Electrically conductive polyolefin compositions
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1978-03-06
•
Granted: 1979-10-02
•
Expires: 1998-03-06
Abstract
Abstract This invention provides an electrically conductive polyolefin composition which contains a balanced mixture of fillers which increase the extrudability of the polyolefin composition into shaped articles of improved flex strength and resistance to shrinkage. The amounts of constituents of compositions of this invention, expressed in parts by weight, are as follows: 100 parts of polypropylene-ethylene copolymer, 15-30 parts of carbon black, 0.25 to 1 part of silica, and 1-10 parts of a fiber-reinforcing agent selected from carbon fibers or mixtures of carbon and glass fibers; and when the fiber-reinforcing agent is a mixture of carbon and glass fibers, then the composition shall contain from 1 to 5 parts of glass fibers and from 1 to 5 parts of carbon fibers.
Inventors
- 👤 Hsue C. Tsien
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 18:03
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/20; H01B1/24; H01M; H01M4/00; H01M4/02; H01M4/64; H01M4/66; H01M4/663; H01M4/668; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
107 words
An electrically conductive polyolefin composition comprising a homogeneous blend of 100 parts by weight of a crystalline polypropylene-ethylene copolymer containing from 20 mole % to about 35 mole % ethylene; from 15 to 30 parts by weight of carbon black; from 0.25 to 1.0 parts by weight of silica; and from 1 to 10 parts by weight of a fiber-reinforcing agent selected from carbon fibers and mixtures of carbon and glass fibers, and when said fiber agent is a mixture of carbon and glass fibers, then said composition shall contain from 1 to 5 parts of glass fibers and from 1 to 5 parts of carbon fibers.
Claim 2
Dependent Claim
107 words
An electrically conductive polyolefin composition comprising a homogeneous blend of 100 parts by weight of a crystalline polypropylene-ethylene copolymer containing from 20 mole % to about 35 mole % ethylene; from 15 to 30 parts by weight of carbon black; from 0.25 to 1.0 parts by weight of silica; and from 1 to 10 parts by weight of a fiber-reinforcing agent selected from carbon fibers and mixtures of carbon and glass fibers, and when said fiber agent is a mixture of carbon and glass fibers, then said composition shall contain from 1 to 5 parts of glass fibers and from 1 to 5 parts of carbon fibers.
Claim 3
Dependent Claim
20 words
The composition of claim 1 wherein said carbon black has a surface area greater than about 500 m 2 /g.
Claim 4
Dependent Claim
19 words
The composition of claim 2 wherein said carbon black has a surface area of about 1000 m 2 /g.
Claim 5
Dependent Claim
17 words
The composition of claim 3 wherein said fiber-reinforcing agent is a mixture of glass and carbon fibers.
Claim 6
Dependent Claim
24 words
The composition of claim 4 wherein the silica is a fumed silicon dioxide having a surface area greater than about 350 m 2 /g.
Claim 7
Dependent Claim
38 words
The composition of claim 5 including from about 5 parts to about 10 parts by weight of a polypropylene-ethylenically unsaturated carboxylic acid copolymer wherein said unsaturated acid is present in from about 2% to about 10% by weight.
Claim 8
Dependent Claim
14 words
The composition of claim 6 wherein the ethylenically unsaturated carboxylic acid is acrylic acid.
Claim 9
Dependent Claim
94 words
A polyolefin composition capable of being extruded into thin sheets having an electric resistivity below about 10 ohm-cm as determined by ASTM Test Method D-257-61 comprising: a homogeneous mixture of 100 parts by weight of a crystalline polypropylene-ethylene copolymer containing from 20 mole % to 35 mole % ethylene; 15 to 30 parts of carbon black; 0.25 to 1.0 part of fumed silicon dioxide; and 1 to 10 parts of a fiber-reinforcing agent selected from carbon fibers and a mixture of carbon and glass fibers containing not more than 5 parts of glass fibers.
Claim 10
Dependent Claim
94 words
A polyolefin composition capable of being extruded into thin sheets having an electric resistivity below about 10 ohm-cm as determined by ASTM Test Method D-257-61 comprising: a homogeneous mixture of 100 parts by weight of a crystalline polypropylene-ethylene copolymer containing from 20 mole % to 35 mole % ethylene; 15 to 30 parts of carbon black; 0.25 to 1.0 part of fumed silicon dioxide; and 1 to 10 parts of a fiber-reinforcing agent selected from carbon fibers and a mixture of carbon and glass fibers containing not more than 5 parts of glass fibers.
Claim 11
Dependent Claim
38 words
The composition of claim 8 including from about 5 parts to about 10 parts by weight of a polypropylene-ethylenically unsaturated carboxylic acid copolymer wherein said unsaturated acid is present in from about 2% to about 10% by weight.
Claim 12
Dependent Claim
14 words
The composition of claim 9 wherein the ethylenically unsaturated carboxylic acid is acrylic acid.
Claim 13
Dependent Claim
127 words
An electrically conductive nonporous polyolefin element comprising a homogeneous mixture of crystalline polypropylene-ethylene copolymer containing from 20 mole % to 35 mole % ethylene and the following constituents in parts by weight per hundred parts by weight of said copolymer: (a) 15 to 30 parts of carbon black; (b) 1 to 10 parts of a fiber-reinforcing agent selected from carbon fibers and mixtures of carbon and glass fibers containing not more than 5 parts of glass fibers, and (c) 0.25 to 1.0 parts of fumed silicon dioxide, said sheet being in the form of a thin sheet having a thickness of from about 150 microns to about 500 microns, and said element having an electric resistivity below about 10 ohm-cm as determined by ASTM Test Method D-257-61.
Claim 14
Dependent Claim
127 words
An electrically conductive nonporous polyolefin element comprising a homogeneous mixture of crystalline polypropylene-ethylene copolymer containing from 20 mole % to 35 mole % ethylene and the following constituents in parts by weight per hundred parts by weight of said copolymer: (a) 15 to 30 parts of carbon black; (b) 1 to 10 parts of a fiber-reinforcing agent selected from carbon fibers and mixtures of carbon and glass fibers containing not more than 5 parts of glass fibers, and (c) 0.25 to 1.0 parts of fumed silicon dioxide, said sheet being in the form of a thin sheet having a thickness of from about 150 microns to about 500 microns, and said element having an electric resistivity below about 10 ohm-cm as determined by ASTM Test Method D-257-61.
Claim 15
Dependent Claim
38 words
The electrically conductive nonporous element of claim 11 wherein said carbon black has a surface area greater than about 500 m 2 /g and wherein said silica has a surface area greater than about 350 m 2 /g.
Claim 16
Dependent Claim
35 words
The nonporous element of claim 12 wherein said fiber-reinforcing agent is selected from a mixture of carbon and glass fibers and wherein 5 parts of glass fibers and 5 parts of carbon fibers are present.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-01 | 1983-04-02 | 1983-10-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-01 | 1987-04-02 | 1987-10-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-01 | 1991-04-02 | 1991-10-02 | $7700.00 | Window Closed / Lapsed |