Hydration of silicate glasses in alcohol-water solutions
Assignee: Corning Glass Works
•
Filing: 1977-09-01
•
Granted: 1979-01-09
•
Expires: 1997-09-01
Abstract
Abstract The present invention is concerned with the production of sodium and/or potassium hydrosilicate glass bodies. The basis of the invention resides in the hydration of anhydrous sodium and/or potassium silicate glass bodies in aqueous alcohol solutions to impart enhanced mechanical strength and thermoplastic properties thereto. The hydrating process, which permits close control to be maintained over the water content absorbed in the glass, can be carried out in liquid solutions of water and relatively short chain, i.e. up to about five carbon atoms, aliphatic alcohols or in gaseous atmospheres of such solutions. An ion exchange reaction of Li+ ions or protons with Na+ and/or K+ ions can be promoted at temperatures above the transformation range of the hydrated glass, and an exchange of K+ ions for Na+ and/or Li+ ions at temperatures below the transformation range. The invention also contemplates treating sodium and/or potassium hydrosilicate glass bodies, produced through the previous hydration of sodium and/or potassium silicate glass bodies, in a gaseous or liquid alcohol or water-alcohol mixture to impart increased strength and impact resistance thereto and alter the absorbed water content therein. The aforementioned ion exchange reactions are also applicable here.
Inventors
- 👤 Roger F. Bartholomew
- 👤 William L. Haynes
- 👤 Leon M. Sanford
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 22:18
CPC Classifications
C; C03; C03C; C03C21/00; C03C21/001; C03C21/002; C03C23/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31; Y10T428/315
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
187 words
A method for making a hydrated glass body which can exhibit improved mechanical strength, impact resistance, Knoop hardness, and chemical durability which consists of the following steps: (a) melting a batch for an anhydrous glass consisting essentially, in mole percent on the oxide basis, of about 3-25% Na 2 O and/or K 2 O and 50-95% SiO 2 , the sum of those components constituting at least 55% of the total composition; (b) forming said melt into an anhydrous glass body of a desired geometry; (c) contacting at least a portion of said glass body with a short chain aliphatic alcohol-H 2 O containing liquid or gaseous environment in a closed autoclave system at a temperature greater than 100° C. but less than the softening point of the anhydrous glass and at a pressure in excess of atmospheric pressure for a period of time sufficient to hydrate and dealkalize at least said portion of said glass body in an amount effective to impart improved mechanical strength, impact resistance, Knoop hardness, and chemical durability thereto; and then (d) cooling said hydrated and dealkalized glass body to room temperature.
Claim 2
Independent Claim
187 words
A method for making a hydrated glass body which can exhibit improved mechanical strength, impact resistance, Knoop hardness, and chemical durability which consists of the following steps: (a) melting a batch for an anhydrous glass consisting essentially, in mole percent on the oxide basis, of about 3-25% Na 2 O and/or K 2 O and 50-95% SiO 2 , the sum of those components constituting at least 55% of the total composition; (b) forming said melt into an anhydrous glass body of a desired geometry; (c) contacting at least a portion of said glass body with a short chain aliphatic alcohol-H 2 O containing liquid or gaseous environment in a closed autoclave system at a temperature greater than 100° C. but less than the softening point of the anhydrous glass and at a pressure in excess of atmospheric pressure for a period of time sufficient to hydrate and dealkalize at least said portion of said glass body in an amount effective to impart improved mechanical strength, impact resistance, Knoop hardness, and chemical durability thereto; and then (d) cooling said hydrated and dealkalized glass body to room temperature.
Claim 3
Dependent Claim
53 words
A method according to claim 1 wherein said anhydrous glass consists essentially, in mole percent on the oxide basis, of about 10-17% Na 2 O and/or K 2 O, 5-20% PbO and/or ZnO, 0-5% Al 2 O 3 , 0-3% B 2 O 3 and/or BaO and/or MgO, and 72-82% SiO 2 .
Claim 4
Dependent Claim
19 words
A method according to claim 1 wherein said short chain aliphatic alcohol contains up to about five carbon atoms.
Claim 5
Dependent Claim
19 words
A method according to claim 1 wherein the volume ratio of alcohol/H 2 O ranges up to about 9:1.
Claim 6
Dependent Claim
60 words
A method according to claim 1 wherein up to about 5% by weight of a lithium compound is dissolved in said aliphatic alcohol-H 2 O containing environment and contact of said glass body with said aliphatic alcohol-H 2 O containing environment is made at a temperature between about the transformation range of the hydrated glass and about 50° C. thereabove.
Claim 7
Dependent Claim
59 words
A method according to claim 1 wherein up to about 5% by weight of acetic acid is dissolved in said aliphatic alcohol-H 2 O containing environment and contact of said glass body with said aliphatic alcohol-H 2 O containing environment is made at a temperature between about the transformation range of the hydrated glass and about 50° C. thereabove.
Claim 8
Dependent Claim
57 words
A method according to claim 1 wherein up to about 5% by weight of a potassium compound is dissolved in said aliphatic alcohol-H 2 O containing environment and contact of said glass body with said aliphatic alcohol-H 2 O containing environment is made at a temperature between 10°-75° C. below the transformation range of the hydrated glass.
Claim 9
Independent Claim
243 words
A method for making an hydrated glass body which can exhibit improved mechanical strength, impact resistance, Knoop hardness, and chemical durability which consists of the following steps: (a) melting a batch for an anhydrous glass consisting essentially, in mole percent on the oxide basis, of about 3-25% Na 2 O and/or K 2 O and 50-95% SiO 2 , the sum of those components constituting at least 55% of the total composition; (b) forming said melt into an anhydrous glass body of a desired geometry; (c) contacting at least a portion of said glass body with a gaseous or liquid H 2 -O-containing environment in a closed autoclave system at elevated temperatures and pressures for a period of time sufficient to hydrate at least said portion of said glass body having an amount of H 2 O absorbed therein effective to impart thermoplastic properties thereto; (d) contacting said hydrated portion of said glass body with a short chain aliphatic alcohol or short chain aliphatic alcohol-H 2 O containing liquid or gaseous environment in a closed autoclave system at a temperature between about 75° C. below the transformation range to about 50° C. thereabove at a pressure in excess of atmospheric pressure for a period of time sufficient to dealkalize said portion of said glass body in an amount effective to impart improved mechanical strength, impact resistance, Knoop hardness, and chemical durability thereto; and then (d) cooling said hydrated-dealkalized glass body to room temperature.
Claim 10
Independent Claim
243 words
A method for making an hydrated glass body which can exhibit improved mechanical strength, impact resistance, Knoop hardness, and chemical durability which consists of the following steps: (a) melting a batch for an anhydrous glass consisting essentially, in mole percent on the oxide basis, of about 3-25% Na 2 O and/or K 2 O and 50-95% SiO 2 , the sum of those components constituting at least 55% of the total composition; (b) forming said melt into an anhydrous glass body of a desired geometry; (c) contacting at least a portion of said glass body with a gaseous or liquid H 2 -O-containing environment in a closed autoclave system at elevated temperatures and pressures for a period of time sufficient to hydrate at least said portion of said glass body having an amount of H 2 O absorbed therein effective to impart thermoplastic properties thereto; (d) contacting said hydrated portion of said glass body with a short chain aliphatic alcohol or short chain aliphatic alcohol-H 2 O containing liquid or gaseous environment in a closed autoclave system at a temperature between about 75° C. below the transformation range to about 50° C. thereabove at a pressure in excess of atmospheric pressure for a period of time sufficient to dealkalize said portion of said glass body in an amount effective to impart improved mechanical strength, impact resistance, Knoop hardness, and chemical durability thereto; and then (d) cooling said hydrated-dealkalized glass body to room temperature.
Claim 11
Dependent Claim
53 words
A method according to claim 8 wherein said anhydrous glass consists essentially, in mole percent on the oxide basis, of about 10-17% Na 2 O and/or K 2 O, 5-20% PbO and/or ZnO, 0-5% Al 2 O 3 , 0-3% B 2 O 3 and/or BaO and/or MgO, and 72-82% SiO 2 .
Claim 12
Dependent Claim
19 words
A method according to claim 8 wherein said short chain aliphatic alcohol contains up to about five carbon atoms.
Claim 13
Dependent Claim
64 words
A method according to claim 8 wherein up to about 5% by weight of a lithium compound is dissolved in said aliphatic alcohol or aliphatic alcohol-H 2 O containing environment and contact of said glass body with said alcohol or alcohol-H 2 O containing environment is made at a temperature between about the transformation range of the hydrated glass and about 50° C. thereabove.
Claim 14
Dependent Claim
63 words
A method according to claim 8 wherein up to about 5% by weight of acetic acid is dissolved in said aliphatic alcohol or aliphatic alcohol-H 2 O containing environment and contact of said glass body with said alcohol or alcohol-H 2 O containing environment is made at a temperature between about the transformation range of the hydrated glass and about 50° C. thereabove.
Claim 15
Dependent Claim
61 words
A method according to claim 8 wherein up to about 5% by weight of a potassium compound is dissolved in said aliphatic alcohol or aliphatic alcohol-H 2 O containing environment and contact of said glass body with said alcohol or alcohol-H 2 O containing environment is made at a temperature between 10°-75° C. below the transformation range of the hydrated glass.
References Cited (Backward Citations)
US2016892A
Cited
US3186816A
Cited
US3844754A
Cited
US3816107A
Cited
US3811853A
Cited
US3839226A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-08 | 1982-07-10 | 1983-01-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-08 | 1986-07-10 | 1987-01-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-08 | 1990-07-10 | 1991-01-09 | $7700.00 | Window Closed / Lapsed |