation of silicious polymeric materials and their applications in the separation of fluids in gaseous phase
Assignee: Petroleo Brasileiro SA Petrobras
•
Filing: 1978-06-28
•
Granted: 1980-02-26
•
Expires: 1998-06-28
Abstract
Abstract This invention relates to a process for the preparation of silicious polymeric materials and their use in the separation of fluids in the gaseous phase, wherein the materials are obtained through three basic procedures: (a) polymerization of monomeric substances in the presence of high purity submicroscopic silica particles in which the polymerization of the monomers can be followed by a deactivation reaction with silylating agent; (b) addition of high purity submicroscopic silica particles to monomeric substances, and coupling regents, which will react with surface hydroxyl groups on the silica and a polymer or monomers which are forming a polymer in the reaction medium; (c) through dispersion of the high purity submicroscopic particles in plymeric organic substances. The materials obtained in this invention are solid, usually white, highly porous, of relatively high surface area, thermally stable and have good mechanical strength, and when used as a packing material in a gas chromatographic column provide excellent results with respect to permeability, efficiency, and selectivity.
Inventors
- 👤 Wilhelm Bruening
- 👤 Inai M. R. deA. Bruening
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 14:00
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/02; B01D53/025; B01J; B01J20/00; B01J20/02; B01J20/10; B01J20/103; B01J20/22; B01J20/26; B01J20/261; B01J20/262; B01J20/265; B01J20/267; B01J20/28; B01J20/28002; B01J20/28004; B01J20/28007; B01J20/28014; B01J20/28026; B01J20/28054; B01J20/28057; B01J20/281; B01J20/282; B01J20/285; B01J20/30; B01J20/3021; B01J20/3078; B82; B82Y; B82Y30/00; C; C08; C08G; C08G83/00; C08G83/001; C08G85/00; C08K; C08K3/00; C08K3/34; C08K3/36; B01J2220/00; B01J2220/40; B01J2220/46; B01J2220/50; B01J2220/54; B01J2220/58
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
153 words
A process for separating the components of a mixture of non-polar organic compounds by gas phase chromatography comprising passing said mixture in a gaseous state through a solid stationary phase of micro-porous free flowing powder having a high surface area and good thermal stability, said phase comprising an intimate mixture of an organic macro molecular component (A) and (B) non-porous high purity silica in particles smaller than 500 angstroms which does not contain calcium, sodium or magnesium and is substantially free of metallic oxides, said silica having a surface area greater than 50 m 2 /g, said macro molecular component (A) having been intimately mixed with the silica (B) by reaction of the monomeric components forming the macro molecular component (A) in the presence of said silica, whereby said silica particles are intimately disseminated throughout organic macro molecular chains without coordinate chemical bonding linkages between the silica and the organic macro molecular component.
Claim 2
Dependent Claim
153 words
A process for separating the components of a mixture of non-polar organic compounds by gas phase chromatography comprising passing said mixture in a gaseous state through a solid stationary phase of micro-porous free flowing powder having a high surface area and good thermal stability, said phase comprising an intimate mixture of an organic macro molecular component (A) and (B) non-porous high purity silica in particles smaller than 500 angstroms which does not contain calcium, sodium or magnesium and is substantially free of metallic oxides, said silica having a surface area greater than 50 m 2 /g, said macro molecular component (A) having been intimately mixed with the silica (B) by reaction of the monomeric components forming the macro molecular component (A) in the presence of said silica, whereby said silica particles are intimately disseminated throughout organic macro molecular chains without coordinate chemical bonding linkages between the silica and the organic macro molecular component.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein the macro molecular component is formed by reaction between amine and diisocyanate.
Claim 4
Dependent Claim
18 words
The process of claim 1 wherein the macro molecular component is formed by reaction between alcohol and diisocyanate.
Claim 5
Dependent Claim
21 words
The process of claim 1 wherein the reaction product is dried, crushed and sieved prior to use as said stationary phase.
Claim 6
Dependent Claim
21 words
The process of claim 1 wherein said silicious-polymeric organic compound is reacted with hexamethyldiasilazane and then is dried, crushed and sieved.
Claim 7
Dependent Claim
21 words
The process of claim 1 wherein said monomeric components are selected from the group consisting of amines, alcohols and organic isocyanates.
Claim 8
Dependent Claim
147 words
A process for separating the components of a mixture of non-polar organic compounds by gas phase chromatography comprising passing said mixture in a gaseous state through a solid stationary phase of micro-porous free flowing powder having a high surface area and good thermal stability, said phase comprising an intimate mixture of an organic macro molecular component (A) and (B) non-porous high purity silica in particles smaller than 500 angstroms which does not contain calcium, sodium or magnesium and is substantially free of metallic oxides, said silica having a surface area greater than 50 m 2 /g, said macro molecular component (A) having been intimately mixed with the silica (B) by dispersing said silica particles (B) in said macro molecular component (A), whereby said silica particles are intimately disseminated throughout organic macro molecular chains without coordinate chemical bonding linkages between the silica and the organic macro molecular component.
Claim 9
Dependent Claim
147 words
A process for separating the components of a mixture of non-polar organic compounds by gas phase chromatography comprising passing said mixture in a gaseous state through a solid stationary phase of micro-porous free flowing powder having a high surface area and good thermal stability, said phase comprising an intimate mixture of an organic macro molecular component (A) and (B) non-porous high purity silica in particles smaller than 500 angstroms which does not contain calcium, sodium or magnesium and is substantially free of metallic oxides, said silica having a surface area greater than 50 m 2 /g, said macro molecular component (A) having been intimately mixed with the silica (B) by dispersing said silica particles (B) in said macro molecular component (A), whereby said silica particles are intimately disseminated throughout organic macro molecular chains without coordinate chemical bonding linkages between the silica and the organic macro molecular component.
Claim 10
Dependent Claim
16 words
The process of claim 7 wherein after said dispersing, the product is dried, crushed and sieved.
Claim 11
Dependent Claim
21 words
The process of claim 7 wherein said silicious-polymeric organic compound is reacted with hexamethyldiasilazane and then is dried, crushed and sieved.
Claim 12
Dependent Claim
12 words
The process of claim 7 wherein said macro molecular component is polystyrene.
Claim 13
Dependent Claim
13 words
The process of claim 7 wherein said macro molecular component is a polyamide.
Claim 14
Dependent Claim
18 words
The process of claim 7 wherein said macro molecular component is formed of diethylene glycol or a carbowax.
Claim 15
Dependent Claim
18 words
The process of claim 7 wherein said macro molecular component is cross-linked after said dispersing is carried out.
Claim 16
Dependent Claim
20 words
The process of claim 13, wherein the macromolecular component is a polyamide and the cross linking agent is a diisocyamate.
Claim 17
Dependent Claim
17 words
The process of claim 7 wherein the surfaces of the silica particles are modified before said dispersing.
References Cited (Backward Citations)
US2728740A
Cited
US3065185A
Cited
US3347020A
Cited
US3672131A
Cited
US3660966A
Cited
US3757490A
Cited
US3984349A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-25 | 1983-08-27 | 1984-02-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-25 | 1987-08-27 | 1988-02-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-25 | 1991-08-27 | 1992-02-26 | $7700.00 | Window Closed / Lapsed |