Lubricating composition applied over primer coat
Assignee: Diamond Shamrock Corp
•
Filing: 1977-12-30
•
Granted: 1979-04-10
•
Expires: 1997-12-30
Abstract
Abstract Since primers can be applied to metal substrates prior to subsequent operation, including metal deformation, they are often applied in coil coating operation. The potential for the removal of primer coating during metal deformation is a drawback to early coating application. There is now provided a lubricant composition particularly adapted to meet this problem. The composition comprises metallic stearate, emulsifier, titanium dioxide and Xanthomonas hydrophilic colloid, all in aqueous medium.
Inventors
- 👤 George A. McIntosh
- 👤 Russell Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 10:13
CPC Classifications
C; C10; C10M; C10M173/00; C10M173/02; C10M2201/00; C10M2201/02; C10M2201/06; C10M2201/062; C10M2201/08; C10M2201/081; C10M2201/082; C10M2201/083; C10M2201/084; C10M2201/086; C10M2207/00; C10M2207/10; C10M2207/12; C10M2207/121; C10M2207/123; C10M2207/125; C10M2207/129; C10M2207/22; C10M2209/00; C10M2209/02; C10M2209/08; C10M2209/084; C10M2209/10; C10M2209/103; C10M2209/104; C10M2209/108; C10M2209/12; C10N; C10N2010/00; C10N2010/04; C10N2040/00; C10N2040/20; C10N2040/24; C10N2040/241; C10N2040/242; C10N2040/243; C10N2040/244; C10N2040/245; C10N2040/246; C10N2040/247; C10N2050/00; C10N2050/01; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
33 words
A lubricant composition particularly adapted for application to a primer coating on a metal substrate, which composition comprises a metallic stearate, emulsifier, titanium dioxide and Xanthomonas hydrophilic colloid, all in an aqueous medium.
Claim 2
Dependent Claim
33 words
A lubricant composition particularly adapted for application to a primer coating on a metal substrate, which composition comprises a metallic stearate, emulsifier, titanium dioxide and Xanthomonas hydrophilic colloid, all in an aqueous medium.
Claim 3
Dependent Claim
25 words
The composition of claim 1 wherein said titanium dioxide component is supplied by pigmentary titanium dioxide having a particule size finer than about 200 mesh.
Claim 4
Dependent Claim
24 words
The composition of claim 1 wherein the metal of said metallic stearate is selected from the group consisting of calcium, zinc and mixtures thereof.
Claim 5
Dependent Claim
21 words
The composition of claim 1 wherein said emulsifier has an HLB number within the range from about 10 to about 12.
Claim 6
Dependent Claim
12 words
The composition of claim 1 further characterized by containing nonionic wetting agent.
Claim 7
Dependent Claim
14 words
The composition of claim 5 wherein said wetting agent is an alkoxylated alkyl phenol.
Claim 8
Dependent Claim
11 words
The composition of claim 1 further characterized by containing colloid preservative.
Claim 9
Dependent Claim
20 words
The composition of claim 1 further characterized by containing a substance providing corrosion resistance when applied to a metal substrate.
Claim 10
Dependent Claim
34 words
The composition of claim 8 wherein said substance is selected from the group consisting of nitrite salts, chromate salts, molybdates, vanadates, zinc and magnesium salts not specifically hereinbefore enumerated, and mixtures of the foregoing.
Claim 11
Dependent Claim
58 words
The composition of claim 1 wherein said Xanthomonas hydrophilic colloid in mixture, which mixture contains said colloid plus a water-soluble thickening polymer selected from the group consisting of natural gums, water-soluble cellulose esters, synthetic gums alginates, dextrins, starches, carageenan and mixtures thereof, and with the weight of said colloid being above about 60 weight percent of said mixture.
Claim 12
Dependent Claim
44 words
The composition of claim 1 further characterized as a concentrate, for subsequent dilution with aqueous medium, which concentrate comprises 1-25 weight percent metallic stearate, 0.5-12 weight percent emulsifier, 0.5-10 weight percent titanium dioxide, 0.2-2 weight percent of said colloid, and a balance of water.
Claim 13
Dependent Claim
31 words
The composition of claim 11 further characterized by being diluted with aqueous medium in a weight proportion of aqueous medium to concentrate within the range from about 2:1 to about 20:1.
Claim 14
Dependent Claim
51 words
A coated metal substrate having a coating providing coating protection to said substrate, said coating comprising a primer coat containing finely divided particulate substance, with said primer coat having an exposed surface film of lubricating composition comprising a metallic stearate, emulsifier, titanium dioxide and Xanthomonas hydrophilic colloid, all in aqueous medium.
Claim 15
Dependent Claim
51 words
A coated metal substrate having a coating providing coating protection to said substrate, said coating comprising a primer coat containing finely divided particulate substance, with said primer coat having an exposed surface film of lubricating composition comprising a metallic stearate, emulsifier, titanium dioxide and Xanthomonas hydrophilic colloid, all in aqueous medium.
Claim 16
Dependent Claim
31 words
The coated metal substrate of claim 13 wherein said primer coat is present in a thickness of at least about 0.1 ml and the lubricant film is present in wet condition.
Claim 17
Dependent Claim
15 words
The coated metal substrate of claim 13 wherein said primer coat is a weldable primer.
Claim 18
Dependent Claim
69 words
A process for deforming coated metal having a primer coat, while retarding coating loss during metal deformation, wherein said primer coat contains finely divided particulate substance, which process comprises, establishing on said primer coat a surface film of lubricating composition and then deforming said coated metal having resulting lubricated coating, wherein said lubricating composition comprises a metallic stearate, emulsifier, titanium dioxide and Xanthomonas hydrophilic colloid, all in aqueous medium.
Claim 19
Dependent Claim
69 words
A process for deforming coated metal having a primer coat, while retarding coating loss during metal deformation, wherein said primer coat contains finely divided particulate substance, which process comprises, establishing on said primer coat a surface film of lubricating composition and then deforming said coated metal having resulting lubricated coating, wherein said lubricating composition comprises a metallic stearate, emulsifier, titanium dioxide and Xanthomonas hydrophilic colloid, all in aqueous medium.
References Cited (Backward Citations)
US2760931A
Cited
US2697072A
Cited
US3282843A
Cited
US3313728A
Cited
US3377278A
Cited
US3664953A
Cited
US3725274A
Cited
US3948686A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-09 | 1982-10-09 | 1983-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-09 | 1986-10-09 | 1987-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-09 | 1990-10-09 | 1991-04-10 | $7700.00 | Window Closed / Lapsed |