Coherent rigid solid material
Assignee: Lebanon Steel Foundry
•
Filing: 1977-11-14
•
Granted: 1979-02-06
•
Expires: 1997-11-14
Abstract
Abstract An especially high strength, high temperature, economical material useful for insulation is preferably made by making up a mix having the following proportions in parts by weight: 20-50 parts expanded perlite; 0.5-4 parts sodium fluosilicate; 0.2-5 parts fiber material; a water solution having 9.5-19 parts total of solids content of sodium or potassium silicate; 2-9 parts zinc oxide; and water which, along with the water in the sodium silicate solution totals 21.5-67 parts; thereafter storing the mix under cover for less than 21/2 hours, compressing the mix to a desired form, and curing and drying it by heating.
Inventors
- 👤 Edward G. Vogel
- 👤 Rodney C. Westlund
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:25
CPC Classifications
F; F16; F16L; F16L59/00; F16L59/02; F16L59/021; F16L59/024; C; C04; C04B; C04B28/00; C04B28/24; C04B28/26; Y; Y10; Y10S; Y10S106/00; Y10S106/01
Claims Analysis
Total Claims: 40
Claim 1
Independent Claim
86 words
A coherent rigid solid material made from a mixture subjected to heat so as to reduce the original content of water, said mixture comprising the following parts by weight: expanded perlite 20 through 50 parts; sodium silicate or potassium silicate including 9.5 through 19 parts solids content of sodium silicate itself; zinc oxide 2 through 9 parts; sodium fluosilicate 1 through 6 parts; and water, to make a total of water, including any that may be associated with the sodium silicate of 21.5 through 67 parts.
Claim 2
Dependent Claim
86 words
A coherent rigid solid material made from a mixture subjected to heat so as to reduce the original content of water, said mixture comprising the following parts by weight: expanded perlite 20 through 50 parts; sodium silicate or potassium silicate including 9.5 through 19 parts solids content of sodium silicate itself; zinc oxide 2 through 9 parts; sodium fluosilicate 1 through 6 parts; and water, to make a total of water, including any that may be associated with the sodium silicate of 21.5 through 67 parts.
Claim 3
Dependent Claim
16 words
The material of claim 1 wherein the mixture further comprises an organic or inorganic fiber material.
Claim 4
Dependent Claim
48 words
The material of claim 2 wherein the fiber material is from a class comprising 1 through 5 parts fiberglass, 0.2 through 1.5 parts heat resistant nylon, 1 through 5 parts mineral wool and 1 through 5 parts of netting, all by weight as a part of the mixture.
Claim 5
Dependent Claim
43 words
The material of claim 3 wherein said netting comprises fibers of a thickness in the ranges of 0.007 to 0.125 inches, openings having areas in the range of 0.06 to 1 square inch and weight of less than l pound per square inch.
Claim 6
Dependent Claim
25 words
The material of claim 3 wherein said fibers of said class exclusive of said netting has an average fiber length of 1/8 through 1 inch.
Claim 7
Dependent Claim
55 words
The material of claim 1 wherein the mixture comprises the following composition by weight: expanded perlite 29 through 45 parts; sodium silicate 11.5 through 18 parts; zinc oxide 3 through 8 parts; and water, to make a total of water, including any that may be associated with the sodium silicate, of 26.5 through 57 parts.
Claim 8
Dependent Claim
55 words
The material of claim 1 wherein the mixture comprises the following composition by weight: expanded perlite 36 through 42 parts; sodium silicate 14.5 through 16.5 parts; zinc oxide 4.5 through 6.8 parts; and water, to make a total of water, including any that may be associated with the sodium silicate, of 32.5 through 43.5 parts.
Claim 9
Dependent Claim
27 words
The material of claim 1 in which the expanded perlite of the mixture has a dry bulk density of 2 through 3 1/2 pounds per cubic foot.
Claim 10
Dependent Claim
22 words
The material of claim 1 in which the zinc oxide of the mixture has an average fineness of not over 0.5 microns.
Claim 11
Dependent Claim
23 words
The material of claim 1 in which the zinc oxide of the mixture has an average fineness of from 0.1 through 0.2 microns.
Claim 12
Dependent Claim
17 words
The material of claim 1 wherein the perlite has an AFS Fineness No. of 70 through 120.
Claim 13
Dependent Claim
27 words
The material of claim 1 in which the sodium silicate has a proportion of silicon dioxide to sodium oxide of 3.1 to 1 through 3.4 to 1.
Claim 14
Dependent Claim
27 words
The material of claim 1 in which the potassium silicate has a proportion of silicon dioxide to sodium dioxide of 2.0 to 1 through 2.7 to 1.
Claim 15
Dependent Claim
27 words
The material of claim 1 in which the sodium silicate is introduced to the mix in a solution have a solids content of 36 to 44 percent.
Claim 16
Dependent Claim
26 words
The material of claim 1 in which the potassium silicate is introduced to the mix in a solution having solids content of 24 to 35 percent.
Claim 17
Dependent Claim
62 words
The material of claim 1 in which the mixture is formed by bringing together a dry powder material including the perlite and a slurry including the sodium silicate, zinc oxide and water and mixing the powder and the slurry at least to the time the mix appears damp and dustfree, and short of the time the mix begins shrinking substantially in volume.
Claim 18
Dependent Claim
41 words
The material of claim 1 in which after the mixing of mixture is completed the mixture is held in storage for a period not exceeding 2 1/2 hours so as to permit the material to be formed into shape under compression.
Claim 19
Dependent Claim
34 words
The material of claim 1 in which between the time of making up the mixture and the time of the subjecting of the material to heat, the material is compressed under vibration into shape.
Claim 20
Dependent Claim
39 words
The material of claim 1 in which between the time of making up the mixture and the time of the subjecting of the material to heat, the material is compressed into shape in a plurality of separate compression steps.
Claim 21
Dependent Claim
30 words
The material of claim 1 in which between the time of making up the mixture and the time of subjecting the material to heat, the material is blown into shape.
Claim 22
Dependent Claim
20 words
The material of claim 1, in which the subjection of the material to heat is at 93° through 99° C.
Claim 23
Dependent Claim
38 words
The material of claim 1 in which the subjection of the material to heat is in a hot air oven at 93° C. through 99° C. for four hours for each inch of minimum dimension of the shape.
Claim 24
Dependent Claim
16 words
The material of claim 1 in which the material is subjected to heat by microwave energy.
Claim 25
Dependent Claim
23 words
The material of claim 1 having a bulk density of 13.0 to 14.0 lb. per cubic foot when subjected to ASTM test C-303.
Claim 26
Dependent Claim
18 words
The material of claim 1 characterized by less than 1% linear change when subjected to ASTM test C-356.
Claim 27
Dependent Claim
18 words
The material of claim 1 characterized by less than 4% weight loss when subjected to ASTM test C-356.
Claim 28
Dependent Claim
38 words
The material of claim 1 characterized by a flexural strength in excess of 45 lb. per square inch for a bulk density of less than 13.5 lb. per cubic foot when tested in accordance with ASTM test C-303.
Claim 29
Dependent Claim
44 words
The material of claim 1 characterized by thermal conductivities of less than 0.53, 0.65 and 0.75 Btu's per inch of thickness per square foot per degree F at 500° F, 700° F, and 900° F respectively when tested in accordance with ASTM test C-777.
Claim 30
Dependent Claim
21 words
The material of claim 1 characterized by a surface smoother than SIS-3 on the official Alloy Casting Institute Surface Indicator Scale.
Claim 31
Dependent Claim
27 words
The material of claim 1 characterized by a surface at least as smooth as or smoother than SIS-2 on the official Alloy Casting Institute Surface Indicator Scale.
Claim 32
Dependent Claim
18 words
The material of claim 1 comprising a plurality of separable segments, said segments comprising mating tongues and grooves.
Claim 33
Dependent Claim
35 words
The material of claim 28 wherein said segments form a hollow tubular configuration having separable surfaces extending substantially parallel to the axis of the tubular configuration, said tongues and grooves being formed in said surfaces.
Claim 34
Dependent Claim
80 words
A coherent rigid solid material made from a mixture subjected to heat so as to reduce the original content of water, said mixture comprising the following parts by weight: expanded perlite 20 through 50 parts; sodium silicate or potassium silicate including 9.5 through 19 parts solids content of sodium silicate itself; zinc oxide 3 through 8 parts; and water, to make a total of water, including any that may be associated with the sodium silicate of 21.5 through 67 parts.
Claim 35
Dependent Claim
80 words
A coherent rigid solid material made from a mixture subjected to heat so as to reduce the original content of water, said mixture comprising the following parts by weight: expanded perlite 20 through 50 parts; sodium silicate or potassium silicate including 9.5 through 19 parts solids content of sodium silicate itself; zinc oxide 3 through 8 parts; and water, to make a total of water, including any that may be associated with the sodium silicate of 21.5 through 67 parts.
Claim 36
Dependent Claim
12 words
The material of claim 33 wherein the mixture comprises a solidifying agent.
Claim 37
Dependent Claim
16 words
The material of claim 34 wherein the solidifying agent comprises 1 through 6 parts sodium fluosilicate.
Claim 38
Dependent Claim
12 words
The material of claim 34 wherein the solidifying agent comprises carbon dioxide.
Claim 39
Dependent Claim
22 words
The material of claim 36 in which the zinc oxide of the mixture has an average fineness of not over 0.5 microns.
Claim 40
Dependent Claim
23 words
The material of claim 36 in which the zinc oxide of the mixture has an average fineness of from 0.1 through .2 microns.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-05 | 1982-08-07 | 1983-02-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-05 | 1986-08-07 | 1987-02-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-05 | 1990-08-07 | 1991-02-06 | $7700.00 | Window Closed / Lapsed |