US4001052A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Hot-rolled low-carbon steel strip with an excellent press-workability capable of forming smooth pressed surface and a method of making the same
Assignee: JFE Steel Corp
•
Filing: 1974-11-13
•
Granted: 1977-01-04
•
Expires: 1994-11-13
Abstract
Abstract Hot-rolled low-carbon steel strip with an excellent press-workability capable of forming a smooth pressed surface consisting essentially of up to 0.12 wt. % carbon, up to 0.01 wt. % nitrogen, up to 0.0094 wt. % boron, and other specific optional ingredients, the B(%)/N(%) ratio being 0.3 to 0.94. The micrograin size number, JIS, of ferrite in the steel strip as hot-rolled is 7 to 9. The steel strip is made by hot-rolling while controlling the temperatures at the entry and delivery ends of a hot-strip finishing mill.
Inventors
- 👤 Yoshio Nakazato
- 👤 Masatoshi Nakazawa
- 👤 Nobuo Ohashi
- 👤 Yo Ito
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 01:38
CPC Classifications
C; C21; C21D; C21D8/00; C21D8/02; C21D8/0221; C21D8/0226; C22; C22C; C22C38/00; C22C38/001
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
144 words
Hot-rolled low-carbon deoxidized steel strip having a smooth pressed surface produced by hot-rolling a low carbon deoxidized steel in a hot-strip mill while maintaining the temperature at the entry end of the hot-strip mill above 950° C and the temperature at the delivery end above the A3 transformation point of the steel to form hot-rolled steel strip, said steel consisting essentially of up to 0.12% by weight of carbon, up to 0.01% by weight of nitrogen, up to 0.0094% by weight of boron, and balance iron, the ratio of the boron content in percent by weight to the nitrogen content in percent by weight being 0.3 to 0.94, said hot-rolled steel strip having a ferrite grain size number, JIS, of 7 to 9, and press forming the steel strip after hot-rolling to form said smooth pressed surface without cold-rolling or annealing said steel strip.
Claim 2
Dependent Claim
144 words
Hot-rolled low-carbon deoxidized steel strip having a smooth pressed surface produced by hot-rolling a low carbon deoxidized steel in a hot-strip mill while maintaining the temperature at the entry end of the hot-strip mill above 950° C and the temperature at the delivery end above the A3 transformation point of the steel to form hot-rolled steel strip, said steel consisting essentially of up to 0.12% by weight of carbon, up to 0.01% by weight of nitrogen, up to 0.0094% by weight of boron, and balance iron, the ratio of the boron content in percent by weight to the nitrogen content in percent by weight being 0.3 to 0.94, said hot-rolled steel strip having a ferrite grain size number, JIS, of 7 to 9, and press forming the steel strip after hot-rolling to form said smooth pressed surface without cold-rolling or annealing said steel strip.
Claim 3
Dependent Claim
55 words
Hot-rolled low-carbon deoxidized steel strip according to claim 1 wherein the carbon content is up to 0.10% by weight and the ratio of the boron content in percent by weight to the carbon content in percent by weight is not smaller than 0.04, and the steel strip has a structure of dispersion of spheroidal carbide.
Claim 4
Dependent Claim
51 words
Hot-rolled low-carbon deoxidized steel strip according to claim 1 wherein the carbon content is up to 0.03% by weight, the ratio of the boron content in percent by weight to the carbon content in percent by weight is not smaller than 0.04, and the steel strip is free from coarse carbides.
Claim 5
Dependent Claim
49 words
Hot-rolled low-carbon deoxidized steel strip according to claim 1 and further including up to 1.20% by weight of manganese and up to 0.03% by weight of sulfur, the ratio of the manganese content in percent by weight to the sulfur content in percent by weight being greater than 10.
Claim 6
Dependent Claim
27 words
Hot-rolled low-carbon deoxidized steel strip according to claim 1 and further including up to 0.03% by weight of sulfur and up to 0.03% by weight of phosphorus.
Claim 7
Dependent Claim
27 words
Hot-rolled low-carbon deoxidized steel strip according to claim 2 and further including up to 0.03% by weight of sulfur and up to 0.03% by weight of phosphorus.
Claim 8
Dependent Claim
27 words
Hot-rolled low-carbon deoxidized steel strip according to claim 3 and further including up to 0.03% by weight of sulfur and up to 0.03% by weight of phosphorus.
Claim 9
Dependent Claim
36 words
Hot-rolled low-carbon deoxidized steel strip according to claim 1 and further including as a deoxidizer up to 0.5 wt.% silicon, up to 0.1 wt.% aluminum, up to 0.05 wt.% titanium, 0.05 wt.% zirconium or mixtures thereof.
Claim 10
Dependent Claim
36 words
Hot-rolled low-carbon deoxidized steel strip according to claim 2 and further including as a deoxidizer up to 0.5 wt.% silicon, up to 0.1 wt.% aluminum, up to 0.05 wt.% titanium, 0.05 wt.% zirconium or mixtures thereof.
Claim 11
Dependent Claim
36 words
Hot-rolled low-carbon deoxidized steel strip according to claim 3 and further including as a deoxidizer up to 0.5 wt.% silicon, up to 0.1 wt.% aluminum, up to 0.05 wt.% titanium, 0.05 wt.% zirconium or mixtures thereof.
Claim 12
Dependent Claim
36 words
Hot-rolled low-carbon deoxidized steel strip according to claim 4 and further including as a deoxidizer up to 0.5 wt.% silicon, up to 0.1 wt.% aluminum, up to 0.05 wt.% titanium, 0.05 wt.% zirconium or mixtures thereof.
Claim 13
Dependent Claim
161 words
A process of manufacturing hot-rolled low-carbon deoxidized steel strip having a smooth pressed surface without cold-rolling or annealing the steel strip after hot-rolling comprising hot-rolling a low-carbon deoxidized steel in a hot-strip mill while maintaining the temperature at the entry end of the hot strip mill above 950° C and the temperature at the delivery end above the A3 transformation point of the steel so as to produce hot-rolled steel strip having a ferrite grain size number, JIS, between 7 and 9, said steel consisting essentially of up to 0.12% by weight of carbon, up to 0.01% by weight nitrogen, up to 0.01% by weight of boron, and balance iron, the ratio of the boron content in percent by weight to the nitrogen content in percent by weight to the nitrogen content in percent by weight being 0.3 to 0.94, and press forming the steel strip after hot-rolling to form said smooth pressed surface without cold-rolling or annealing said steel strip.
Claim 14
Dependent Claim
161 words
A process of manufacturing hot-rolled low-carbon deoxidized steel strip having a smooth pressed surface without cold-rolling or annealing the steel strip after hot-rolling comprising hot-rolling a low-carbon deoxidized steel in a hot-strip mill while maintaining the temperature at the entry end of the hot strip mill above 950° C and the temperature at the delivery end above the A3 transformation point of the steel so as to produce hot-rolled steel strip having a ferrite grain size number, JIS, between 7 and 9, said steel consisting essentially of up to 0.12% by weight of carbon, up to 0.01% by weight nitrogen, up to 0.01% by weight of boron, and balance iron, the ratio of the boron content in percent by weight to the nitrogen content in percent by weight to the nitrogen content in percent by weight being 0.3 to 0.94, and press forming the steel strip after hot-rolling to form said smooth pressed surface without cold-rolling or annealing said steel strip.
Claim 15
Dependent Claim
26 words
A process according to claim 12 wherein said steel further contains up to 0.03% by weight of sulfur and up to 0.03% by weight of phosphorus.
Claim 16
Dependent Claim
19 words
A process according to claim 12 wherein said carbon content in said steel is up to 0.10% by weight.
Claim 17
Dependent Claim
19 words
A process according to claim 12 wherein said carbon content in said steel is up to 0.03% by weight.
Claim 18
Dependent Claim
35 words
A process according to claim 12 wherein said steel further contains as a deoxidizer up to 0.5 wt.% silicon, up to 0.1 wt.% aluminum, up to 0.05 wt.% titanium, 0.05 wt.% zirconium or mixtures thereof.
Claim 19
Dependent Claim
148 words
An automobile bumper made of hot-rolled low-carbon deoxidized steel strip having a smooth pressed surface produced by hot-rolling a low-carbon deoxidized steel in a hot-strip mill while maintaining the temperature at the entry end of the hot-strip mill above 950° C and the temperature at the delivery end above the A3 transformation point of the steel to form hot-rolled steel strip, said steel consisting essentially of up to 0.12% by weight of carbon, up to 0.01% by weight of nitrogen, up to 0.01% by weight of boron, and balance iron, the ratio of the boron content in percent by weight to the nitrogen content in percent by weight being 0.3 to 0.94, said hot-rolled steel strip having a ferrite grain size number, JIS, of 7 to 9, and press forming the steel strip after hot-rolling to form said smooth pressed surface without cold-rolling or annealing said steel strip.
Claim 20
Dependent Claim
148 words
An automobile bumper made of hot-rolled low-carbon deoxidized steel strip having a smooth pressed surface produced by hot-rolling a low-carbon deoxidized steel in a hot-strip mill while maintaining the temperature at the entry end of the hot-strip mill above 950° C and the temperature at the delivery end above the A3 transformation point of the steel to form hot-rolled steel strip, said steel consisting essentially of up to 0.12% by weight of carbon, up to 0.01% by weight of nitrogen, up to 0.01% by weight of boron, and balance iron, the ratio of the boron content in percent by weight to the nitrogen content in percent by weight being 0.3 to 0.94, said hot-rolled steel strip having a ferrite grain size number, JIS, of 7 to 9, and press forming the steel strip after hot-rolling to form said smooth pressed surface without cold-rolling or annealing said steel strip.
References Cited (Backward Citations)
US2357876A
Cited
US2771651A
Cited
US2772154A
Cited
US2999749A
Cited
US3716420A
Cited
US3725143A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-01-04 | 1980-07-05 | 1981-01-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-01-04 | 1984-07-05 | 1985-01-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-01-04 | 1988-07-05 | 1989-01-04 | $7700.00 | Window Closed / Lapsed |