Magnetic recording material
Assignee: Fujifilm Holdings Corp
•
Filing: 1977-03-09
•
Granted: 1979-01-16
•
Expires: 1997-03-09
Abstract
Abstract A magnetic recording material, which comprises a non-magnetic support having thereon a magnetic layer containing ferromagnetic powder dispersed in a binder, with the magnetic layer containing an organic silicone compound represented by the following general formula (I); ##STR1## wherein R, R' and R", which may be the same or different, each has 7 to 21 carbon atoms and represents an alkyl group, an alkenyl group, an alkadienyl group, an alkatrienyl group or an alkatetraenyl group, m represents an integer of 1 to 100; n represents an integer of 0 to 250; and m+n≦300 and m≧n/5.
Inventors
- 👤 Hiroshi Ogawa
- 👤 Matsuaki Nakamura
- 👤 Masashi Aonuma
- 👤 Yasuo Tamai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 04:51
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/71; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/25; Y10T428/256; Y10T428/257; Y10T428/26; Y10T428/266; Y10T428/31504; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
97 words
A magnetic recording material, which comprises a non-magnetic support having thereon a magnetic layer containing ferromagnetic powder dispersed in a binder, with the magnetic layer containing an organic silicone compound represented by the following general formula [I]; ##STR19## wherein R, R' and R", which may be the same or different, each has 7 to 21 carbon atoms and represents an alkyl group, an alkenyl group, an alkadienyl group, an alkatrienyl group or an alkatetraenyl group; m represents an integer of 1 to 100; n represents an integer of 0 to 250; and m + n≦300 and m≧n/5.
Claim 2
Dependent Claim
97 words
A magnetic recording material, which comprises a non-magnetic support having thereon a magnetic layer containing ferromagnetic powder dispersed in a binder, with the magnetic layer containing an organic silicone compound represented by the following general formula [I]; ##STR19## wherein R, R' and R", which may be the same or different, each has 7 to 21 carbon atoms and represents an alkyl group, an alkenyl group, an alkadienyl group, an alkatrienyl group or an alkatetraenyl group; m represents an integer of 1 to 100; n represents an integer of 0 to 250; and m + n≦300 and m≧n/5.
Claim 3
Dependent Claim
27 words
The magnetic recording material of claim 1, wherein m + n of said organic silicone compound represented by the general formula [I] is not more than 100.
Claim 4
Dependent Claim
45 words
The magnetic recording material of claim 1, wherein R, R' and R" in said organic silicone compound represented by the general formula [I] each represents an alkyl group, an alkenyl group, an alkadenyl group or an alkatrienyl group, each having 7 to 21 carbon atoms.
Claim 5
Dependent Claim
44 words
The magnetic recording material of claim 3, wherein R, R' and R" in said organic silicone compound represented by the general formula [I] each represents an alkyl group selected from the group consisting of a capryl group, a myristyl group and a behenyl group.
Claim 6
Dependent Claim
41 words
The magnetic recording material of claim 3, wherein R, R' and R" in said organic silicone compound represented by the general formula [I] each represents an alkenyl group selected from the group consisting of an oleyl group and a linolyl group.
Claim 7
Dependent Claim
44 words
The magnetic recording material of claim 1, wherein said organic silicone compound represented by the general formula [I] is present in said magnetic layer in an amount of about 0.1 to 5 parts by weight per 100 parts by weight of said ferromagnetic powder.
Claim 8
Dependent Claim
42 words
The magnetic recording material of claim 1, wherein the weight ratio of said ferromagnetic powder and said binder is such that about 10 to 400 parts by weight of the binder is present per 100 parts by weight of the ferromagnetic powder.
Claim 9
Dependent Claim
35 words
The magnetic recording material of claim 7, wherein about 0.5 to about 20 parts by weight of a dispersing agent is present in said magnetic layer per 100 parts by weight of said ferromagnetic powder.
Claim 10
Dependent Claim
34 words
The magnetic recording material of claim 7, wherein about 0.2 to about 20 parts by weight of a lubricant is present in said magnetic layer per 100 parts by weight of said ferromagnetic powder.
Claim 11
Dependent Claim
56 words
The magnetic recording material of claim 7, wherein about 0.5 to about 20 parts by weight of an abrasive having a Mohs' hardness of not less than 5 and having a mean particle size of about 0.05 to about 5 μm is present in said magnetic layer per 100 parts by weight of said ferromagnetic powder.
Claim 12
Dependent Claim
40 words
The magnetic recording material of claim 7, wherein about 0.02 to about 20 parts by weight of an electrically conductive powder is present as an antistatic agent in said magnetic layer per 100 parts by weight of said ferromagnetic powder.
Claim 13
Dependent Claim
40 words
The magnetic recording material of claim 7, wherein about 0.1 to about 10 parts by weight of a surface active agent is present as an antistatic agent in said magnetic layer per 100 parts by weight of said ferromagnetic powder.
Claim 14
Dependent Claim
42 words
The magnetic recording material of claim 1, wherein said ferromagnetic powder is a ferromagnetic iron oxide or ferromagnetic chromium dioxide, having an axial ratio of about 2:1 to about 20:1 and having an average length of about 0.2 to about 2.0 μm.
Claim 15
Dependent Claim
38 words
The magnetic recording material of claim 13, wherein said ferromagnetic iron oxide contains 0 to about 10 atomic % of at least one divalent metal selected from the group consisting of Cr, Mn, Co, Ni, Cu and Zn.
Claim 16
Dependent Claim
16 words
The magnetic recording material of claim 13, wherein said ferromagnetic iron oxide is Berthollide iron oxide.
Claim 17
Dependent Claim
16 words
The magnetic recording material of claim 14, wherein said ferromagnetic iron oxide is Berthollide iron oxide.
Claim 18
Dependent Claim
44 words
The magnetic recording material of claim 1, wherein said ferromagnetic powder is a ferromagnetic alloy powder comprising needle-like particles wherein about 2 to about 20 particles of a length of about 50 to about 1,000 A are connected to each other as a chain.
Claim 19
Dependent Claim
29 words
The magnetic recording material of claim 1, wherein said non-magnetic support is a film, a tape, or a sheet of a thickness of about 2 to about 50 μm.
Claim 20
Dependent Claim
27 words
The magnetic recording material of claim 1, wherein said non-magnetic support is a disc or a card of a thickness of about 0.5 to about 10 mm.
Claim 21
Dependent Claim
106 words
A magnetic recording material which comprises a non-magnetic support having thereon a magnetic layer containing ferromagnetic powder dispersed in a binder, with the magnetic layer containing 0.1 to 5 parts by weight per 100 parts ferromagnetic powder of an organic silicone compound represented by the following general formula [I]; ##STR20## wherein R, R' and R", which may be the same or different, each has 7 to 21 carbon atoms and represents an alkyl group, an alkenyl group, an alkadienyl group, or an alkatrienyl group; m represents an integer of 1 to 100; n represents an integer of 0 to 250; and m + n≦100 and m≧n/5.
Claim 22
Dependent Claim
106 words
A magnetic recording material which comprises a non-magnetic support having thereon a magnetic layer containing ferromagnetic powder dispersed in a binder, with the magnetic layer containing 0.1 to 5 parts by weight per 100 parts ferromagnetic powder of an organic silicone compound represented by the following general formula [I]; ##STR20## wherein R, R' and R", which may be the same or different, each has 7 to 21 carbon atoms and represents an alkyl group, an alkenyl group, an alkadienyl group, or an alkatrienyl group; m represents an integer of 1 to 100; n represents an integer of 0 to 250; and m + n≦100 and m≧n/5.
Claim 23
Dependent Claim
44 words
The magnetic recording material of claim 20, wherein R, R' and R" in said organic silicone compound represented by the general formula [I] each represents an alkyl group selected from the group consisting of a capryl group, a myristyl group and a behenyl group.
Claim 24
Dependent Claim
41 words
The magnetic recording material of claim 20, wherein R, R' and R" in said organic silicone compound represented by the general formula [I] each represents an alkenyl group selected from the group consisting of an oleyl group and a linolyl group.
Claim 25
Dependent Claim
42 words
The magnetic recording material of claim 20, wherein the weight ratio of said ferromagnetic powder and said binder is such that about 10 to 400 parts by weight of the binder is present per 100 parts by weight of the ferromagnetic powder.
References Cited (Backward Citations)
US3996407A
Cited
US4007314A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-15 | 1982-07-17 | 1983-01-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-15 | 1986-07-17 | 1987-01-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-15 | 1990-07-17 | 1991-01-16 | $7700.00 | Window Closed / Lapsed |