Process for the preparation of new high-molecular segmented polyester-polycarbonates which can be processed by thermoplastic methods and new polyester-polycarbonates obtained according to the process
Assignee: Bayer AG
•
Filing: 1977-07-18
•
Granted: 1979-10-02
•
Expires: 1997-07-18
Abstract
Abstract The subject of the present invention is a process for the preparation of new high-molecular weight polyester-polycarbonates which contain incorporated segments containing carboxyl groups and can be processed by thermoplastic methods, which process is characterized in that segments which contain carboxyl groups and have average molecular weights Mn (number-average of the molecular weight determined via the acid number of the segments containing carboxyl groups) of greater than about 600, preferably of greater than about 800 and in particular of between about 1,000 and 20,000, are reacted with diphenols and phosgene by the known two-phase boundary polycondensation process at a pH value of between about 9 and 14 and at a temperature of between about 0° C. and 80° C. and preferably of between about 15° C. and 40° C. and the resulting reaction products are either subjected to a heat treatment at temperatures of between about 40° C. and 170° C. for between about 5 minutes to 24 hours or are subjected, at temperatures of between about 130° C., and 250° C., to shear forces of between about 720 and 2520 kJ/kg of polymer or are gelled in solution by organic solvents. The invention also relates to the polyester-polycarbonates which are obtainable according to the invention and contain at least 2 phases, resulting from the polycarbonate constituent and the segment fraction which has terminal carboxyl groups.
Inventors
- 👤 Manfred Schreckenberg
- 👤 Klaus Konig
- 👤 Dieter Freitag
- 👤 Volker Serini
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:04
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/64; C08G63/66; C08G64/00; C08G64/04; C08G64/06
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
86 words
A process for the production of a high-molecular weight, polyester-polycarbonate which can be processed by thermoplastic methods, comprising reacting segments which contain carboxyl groups and have average molecular weights Mn of greater than about 600 with one or more bisphenols, phosgene and about 0.2-5 mol %, relative to the mol amount of bisphenols, of a tertiary aliphatic amine by the two-phase boundary polycondensation process at a pH value of between about 9 and 14 and at a temperature of between about 0° C. and 80° C.
Claim 2
Dependent Claim
86 words
A process for the production of a high-molecular weight, polyester-polycarbonate which can be processed by thermoplastic methods, comprising reacting segments which contain carboxyl groups and have average molecular weights Mn of greater than about 600 with one or more bisphenols, phosgene and about 0.2-5 mol %, relative to the mol amount of bisphenols, of a tertiary aliphatic amine by the two-phase boundary polycondensation process at a pH value of between about 9 and 14 and at a temperature of between about 0° C. and 80° C.
Claim 3
Dependent Claim
21 words
A process according to claim 1, in which the segments which contain carboxyl groups have a Mn greater than about 800.
Claim 4
Dependent Claim
23 words
A process according to claim 1, in which the segments which contain carboxyl groups have a Mn of between about 1,000 and 20,000.
Claim 5
Dependent Claim
27 words
A process according to claim 1, in which the two-phase boundary polycondensation process is carried out at a temperature of between about 15° C. and 40° C.
Claim 6
Dependent Claim
14 words
A process according to claim 1, in which the carboxyl-containing segments have 2-COOH groups.
Claim 7
Dependent Claim
100 words
A process for the production of a high-molecular weight, polyester-polycarbonate which can be processed by thermoplastic methods comprising: (a) reacting segments which contain carboxyl groups having a number average molecular weight, Mn, of greater than about 600 with diphenols, phosgene and about 0.2-5 mol %, relative to the mol amount of diphenols, of a tertiary aliphatic amine by a two-phase boundary condensation process at a pH value of between about 9 and 14 and at a temperature of between about 0° C. and 80° C. to form a solution of the polyester-polycarbonate, and (b) isolating the polyester-polycarbonate from the solution.
Claim 8
Dependent Claim
100 words
A process for the production of a high-molecular weight, polyester-polycarbonate which can be processed by thermoplastic methods comprising: (a) reacting segments which contain carboxyl groups having a number average molecular weight, Mn, of greater than about 600 with diphenols, phosgene and about 0.2-5 mol %, relative to the mol amount of diphenols, of a tertiary aliphatic amine by a two-phase boundary condensation process at a pH value of between about 9 and 14 and at a temperature of between about 0° C. and 80° C. to form a solution of the polyester-polycarbonate, and (b) isolating the polyester-polycarbonate from the solution.
Claim 9
Dependent Claim
25 words
The process of claim 6 wherein the polyester-polycarbonate having incorporated segments containing carboxyl groups has a weight-average molecular weight, Mn, of about 25,000 to 200,000.
Claim 10
Dependent Claim
193 words
A process for the production of a high-molecular weight, polyester-polycarbonate which can be processed by thermoplastic methods comprising: (a) reacting segments which contain carboxyl groups having a number average molecular weight, Mn, of greater than about 600 which are selected from the group of compounds consisting of (i) polyesters containing --COOH groups, (ii) polyethers containing at least one hydroxyl group per molecule which have been acylated with cyclic dicarboxylic acid anhydrides, (iii) polythioethers containing at least one hydroxyl group per molecule which have been acylated with cyclic dicarboxylic acid anhydrides, (iv) polyacetals containing at least one hydroxyl group per molecule which have been acylated with cyclic dicarboxylic acid anhydrides, and (v) aliphatic polycarbonates containing at least one hydroxyl group per molecule which have been acylated with cyclic dicarboxylic acid anhydrides, with diphenols, phosgene and about 0.2-5 mole %, relative to the mol amount of diphenols, of a tertiary aliphatic amine by a two-phase boundary condensation process at a pH value of between about 9 and 14 and at a temperature of between about 0° C. and 80° C. to form a solution of the polyester-polycarbonate, and (b) isolating the polyester-polycarbonate from the solution.
Claim 11
Dependent Claim
193 words
A process for the production of a high-molecular weight, polyester-polycarbonate which can be processed by thermoplastic methods comprising: (a) reacting segments which contain carboxyl groups having a number average molecular weight, Mn, of greater than about 600 which are selected from the group of compounds consisting of (i) polyesters containing --COOH groups, (ii) polyethers containing at least one hydroxyl group per molecule which have been acylated with cyclic dicarboxylic acid anhydrides, (iii) polythioethers containing at least one hydroxyl group per molecule which have been acylated with cyclic dicarboxylic acid anhydrides, (iv) polyacetals containing at least one hydroxyl group per molecule which have been acylated with cyclic dicarboxylic acid anhydrides, and (v) aliphatic polycarbonates containing at least one hydroxyl group per molecule which have been acylated with cyclic dicarboxylic acid anhydrides, with diphenols, phosgene and about 0.2-5 mole %, relative to the mol amount of diphenols, of a tertiary aliphatic amine by a two-phase boundary condensation process at a pH value of between about 9 and 14 and at a temperature of between about 0° C. and 80° C. to form a solution of the polyester-polycarbonate, and (b) isolating the polyester-polycarbonate from the solution.
References Cited (Backward Citations)
US3207814A
Cited
US3287442A
Cited
US3409704A
Cited
US3367993A
Cited
US3461187A
Cited
US3419635A
Cited
US3641200A
Cited
US3843708A
Cited
US4001184A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-01 | 1983-04-02 | 1983-10-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-01 | 1987-04-02 | 1987-10-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-01 | 1991-04-02 | 1991-10-02 | $7700.00 | Window Closed / Lapsed |