Polyimide resin-forming composition
Assignee: Trace Mountain Products Inc
•
Filing: 1977-10-05
•
Granted: 1980-01-15
•
Expires: 1997-10-05
Abstract
Abstract Polyimides of the formula ##STR1## Methods of making and polymerizing precursors for such polymers. Coating and adhesive compositions including constituents which can be converted into polyimides with the foregoing structure. Methods of making and using the compositions. Adhesion promoters for such compositions which are reaction products of aromatic dianhydrides and cyclic oxoimines, and methods of producing and using the adhesion promoters.
Inventors
- 👤 John Gagliani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 14:13
CPC Classifications
C; C07; C07D; C07D209/00; C07D209/02; C07D209/44; C07D209/48; C08; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/1003; C08G73/1057; C08G73/1064; C08G73/1067; C08G73/1071; C08G73/1075; C08G73/1082; C09; C09J; C09J179/00; C09J179/04; C09J179/08
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
139 words
A composition of matter comprising an imideforming material consisting essentially of a homogeneous solution of a stoichiometric adduct of: (a) an N-substituted cyclic bisimide with terminal carboxyl groups of the formula ##STR11## wherein x is 4 to 6 and A 2 is a tetravelent, aromatic radical of the formula ##STR12## dissolved in a solvent to form a stable solution thereof; and (b) one or more aromatic diamines capable of forming a polyimide by an exchange reaction with the terminal carboxyl groups of said bisimide upon the application of heat to said adduct, said aromatic diamine having the formula H 2 N--A 1 --NH 2 in which A 1 is a divalent aromatic radical selected from the group consisting of ##STR13## said adduct being of the formula: ##STR14## wherein A 1 , A 2 and x have the above-indicated values.
Claim 2
Dependent Claim
139 words
A composition of matter comprising an imideforming material consisting essentially of a homogeneous solution of a stoichiometric adduct of: (a) an N-substituted cyclic bisimide with terminal carboxyl groups of the formula ##STR11## wherein x is 4 to 6 and A 2 is a tetravelent, aromatic radical of the formula ##STR12## dissolved in a solvent to form a stable solution thereof; and (b) one or more aromatic diamines capable of forming a polyimide by an exchange reaction with the terminal carboxyl groups of said bisimide upon the application of heat to said adduct, said aromatic diamine having the formula H 2 N--A 1 --NH 2 in which A 1 is a divalent aromatic radical selected from the group consisting of ##STR13## said adduct being of the formula: ##STR14## wherein A 1 , A 2 and x have the above-indicated values.
Claim 3
Dependent Claim
31 words
A composition according to claim 1, wherein said solvent is acetone, methylethyl ketone, ethanol, dimethyl formamide, dimethyl acetamide, N-methyl pyrrolidone, or a mixture of two or more of the foregoing solvents.
Claim 4
Dependent Claim
19 words
A composition according to claim 1, wherein the imide-forming material is benzophenonetetracarboxylimide-N,N'-pentamethylene-5,5'-dicarboxylic acid and the diamine is 4,4'-diaminodiphenyl ether.
Claim 5
Dependent Claim
22 words
A composition according to claim 3, wherein the solvent is a mixture of equal parts of acetone, dimethyl formamide and methylethyl ketone.
Claim 6
Dependent Claim
23 words
A composition according to claim 1, further comprising from about 0.1 to 2.5 parts by weight of filler per part of imide-forming material.
Claim 7
Dependent Claim
41 words
A composition according to claim 5, wherein the filler is an aluminum hydroxide, magnesium oxide, chromium oxide, aluminum phosphate or magnesium phosphate; phosphoric acid; aluminum; copper; a steel; a fluorocarbon resin; or a mixture of two or more of the foregoing.
Claim 8
Dependent Claim
46 words
A composition according to claim 5, wherein said filler is a mixture of 8-20 parts aluminum hydroxide, 20-60 parts chromium trioxide, 15-50 parts magnesium oxide and 150-300 parts phosphoric acid used in a ratio of one part by weight of filler per part of imide-forming material.
Claim 9
Dependent Claim
39 words
A composition according to claim 5, further comprising at least 0.1 part of an adhesion promoter per molecular part of amine or amine mixture, said adhesion promoter being the reaction product of a dianhydride and a primary amine-terminated silane.
Claim 10
Dependent Claim
32 words
A composition according to claim 8, wherein the adhesion promoter is obtained by reacting substantially equimolar parts of a primary amine-terminated silane with one part by weight of an aromatic acid dianhydride.
Claim 11
Dependent Claim
20 words
A composition according to claim 9, in which the silane is aminopropyltriethoxy silane and the dianhydride is 3,3',4,4'-benzophenonetetracarboxylic acid dianhydride.
References Cited (Backward Citations)
US3274159A
Cited
US3290165A
Cited
FR1427087A
Cited
US3426098A
Cited
US3518230A
Cited
US3658773A
Cited
US3792061A
Cited
US3988374A
Cited
US3962278A
Cited
US3753998A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-14 | 1983-07-16 | 1984-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-14 | 1987-07-16 | 1988-01-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-14 | 1991-07-16 | 1992-01-15 | $7700.00 | Window Closed / Lapsed |