Zinc dust primer systems for metal sheets deformable by noncutting processes
Assignee: Bonaval Werke GmbH
•
Filing: 1974-10-23
•
Granted: 1976-04-06
•
Expires: 1994-10-23
Abstract
Abstract The invention relates to a zinc dust primer system which renders possible a mass production working of metal sheets by noncutting processes. The said primer system consists of a lower or bottom layer containing the actual zinc dust primer, and a covering layer containing a substance promoting sliding and a binder. A suitable substance promoting sliding is, in particular, graphite. The system of the invention is especially applicable in the automobile, shipbuilding and packing industries and in the construction of steel furniture. It is of special interest in the case of the coil-coating process.
Inventors
- 👤 Karl-Heinz Lochner
- 👤 Johann Lenzen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 05:55
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/50; B05D7/52; B05D7/54; B05D7/14; B05D2601/00; B05D2601/20; B05D2601/28; B05D2701/00; B05D5/00; B05D5/08; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31515
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
125 words
An improved zinc dust primer system for metal which primer system can be deformed without suffering damage and which comprises a lower layer (a), applied to a metal layer or base which has been preliminarily treated by phosphating or chromating, consisting of a zinc dust primer having a zinc content of 80 to 95 percent by weight, wherein the improvement comprises a firmly adhering covering film (b) which consists essentially of a mixture of 50 to 70 percent by weight of a substance promoting sliding selected from the group consisting of oil, silicone oil, wax, fat, graphite, molybdenum sulphide and other heavy metal sulphides, and 50 to 30 percent by weight of an organic binder based on high polymers or on substances forming high polymers.
Claim 2
Dependent Claim
125 words
An improved zinc dust primer system for metal which primer system can be deformed without suffering damage and which comprises a lower layer (a), applied to a metal layer or base which has been preliminarily treated by phosphating or chromating, consisting of a zinc dust primer having a zinc content of 80 to 95 percent by weight, wherein the improvement comprises a firmly adhering covering film (b) which consists essentially of a mixture of 50 to 70 percent by weight of a substance promoting sliding selected from the group consisting of oil, silicone oil, wax, fat, graphite, molybdenum sulphide and other heavy metal sulphides, and 50 to 30 percent by weight of an organic binder based on high polymers or on substances forming high polymers.
Claim 3
Dependent Claim
25 words
An improved zinc dust primer system according to claim 1, wherein the covering film (b) contains, as the substance promoting sliding, graphite or molybdenum sulphide.
Claim 4
Dependent Claim
48 words
An improved zinc primer system according to claim 1, wherein the high polymer contained in the covering film (b) is a polyester resin, an epoxide resin, a polyvinyl compound, a polyacrylic or polymethacrylic compound or corresponding initial products that can be polycondensed or polymerised to form high polymers.
Claim 5
Dependent Claim
22 words
An improved zinc dust primer system according to claim 3, wherein the high polymer contained in the covering film (b) is polyvinylbutyral.
Claim 6
Dependent Claim
28 words
An improved zinc dust primer system according to claim 1, wherein the covering film (b) contains graphite as the substance promoting sliding, and polyvinylbutyral as the high polymer.
Claim 7
Dependent Claim
134 words
A process for modification of metal surfaces with an improved zinc dust primer system for metal which primer system can be deformed without suffering damage and which comprises a lower layer (a), applied to a metal layer or base which has been preliminarily treated by phosphating or chromating, consisting of a zinc dust primer having a zinc content of 80 to 95 percent by weight, wherein the improvement comprises applying a firmly adhering covering film (b) which consists essentially of a mixture of 50 to 70 percent by weight of a substance promoting sliding selected from the group consisting of oil, silicone oil, wax, fat, graphite, molybdenum sulphide and other heavy metal sulphides, and 50 to 30 percent by weight of an organic binder based on high polymers or on substances forming high polymers.
Claim 8
Dependent Claim
134 words
A process for modification of metal surfaces with an improved zinc dust primer system for metal which primer system can be deformed without suffering damage and which comprises a lower layer (a), applied to a metal layer or base which has been preliminarily treated by phosphating or chromating, consisting of a zinc dust primer having a zinc content of 80 to 95 percent by weight, wherein the improvement comprises applying a firmly adhering covering film (b) which consists essentially of a mixture of 50 to 70 percent by weight of a substance promoting sliding selected from the group consisting of oil, silicone oil, wax, fat, graphite, molybdenum sulphide and other heavy metal sulphides, and 50 to 30 percent by weight of an organic binder based on high polymers or on substances forming high polymers.
Claim 9
Dependent Claim
24 words
A process according to claim 6, wherein there is applied a covering film (b) containing graphite or molybdenum sulphide as the substance promoting sliding.
Claim 10
Dependent Claim
47 words
A process according to claim 6, wherein there is applied a covering film (b) containing, as the high polymer, a polyester resin, an epoxide resin, a polyvinyl compound, a polyacrylic or polymethacrylic compound or corresponding initial products that can be polycondensed or polymerised to form high polymers.
Claim 11
Dependent Claim
20 words
A process according to claim 8, wherein there is applied a covering film (b) containing polyvinylbutyral as the high polymer.
Claim 12
Dependent Claim
27 words
A process according to claim 6, wherein there is applied a covering film (b) containing graphite as the substance promoting sliding, and polyvinylbutyral as the high polymer.
Claim 13
Dependent Claim
48 words
A process according to claim 6, wherein the covering film (b) is applied by application of a solution or dispersion of the constituents for the covering film (b) using the spraying, brushing, dipping, flooding or coil-coating process, and subsequent removal of the solvent or dispersing agent by evaporation.
Claim 14
Dependent Claim
17 words
A process according to claim 6, wherein the covering film (b) is applied by a powder-coating process.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-06 | 1979-10-06 | 1980-04-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-06 | 1983-10-06 | 1984-04-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-06 | 1987-10-06 | 1988-04-06 | $7700.00 | Window Closed / Lapsed |