Hydrophilic polyurethane foams with good wet strength
Assignee: WR Grace and Co
•
Filing: 1977-02-28
•
Granted: 1978-11-28
•
Expires: 1997-02-28
Abstract
Abstract Disclosed herein is a polyurethane foam having good wet strength. The foam is prepared by reacting a urethane prepolymer with large amounts of water containing a poly(amino)urea and optionally other ingredients, e.g. surfactants. The poly(amino)urea is characterized as being the water soluble reaction product of a polyamine with a urethane prepolymer, said reaction product being further reacted with a crosslinking agent, e.g. epichlorohydrin.
Inventors
- 👤 Donald W. Larsen
- 👤 Louis L. Wood
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 10:44
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/83; C08G18/831; C08G18/08; C08G18/10; C08G18/12; C08G18/28; C08G18/40; C08G18/48; C08G18/4833; C08G18/50; C08G18/5021; C08G18/5036; C08G18/5042; C08G2110/00; C08G2110/0083; Y; Y10; Y10S; Y10S521/00; Y10S521/905
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
62 words
A method for preparing a hydrophilic foam having good wet strength comprising reacting, under foam-forming conditions: (A) a urethane prepolymer formed by capping a hydrophilic oxyalkylene polyol with an isocyanate; and (B) an aqueous dispersion containing from about 0.1 to about 5 parts of weight based on the weight of the prepolymer of an essentially linear polyurea reacted with a crosslinking agent.
Claim 2
Independent Claim
62 words
A method for preparing a hydrophilic foam having good wet strength comprising reacting, under foam-forming conditions: (A) a urethane prepolymer formed by capping a hydrophilic oxyalkylene polyol with an isocyanate; and (B) an aqueous dispersion containing from about 0.1 to about 5 parts of weight based on the weight of the prepolymer of an essentially linear polyurea reacted with a crosslinking agent.
Claim 3
Dependent Claim
21 words
A method as in claim 1 wherein the polyurea is the reaction product of a polyamine and a hydrophilic urethane prepolymer.
Claim 4
Dependent Claim
45 words
A method as in claim 1 wherein the reaction product of the polyurea with the crosslinking agent is water soluble and characterized as providing a viscosity of from about 200 to about 15,000 cps when dissolved in water at a concentration of 25 weight percent.
Claim 5
Dependent Claim
12 words
A method as in claim 1 wherein the crosslinking agent is epichlorohydrin.
Claim 6
Dependent Claim
12 words
A method as in claim 1 wherein the crosslinking agent is formalin.
Claim 7
Dependent Claim
22 words
A method as in claim 1 wherein the polyol portion of the prepolymer contains at least 40 mole percent of oxyethylene units.
Claim 8
Dependent Claim
22 words
A method as in claim 1 wherein the polyol portion of the prepolymer contains at least 75 mole percent of oxyethylene units.
Claim 9
Dependent Claim
17 words
A method as in claim 1 wherein the aqueous polyurea dispersion additionally has hydrophilic fibers dispersed therein.
Claim 10
Dependent Claim
54 words
A hydrophilic foam comprising the reaction product of: (A) a urethane prepolymer formed by capping a hydrophilic oxyalkylene polyol with an isocyanate; and (B) an aqueous dispersion containing from about 0.1 to about 5 parts of weight based on the weight of the prepolymer of an essentially linear polyurea reacted with a crosslinking agent.
Claim 11
Dependent Claim
54 words
A hydrophilic foam comprising the reaction product of: (A) a urethane prepolymer formed by capping a hydrophilic oxyalkylene polyol with an isocyanate; and (B) an aqueous dispersion containing from about 0.1 to about 5 parts of weight based on the weight of the prepolymer of an essentially linear polyurea reacted with a crosslinking agent.
Claim 12
Dependent Claim
21 words
A foam as in claim 9 wherein the polyurea is the reaction product of a polyamine and a hydrophilic urethane prepolymer.
Claim 13
Dependent Claim
45 words
A foam as in claim 9 wherein the reaction product of the polyurea with the crosslinking agent is water soluble and characterized as providing a viscosity of from about 200 to about 15,000 cps when dissolved in water at a concentration of 25 weight percent.
Claim 14
Dependent Claim
12 words
A foam as in claim 9 wherein the crosslinking agent is epichlorohydrin.
Claim 15
Dependent Claim
12 words
A foam as in claim 9 wherein the crosslinking agent is formalin.
Claim 16
Dependent Claim
22 words
A foam as in claim 9 wherein the polyol portion of the prepolymer contains at least 40 mole percent of oxyethylene units.
Claim 17
Dependent Claim
22 words
A foam as in claim 9 wherein the polyol portion of the prepolymer contains at least 75 mole percent of oxyethylene units.
Claim 18
Dependent Claim
17 words
A foam as in claim 9 wherein the aqueous polyurea dispersion additionally has hydrophilic fibers dispersed therein.
References Cited (Backward Citations)
US3002937A
Cited
US3836493A
Cited
US3892696A
Cited
US3953406A
Cited
US3854535A
Cited
US3903232A
Cited
US4073840A
Cited
US3939105A
Cited
US3940542A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-27 | 1982-05-29 | 1982-11-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-27 | 1986-05-29 | 1986-11-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-27 | 1990-05-29 | 1990-11-28 | $7700.00 | Window Closed / Lapsed |