Abstract A drawing quality hot-dip coated low carbon aluminum killed steel strip produced by conventional steel strip forming and continuous hot-dip coating procedures wherein the hot rolled coiling temperature is maintained within a temperature range of 1250° F. - 1300° F. and the cold rolled steel strip is continuously heat treated on a Sendzimir-type continuous hot-dip coating line at a temperature of between 1850° F. and 1950° F. before cooling the strip to about the temperature of the hot-dip coating bath and immersing the strip in a hot-dip galvanizing or aluminum coating bath followed by conventional annealing. The microstructure of the drawing quality hot-dip coated steel strip is characterized by spaced islands formed of fine pearlite and fine ferrite having a grain size of about ASTM 9-10 surrounded by areas of large ferrite grains having the grain size of about ASTM 7.5-8. A typical hot-dip coated drawing quality steel strip produced by the process has a Rockwell B hardness of about 47, an average lower yield strength of about 32 KSI and an average ultimate tensile strength of 50 KSI and an average total elongation percent in two inches of about 40 percent.
A drawing quality hot-dip coated steel sheet consisting essentially of a cold rolled sheet of a low carbon aluminum killed steel free of alloying elements not normally present in a low carbon aluminum killed steel and having a hot-dip coating of a metal which provides protection against corrosion, said steel after hot-dip coating having a microstructure as in FIG. 1, and said microstructure consisting essentially of a small volume fraction of spaced islands of fine ferrite having a grain size of about 9-10 interspersed with fine pearlite and the balance of large ferrite grains having a grain size of about ASTM 7.5-8 with small grain boundary cementite.
Claim 2
Dependent Claim
107 words
A drawing quality hot-dip coated steel sheet consisting essentially of a cold rolled sheet of a low carbon aluminum killed steel free of alloying elements not normally present in a low carbon aluminum killed steel and having a hot-dip coating of a metal which provides protection against corrosion, said steel after hot-dip coating having a microstructure as in FIG. 1, and said microstructure consisting essentially of a small volume fraction of spaced islands of fine ferrite having a grain size of about 9-10 interspersed with fine pearlite and the balance of large ferrite grains having a grain size of about ASTM 7.5-8 with small grain boundary cementite.
Claim 3
Dependent Claim
54 words
A hot-dip coated steel strip as in claim 1, wherein said hot-dip coated steel strip has a Rockwell B hardness of about 47, an average lower yield strength of about 32 KSI, an average ultimate tensile strength of about 50 KSI, and an average total elongation percent in two inches of about 40 percent.
Claim 4
Dependent Claim
15 words
A steel strip as in claim 1, wherein said hot-dip coating is a galvanized coating.
Claim 5
Dependent Claim
15 words
A steel strip as in claim 1, wherein said hot-dip coating is an aluminum coating.