Process for the manufacture of polyurethane adhesives
Assignee: BASF Corp
•
Filing: 1976-09-16
•
Granted: 1979-05-22
•
Expires: 1996-09-16
Abstract
Abstract Process for the manufacture of polyurethane adhesives with uniform molecular weights which are accurately adjustable and reproducible consisting of diisocyanates, polyols, chain extenders if required, catalysts and additives, all of which are soluble in polar, organic solvents which are inert with respect to isocyanate groups. The polyaddition process is carried out by using an excess of diisocyanate, the reaction is terminated upon reaching the desired molecular weight, and the still existing excess isocyanate groups are allowed to react with alcohols, ammonia and/or amines. The process is characterized in that the polyurethanepolyaddition products are crushed into particles of 1-15 mm and that they are treated with possibly substituted primary, aliphatic mono- to trivalent alcohols, ammonia and/or aliphatic, cycloaliphatic or aromatic mono- or diamines in the liquid or vapor phase in the absence of organic solvents.
Inventors
- 👤 Georg Falkenstein
- 👤 Otto Volkert
- 👤 Lothar Mampel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 12:16
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K5/00; C08K5/04; C08K5/07; C08K5/10; C08K5/15; C08K5/16; C08K5/20; C08K5/54; C08L; C08L1/00; C08L1/08; C08L1/10; C08L1/12; C08L1/16; C08L1/18; C08L23/00; C08L23/02; C08L23/04; C08L23/06; C08L33/00; C08L33/04; C08L33/06; C08L33/08; C08L61/00; C08L61/04; C08L61/06; C08L67/00; C08L75/00; C08L75/04; C08L93/00; C09; C09J; C09J175/00; C09J175/04; C08G2170/00; C08G2170/90; C08L2666/00; C08L2666/02; C08L2666/28; C08L2666/54; Y; Y10; Y10S; Y10S528/00; Y10S528/905
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
128 words
A process for the manufacture of polyurethane adhesives having uniform molecular weights, which comprises the steps of reacting a stoichiometric excess of organic diisocyanate with a polyol and from 0 to 10% by weight of a chain extender in the presence of a suitable catalyst, said excess of organic diisocyanate is defined to mean the ratio of isocyanate groups to the active polyol hydrogen atoms and those of any chain extender exceeds 1:1.001, holding the reaction mixture at a tempering reaction temperature while periodically checking the molecular weight of the reaction product, cooling and crushing the reaction product at a 40,000 to 60,000 molecular weight into particles, and treating the crushed particles with an excess of alcohol, ammonia, amine, or mixtures thereof in the absence of organic solvent.
Claim 2
Dependent Claim
128 words
A process for the manufacture of polyurethane adhesives having uniform molecular weights, which comprises the steps of reacting a stoichiometric excess of organic diisocyanate with a polyol and from 0 to 10% by weight of a chain extender in the presence of a suitable catalyst, said excess of organic diisocyanate is defined to mean the ratio of isocyanate groups to the active polyol hydrogen atoms and those of any chain extender exceeds 1:1.001, holding the reaction mixture at a tempering reaction temperature while periodically checking the molecular weight of the reaction product, cooling and crushing the reaction product at a 40,000 to 60,000 molecular weight into particles, and treating the crushed particles with an excess of alcohol, ammonia, amine, or mixtures thereof in the absence of organic solvent.
Claim 3
Dependent Claim
57 words
A process for the manufacture of polyurethane adhesives as defined in claim 1, in which the ratio of the active polyol hydrogen atoms and those of any chain extender to the isocyanate groups is in the range of 1:1.05 to 1:1.1, and the reaction mixture is held at the tempering temperature from about 2 to 24 hours.
Claim 4
Dependent Claim
137 words
A process for the manufacture of polyurethane adhesives having uniform molecular weights, which comprises the steps of bringing organic diisocyanate and polyol together with a suitable catalyst, additives and from 0 to 10% by weight of chain extenders based on the total polyol and chain extender, with the ratio of the polyol hydrogen atoms and those of any chain extender reactive with the isocyanate groups to the isocyanate groups being in the range of from 1:1.001 to 1:2, reacting the mixture at a final temperature of the order of 90°-130° C. until a molecular weight of 40,000 to 60,000 is obtained, cooling and breaking up the reaction product into particles of the order of 1-15 mm, and treating the particles with an excess of alcohol, ammonia, amine or mixtures thereof in the absence of organic polyurethane solvents.
Claim 5
Dependent Claim
137 words
A process for the manufacture of polyurethane adhesives having uniform molecular weights, which comprises the steps of bringing organic diisocyanate and polyol together with a suitable catalyst, additives and from 0 to 10% by weight of chain extenders based on the total polyol and chain extender, with the ratio of the polyol hydrogen atoms and those of any chain extender reactive with the isocyanate groups to the isocyanate groups being in the range of from 1:1.001 to 1:2, reacting the mixture at a final temperature of the order of 90°-130° C. until a molecular weight of 40,000 to 60,000 is obtained, cooling and breaking up the reaction product into particles of the order of 1-15 mm, and treating the particles with an excess of alcohol, ammonia, amine or mixtures thereof in the absence of organic polyurethane solvents.
Claim 6
Dependent Claim
45 words
A process for the manufacture of polyurethane adhesives as defined in claim 3, in which the ratio of the polyol hydrogen atoms and those of any chain extender reactive with the isocyanate group to the isocyanate groups is in the range of 1:1.05 and 1:1.1.
Claim 7
Dependent Claim
46 words
A process for the manufacture of polyurethane adhesives as defined in claim 3, in which the particles are treated with alcohol, ammonia, amine or mixtures thereof in a ratio of from about 1-100 grams of alcohol, ammonia, amine or mixtures thereof per gram of particulate polyurethane.
Claim 8
Dependent Claim
46 words
A process for the manufacture of polyurethane adhesives as defined in claim 4, in which the particles are treated with alcohol, ammonia, amine, or mixtures thereof in a ratio of from about 1-100 grams of alcohol, ammonia, amine, or mixtures thereof per gram of particulate polyurethane.
Claim 9
Dependent Claim
45 words
A process for the manufacture of polyurethane adhesives as defined in claim 3, in which the particles are treated with an excess of alcohol, ammonia, amine, or mixtures thereof at a temperature of from 10°-100° C. for a time of from 3 to 120 minutes.
Claim 10
Dependent Claim
22 words
A process for the manufacture of polyurethane adhesives as defined in claim 7, in which the particulate polyurethane is treated with ammonia.
Claim 11
Dependent Claim
46 words
A process for the manufacture of polyurethane adhesives as defined in claim 5, in which the particles are treated with an alcoholic solution of ammonia, amine or mixtures thereof, with the total amine and ammonia content of the solution being 0.5-10.0% by weight of the solution.
Claim 12
Dependent Claim
30 words
A process for the manufacture of polyurethane adhesives as defined in claim 9, in which the alcoholic solution has a total ammonia and amine content of from 1-5% by weight.
References Cited (Backward Citations)
US2871227A
Cited
US3310533A
Cited
US3321433A
Cited
US3326861A
Cited
US3933756A
Cited
US4046741A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-21 | 1982-11-20 | 1983-05-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-21 | 1986-11-20 | 1987-05-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-21 | 1990-11-20 | 1991-05-22 | $7700.00 | Window Closed / Lapsed |