US4166049A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process of producing a rubberized asphalt composition suitable for use in road and highway construction and repair and product
Assignee: U S Rubber Reclaiming Co Inc
•
Filing: 1976-08-27
•
Granted: 1979-08-28
•
Expires: 1996-08-27
Abstract
Abstract Process of providing a rubberized asphalt from reclaimed rubber produced from whole scrapped tires and having a composition of about 15-20 percent acetone extractible oils, resins, and other rubber compounding ingredients such as antioxidants, antiozants, emulsifiers, and the like, about 10-35 percent carbon black, about 10-20 percent ash primarily from zinc oxide, titanium dioxide, clay, whiting, and talc, and about 35-45 percent rubber hydrocarbon of which 15-30 percent is a mixture of synthetic rubbers such as SBR, neoprene, polybutadiene, isoprene, butyl, and chlorobutyl, and other 10-20 percent is natural rubber and an asphalt at a level of 5-25 percent rubber to 75-95 percent asphalt by weight, the asphalt having a composition of 20-30 percent asphaltenes, 5-15 percent nitrogen bases, 10-20 percent first acidaffins, 30-40 percent second acidaffins, and 10-20 percent paraffins, and the rubber and asphalt being cooked at about 350-450 degrees F. for 30 minutes to 2 hours, which improves the adhesion of the asphalt, reduces stripping, and improves the strength and flexibility of the asphalt; and the product so formed. Asphalts having less than 30 percent second acidaffins content do not produce the desired adhesive properties when combined with rubber and those that contain more than 40 percent of this component become soft and sticky at summer pavement temperature. Also a process for producing a rubberized asphalt product suitable for joint and crack sealing, membrance, chip seals, and as a binder for asphaltic concrete, and having a viscosity of less than 800 centipoises at 400° F. and being sprayable using conventional equipment may be provided as may the product itself. It may be provided by cooking at 350°-450° F. for 30 minutes to 2 hours, a composition containing 20-60 percent reclaimed ("devulcanized") rubber, 15-20 percent high rubber scrap, 15-50 percent of a scrap rubber crumb having a somewhat lower rubber content, and an asphalt composed of 20-30 percent asphaltenes, 5-15 percent nitrogen basis, 10-20% first acidaffins, 30-40% second acidaffins, and 10-20 percent paraffins; the rubber-asphalt proportion being 5-25 percent rubber to 75-95 percent asphalt by weight.
Inventors
- 👤 Bobby J. Huff
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 16:16
CPC Classifications
C; C10; C10C; C10C3/00; C10C3/02; C10C3/026; C08; C08L; C08L95/00; C08L2207/00; C08L2207/20; C08L2207/24
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
127 words
A process for producing a rubberized asphalt for highway construction and maintenance comprising reacting together for from thirty minutes to two hours at 350°-450° F. 75-95% by weight of asphalt and 5-25% by weight of rubber, wherein said asphalt has a composition of 20-30% asphaltenes, 5-15% nitrogen bases, 10-20% first acidaffins, 30-40% second acidaffins and 10-20% paraffins, and wherein the rubber is devulcanized reclaimed rubber produced from whole scrapped tires and having a composition of about 15-20% rubber compounding ingredients comprising acetone extractible oils, resins, and others, about 10-35% carbon black, 10-20% ash and about 35-45% rubber hydrocarbon of which 30-85% is at least one member of the group consisting of SBR, neoprene, polybutadiene, poly-isoprene, and butyl and chlorobutyl rubber, and of which 15-70% is natural rubber.
Claim 2
Dependent Claim
116 words
A process for producing a rubberized asphalt for highway construction and maintenance comprising reacting together for from thirty minutes to two hours at 350-450° F. 75-95% by weight of asphalt 5-25% by weight of rubber, wherein said asphalt has a composition of 20-30% asphaltenes, 5-15% nitrogen bases, 10-20% first acidaffins, 30-40% second acidaffins and 10-20% paraffins, and wherein the rubber is a blend of 50-75 parts by weight of devulcanized rubber of a composition of about 15-20% rubber compounding ingredients, about 10-35% carbon black, about 10-20% ash, and about 35-45% rubber hydrocarbon of which 30-85% consists of synthetic tire rubbers and about 15-70% is natural rubber; and 25-50 parts by weight of vulcanized scrap rubber crumb.
Claim 3
Dependent Claim
116 words
A process for producing a rubberized asphalt for highway construction and maintenance comprising reacting together for from thirty minutes to two hours at 350-450° F. 75-95% by weight of asphalt 5-25% by weight of rubber, wherein said asphalt has a composition of 20-30% asphaltenes, 5-15% nitrogen bases, 10-20% first acidaffins, 30-40% second acidaffins and 10-20% paraffins, and wherein the rubber is a blend of 50-75 parts by weight of devulcanized rubber of a composition of about 15-20% rubber compounding ingredients, about 10-35% carbon black, about 10-20% ash, and about 35-45% rubber hydrocarbon of which 30-85% consists of synthetic tire rubbers and about 15-70% is natural rubber; and 25-50 parts by weight of vulcanized scrap rubber crumb.
Claim 4
Dependent Claim
24 words
A process according to claim 2, wherein at least 50% of the rubber hydrocarbon content of said vulcanized scrap rubber crumb is natural rubber.
Claim 5
Dependent Claim
25 words
A process according to claim 3, wherein the rubber hydrocarbon content of said vulcanized rubber crumb consists of 80-100% natural rubber and 0-20% synthetic rubber.
Claim 6
Dependent Claim
128 words
A rubberized asphalt suitable for use in highway construction and repair as a joint and crack sealer, chip sealer binder, membrane interlayer, or binder for asphaltic concrete and which has exceptional adhesive and cohesive properties and is extremely flexible and elastic at low temperatures yet very stable and resistant to bleeding at high temperatures and is prepared by reacting together for from 30 minutes to two hours at 350-450 degrees F., 75-95% by weight of an asphalt having a composition of 20-30% asphaltenes, 5-15% nitrogen bases, 10-20% first acidaffins, 30-40% second acidaffins and 10-20% paraffins, and 5-25% by weight of scrap rubber to produce a material having a viscosity of less than 800 centipoises at 400° F. so that it can be sprayed with conventional asphalt distributing equipment.
Claim 7
Dependent Claim
128 words
A rubberized asphalt suitable for use in highway construction and repair as a joint and crack sealer, chip sealer binder, membrane interlayer, or binder for asphaltic concrete and which has exceptional adhesive and cohesive properties and is extremely flexible and elastic at low temperatures yet very stable and resistant to bleeding at high temperatures and is prepared by reacting together for from 30 minutes to two hours at 350-450 degrees F., 75-95% by weight of an asphalt having a composition of 20-30% asphaltenes, 5-15% nitrogen bases, 10-20% first acidaffins, 30-40% second acidaffins and 10-20% paraffins, and 5-25% by weight of scrap rubber to produce a material having a viscosity of less than 800 centipoises at 400° F. so that it can be sprayed with conventional asphalt distributing equipment.
Claim 8
Dependent Claim
78 words
A material as in claim 5 wherein said rubber is devulcanized reclaimed rubber produced from whole scrapped tires and having a composition of about 15-20% rubber compounding ingredients comprising acetone extractible oils, resins, and others, about 10-35% carbon black, 10-20% ash and about 35-45% rubber hydrocarbon of which 30-85% is at least one member of the group of synthetic rubbers consisting of SBR, neoprene, polybutadiene, poly-isoprene, and butyl and chlorobutyl rubber, and of which 15-70% is natural rubber.
Claim 9
Dependent Claim
129 words
A material as in claim 4 wherein said rubber is a blend of 50-75 parts by weight of devulcanized rubber of a composition of about 15-20 % rubber compounding ingredients comprising acetone extractible oils, resins, and others, about 10-35% carbon black, 10-20% ash primarily from zinc oxide, titanium dioxide, clay, whiting, and talc, and about 35-45% rubber hydrocarbon of which 30-85% is at least one member of the group consisting of SBR, neoprene, polybutadiene, polyisoprene, and butyl and chlorobutyl rubber, and of which 15-70% is natural rubber; and 25-50 parts by weight of vulcanized rubber having the high natural rubber content specified below comprising about 5-10% acetone extractibles, 25-30% carbon black, 0-10% ash, and 55-65% rubber hydrocarbon of which 80-100% is natural rubber and only 0-20% is synthetic rubber.
Claim 10
Dependent Claim
170 words
A material as in claim 4 wherein said rubber is a blend of 20-60 parts by weight of devulcanized rubber having a composition of about 15-20 parts of rubber compounding ingredients comprising acetone extractible oils, resins, and others, about 10-35% carbon black, 10-20% ash and about 35-45% rubber hydrocarbon of which 30-85% is at least one member of the group consisting of SBR, neoprene, polybutadiene, polyisoprene, and butyl and chlorobutyl rubber and of which 15-70% is natural rubber, 20-40 parts by weight of vulcanized rubber crumb comprising 25-50 parts by weight of vulcanized rubber having the high natural rubber content specified below and comprising about 5-10% acetone extractibles, 25-30% carbon black, 0-10% ash, and 55-65% rubber hydrocarbon of which 80-100% is natural rubber and only 0-20% is synthetic rubber, and 20-50 by weight of vulcanized rubber crumb derived from tire parts with a chemical composition of about 15-20% acetone extractibles, 25-35% carbon black, 0-10% ash, and 45-55% rubber hydrocarbon of which 55-90% is natural rubber and 10-45% is synthetic rubber.
Claim 11
Dependent Claim
68 words
A process for producing a rubberized asphalt for highway construction and maintenance comprising reacting together for from thirty minutes to two hours at 350°-450° F. 75-95% by weight of asphalt and 5-25% by weight of rubber, wherein said asphalt has a composition of 20-30% asphaltenes, 5-15% nitrogen bases, 10-20% first acidaffins, 30-40% second acidaffins and 10-20% paraffins, and wherein said rubber consists essentially of vulcanized scrap rubber crumb.
Claim 12
Dependent Claim
68 words
A process for producing a rubberized asphalt for highway construction and maintenance comprising reacting together for from thirty minutes to two hours at 350°-450° F. 75-95% by weight of asphalt and 5-25% by weight of rubber, wherein said asphalt has a composition of 20-30% asphaltenes, 5-15% nitrogen bases, 10-20% first acidaffins, 30-40% second acidaffins and 10-20% paraffins, and wherein said rubber consists essentially of vulcanized scrap rubber crumb.
Claim 13
Dependent Claim
24 words
A process according to claim 9, wherein at least 50% of the rubber hydrocarbon content of said vulcanized scrap rubber crumb is natural rubber.
Claim 14
Dependent Claim
39 words
A process according to claim 10, wherein said vulcanized rubber crumb is composed of about 5-10% acetone extractibles, 25-30% carbon black, 0-10% ash and 55-65% rubber hydrocarbon of which 80-100% is a natural rubber and 0-20% is synthetic rubber.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-08-27 | 1983-02-26 | 1983-08-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-08-27 | 1987-02-26 | 1987-08-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-08-27 | 1991-02-26 | 1991-08-28 | $7700.00 | Window Closed / Lapsed |