Process for improving corrosion resistant characteristics of chrome plated aluminum and aluminum alloys
Assignee: Rio Tinto Switzerland AG
•
Filing: 1978-04-11
•
Granted: 1979-07-31
•
Expires: 1998-04-11
Abstract
Abstract The invention relates to a method for preparing aluminum and aluminum alloy objects for plating which results in an article whch exhibits improved corrosion resistant characteristics. The process includes anodizing the aluminum object in an acid bath, placing the anodized object in contact with a chemical which impregnates and is absorbed by the oxidized crystalline surface and finally exposing the treated aluminum object to heat so that the impregnating chemical is pyrolyzed to form an electronically conductive oxide thereby permitting the plating process while preserving an anodic coating of high ionic resistance.
Inventors
- 👤 Michael J. Pryor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 05:24
CPC Classifications
C; C25; C25D; C25D5/00; C25D5/48; C25D5/50; C25D5/34; C25D5/42; C25D5/44; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
82 words
A coated article which is readily plated by standard plating techniques and characterized by high corrosion resistance to the acid nature of the plating bath comprising an aluminum substrate, a microporous anodic oxidized crystalline surface on said substrate including in part comparatively large pores substantially normal to said substrate, and an electronically conductive oxide of high ionic resistance continuously distributed in said microporous anodic oxidized crystalline surface and said large pores so as to form a continuous high corrosion resistant barrier layer.
Claim 2
Dependent Claim
82 words
A coated article which is readily plated by standard plating techniques and characterized by high corrosion resistance to the acid nature of the plating bath comprising an aluminum substrate, a microporous anodic oxidized crystalline surface on said substrate including in part comparatively large pores substantially normal to said substrate, and an electronically conductive oxide of high ionic resistance continuously distributed in said microporous anodic oxidized crystalline surface and said large pores so as to form a continuous high corrosion resistant barrier layer.
Claim 3
Dependent Claim
17 words
A coated article according to claim 1 wherein said conductive oxide is Ti 2 O 3 .
Claim 4
Dependent Claim
14 words
A coated article according to claim 1 wherein the conductive oxide is stannous oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-30 | 1983-01-29 | 1983-07-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-30 | 1987-01-29 | 1987-07-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-30 | 1991-01-29 | 1991-07-31 | $7700.00 | Window Closed / Lapsed |