US4184877A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the manufacture of photographic silver halide emulsions containing silver halide crystals of the twinned type
Assignee: Ilford Imaging UK Ltd
•
Filing: 1978-03-06
•
Granted: 1980-01-22
•
Expires: 1998-03-06
Abstract
Abstract A method of preparing photographic silver iodobromide or iodochloride emulsions the silver halide crystals of which are of the twinned octahedral or cubic type, which emulsions have improved homogeneity of iodide content and controlled size distribution of the crystal grains, comprising the following steps: (a) forming a colloid dispersing medium silver halide crystals containing at least 90 mole % iodide these said crystals being predominantly of the hexagonal lattice structure, (b) mixing in the dispersing medium containing the said silver halide crystals an aqueous solution of a silver salt and an aqueous solution of an alkali metal or ammonium halide so forming twinned silver halide crystals containing iodide and the halides being added, the rate of addition of silver salt and alkali metal or ammonium bromide being so controlled that the silver halide crystals formed in this step are predominantly twinned and optionally (c) then causing the twinned crystals to increase in size by adding to the colloidal dispersion further aqueous silver salt solution and further alkali metal or ammonium halide and then finally optionally (d) removing the water-soluble salts formed and chemically sensitizing the emulsion. The new photographic emulsions exhibit a high covering power and contrast on development.
Inventors
- 👤 Trevor J. Maternaghan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:22
CPC Classifications
G; G03; G03C; G03C1/00; G03C1/005; G03C1/0051; G03C1/06; G03C1/08; G03C1/09; G03C1/10; G03C2001/0058; G03C1/015; G03C2001/0156; G03C1/035; G03C2001/03535; G03C2001/03552; G03C2001/03558; G03C2001/03594; G03C2200/00; G03C2200/43; G03C2200/44
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
167 words
A method of preparing a silver halide emulsion of the twinned type which comprises the steps of (a) forming in a colloid dispersing medium silver halide crystals containing at least 90 mole % iodide these said crystals being predominantly of the hexagonal lattice structure, (b) mixing in the dispersing medium containing the said silver halide crystals an aqueous solution of a silver salt and an aqueous solution of an alkali metal or ammonium bromide or chloride or mixtures thereof so forming twinned silver halide crystals containing iodide and the halide or halides being added, the rate of addition of silver salt and alkali metal or ammonium bromide being so controlled that the silver halide crystals formed in this step are predominantly twinned and optionally (d) then causing the twinned crystals to increase in size by adding to the colloidal dispersion further aqueous silver salt solution and further alkali metal or ammonium halide and then finally optionally (e) removing the water-soluble salts formed and chemically sensitising the emulsion.
Claim 2
Independent Claim
167 words
A method of preparing a silver halide emulsion of the twinned type which comprises the steps of (a) forming in a colloid dispersing medium silver halide crystals containing at least 90 mole % iodide these said crystals being predominantly of the hexagonal lattice structure, (b) mixing in the dispersing medium containing the said silver halide crystals an aqueous solution of a silver salt and an aqueous solution of an alkali metal or ammonium bromide or chloride or mixtures thereof so forming twinned silver halide crystals containing iodide and the halide or halides being added, the rate of addition of silver salt and alkali metal or ammonium bromide being so controlled that the silver halide crystals formed in this step are predominantly twinned and optionally (d) then causing the twinned crystals to increase in size by adding to the colloidal dispersion further aqueous silver salt solution and further alkali metal or ammonium halide and then finally optionally (e) removing the water-soluble salts formed and chemically sensitising the emulsion.
Claim 3
Dependent Claim
16 words
A method according to claim 1 wherein the final emulsion is of the twinned octahedral type.
Claim 4
Dependent Claim
16 words
A method according to claim 1 wherein the final emulsion is of the twinned cubic type.
Claim 5
Dependent Claim
30 words
A method according to claim 1 wherein the silver iodide content in the dispersing medium at the commencement of step (b) is in the range of 0.05 to 2.0 moles/liter.
Claim 6
Dependent Claim
31 words
A method according to claim 4 wherein the silver iodide content in the colloid dispersing medium at the commencement of step (b) is in the range of 0.10 to 1.0 mole/liter.
Claim 7
Dependent Claim
29 words
A method according to claim 1 wherein the median linear size of the silver iodide crystals formed in step (a) is within the range of 0.05 to 5 microns.
Claim 8
Dependent Claim
25 words
A method according to claim 6 wherein the median linear size of the silver iodide crystals is within the range of 0.1 to 1.0 microns.
Claim 9
Dependent Claim
48 words
A method according to claim 1 wherein step (b) aqueous 3-5 M solutions of silver nitrate and ammonium bromide or ammonium chloride are added to a stirred dispersion of silver iodide in gelatin solution, at a fixed temperature and pAg maintained in the range of 5.0 to 11.0.
Claim 10
Dependent Claim
15 words
A method according to claim 8 wherein the pAg range is from 6.0 to 10.0.
Claim 11
Dependent Claim
20 words
A method according to claim 8 wherein the temperature is maintained at a fixed value between 35° to 90° C.
Claim 12
Dependent Claim
24 words
A method according to claim 1 where in step (b) the flow rate of the silver salt is maintained constant as predetermined by experiment.
Claim 13
Dependent Claim
44 words
A method according to claim 1 where in step (b) the volumes of silver salt and ammonium or alkali metal halides are added such that the silver iodide comprises from 0.01 to 20 mole % of the total silver halide in the final emulsion.
Claim 14
Dependent Claim
20 words
A method according to claim 1 wherein step (a) is carried out in the presence of a silver iodide solvent.
Claim 15
Dependent Claim
28 words
A method according to claim 1 wherein step (a) is carried out in the presence of a noble metal or sulphur or selenium salt or a reducing agent.
Claim 16
Dependent Claim
98 words
A method according to claim 14 wherein the noble metal is iridium. twinned silver halide crystals containing iodide and the halide or halides being added, the rate of addition of silver salt and alkali metal or ammonium bromide being so controlled that the silver halide crystals formed in this step are predominantly twinned and optionally (d) then causing the twinned crystals to increase in size by adding to the colloidal dispersion further aqueous silver salt solution and further alkali metal or ammonium halide and then finally optionally (e) removing the water-soluble salts formed and chemically sensitising the emulsion.
Claim 17
Dependent Claim
22 words
A method according to claim 1 wherein step (b) is carried out in the presence of a fixed concentration of excess halide.
Claim 18
Dependent Claim
12 words
A silver halide emulsion prepared by the method of any claim 1.
Claim 19
Dependent Claim
17 words
Photographic silver halide material which comprises at least one silver halide emulsion as claimed in claim 17.
Claim 20
Dependent Claim
91 words
A method of preparing a monodisperse silver halide emulsion of the twinned type which consists essentially of steps (a), (b), (d), and optionally (e) as defined in claim 1 wherein, in step (d) there is added further aqueous solutions of silver nitrate and ammonium or alkali halide at such a rate to the twinned crystals that no further nucleation of crystals occurs, the pAg of the solution being maintained at a fixed value in the range 5-12, and the temperature of the solution being maintained constant in the range 35°-90° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-21 | 1983-07-23 | 1984-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-21 | 1987-07-23 | 1988-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-21 | 1991-07-23 | 1992-01-22 | $7700.00 | Window Closed / Lapsed |