Method for forming a fiber reinforced foam article
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1975-04-07
•
Granted: 1978-02-14
•
Expires: 1995-04-07
Abstract
Abstract A fiber reinforced foam having a predetermined uniform distribution of fibers throughout the skin and core is prepared by slurrying fibers with a major component of a foamable resin composition, thereafter adding the balance of the components necessary to form a foamable composition and allowing the so formed composition to foam under controlled temperatures and pressures.
Inventors
- 👤 Glen E. W. Saidla
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 22:18
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/02; B29C44/12; B29B; B29B7/00; B29B7/80; B29B7/88; B29B7/90; B29B7/905; C; C08; C08J; C08J9/00; C08J9/0085; B29K; B29K2105/00; B29K2105/06; B29K2105/12; Y; Y10; Y10S; Y10S264/00; Y10S264/17; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249986
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
157 words
A method of forming a foam article having a predetermined distribution of randomly oriented fiber filaments of staple length throughout the article and a substantially uniform weight ratio of fiber filaments to foam resin throughout comprising: (a) adding fibers of staple length to at least one major component of a foamable resin composition thereby forming a fiber slurry; b. pumping said slurry through a circulating line for a time sufficient to separate the fibers into discrete fiber filaments and to wet said fiber filaments with said major component while maintaining the structural integrity of said fiber filament thereby forming a substantially uniform dispersion of randomly oriented fibers in said component; c. mixing said dispersion with the balance of components necessary to form a foamable resin composition; d. thereafter allowing the resin composition to foam in an appropriate mold whereby a foam article is provided having a substantially uniform weight ratio of fiber filaments to foam resin throughout.
Claim 2
Independent Claim
157 words
A method of forming a foam article having a predetermined distribution of randomly oriented fiber filaments of staple length throughout the article and a substantially uniform weight ratio of fiber filaments to foam resin throughout comprising: (a) adding fibers of staple length to at least one major component of a foamable resin composition thereby forming a fiber slurry; b. pumping said slurry through a circulating line for a time sufficient to separate the fibers into discrete fiber filaments and to wet said fiber filaments with said major component while maintaining the structural integrity of said fiber filament thereby forming a substantially uniform dispersion of randomly oriented fibers in said component; c. mixing said dispersion with the balance of components necessary to form a foamable resin composition; d. thereafter allowing the resin composition to foam in an appropriate mold whereby a foam article is provided having a substantially uniform weight ratio of fiber filaments to foam resin throughout.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein the foamable thermoset resin is a polyurethane resin.
Claim 4
Dependent Claim
38 words
The method of claim 2 wherein the fiber is mixed with a polyisocyanate to form a fiber slurry, and said fiber slurry is mixed with a polyol, catalyst and blowing agent whereby said foamable polyurethane resin is obtained.
Claim 5
Dependent Claim
21 words
The method of claim 1 wherein the fiber is selected from the group consisting of glass, carbon, graphite, and boron fibers.
Claim 6
Dependent Claim
10 words
The method of claim 4 wherein the fiber is glass.
Claim 7
Dependent Claim
29 words
The method of claim 1 wherein the fiber is glass and is present in an amount greater than 10 wt. % based on the total weight of the resin.
Claim 8
Dependent Claim
163 words
In the method of forming a polyurethane foam article having a low density core and a high density skin from at least a two component polyurethane resin system, the improvement comprising adding glass fibers in the range from about 1 wt. % to about 50 wt. % of glass fibers based on the total weight of resin system to one of the two components; pumping said fibers and said component through a circulating line for a time sufficient to separate said fibers into discrete randomly oriented fiber filaments and to wet said fiber filaments with said component without destroying the structural integrity of said fibers thereby forming a substantially uniformly dispersion of said fibers in said component; mixing said dispersion with said second component whereby a foamable composition is obtained; allowing said foamable composition to form in a closed mold at a pressure of from about 10 psi to about 100 psi whereby a fiber-reinforced integral skin is formed on a fiber-reinforced core.
Claim 9
Dependent Claim
163 words
In the method of forming a polyurethane foam article having a low density core and a high density skin from at least a two component polyurethane resin system, the improvement comprising adding glass fibers in the range from about 1 wt. % to about 50 wt. % of glass fibers based on the total weight of resin system to one of the two components; pumping said fibers and said component through a circulating line for a time sufficient to separate said fibers into discrete randomly oriented fiber filaments and to wet said fiber filaments with said component without destroying the structural integrity of said fibers thereby forming a substantially uniformly dispersion of said fibers in said component; mixing said dispersion with said second component whereby a foamable composition is obtained; allowing said foamable composition to form in a closed mold at a pressure of from about 10 psi to about 100 psi whereby a fiber-reinforced integral skin is formed on a fiber-reinforced core.
Claim 10
Independent Claim
205 words
A method of forming a polyurethane foam article having a predetermined distribution of randomly oriented glass fiber filaments throughout the article and a substantially uniform weight ratio of fiber filaments to foam resin throughout comprising: (a) adding to at least one major component of a foamable polyurethane resin composition glass fiber bundles in an amount ranging from about 1% to about 50 weight % based on the total weight of the polyurethane resin composition, thereby forming a fiber slurry, said fiber slurry, said fiber bundles consisting of a plurality of filaments in a bundle and said filaments being of staple length; b. pumping said fiber slurry through a circulating line for a time sufficient to separate the fibers in the bundles into discrete fiber filaments and to wet said fiber filaments with said major component while maintaining the structural integrity of said fibers, thereby forming a substantially uniform dispersion of randomly oriented staple length glass fibers in said component; c. mixing said dispersion with the balance of components necessary to form a foamable polyurethane resin composition; d. thereafter allowing the resin composition to foam in an appropriate mold whereby said foam article has a substantially uniform weight ratio of fiber filaments to foam resin throughout.
Claim 11
Independent Claim
205 words
A method of forming a polyurethane foam article having a predetermined distribution of randomly oriented glass fiber filaments throughout the article and a substantially uniform weight ratio of fiber filaments to foam resin throughout comprising: (a) adding to at least one major component of a foamable polyurethane resin composition glass fiber bundles in an amount ranging from about 1% to about 50 weight % based on the total weight of the polyurethane resin composition, thereby forming a fiber slurry, said fiber slurry, said fiber bundles consisting of a plurality of filaments in a bundle and said filaments being of staple length; b. pumping said fiber slurry through a circulating line for a time sufficient to separate the fibers in the bundles into discrete fiber filaments and to wet said fiber filaments with said major component while maintaining the structural integrity of said fibers, thereby forming a substantially uniform dispersion of randomly oriented staple length glass fibers in said component; c. mixing said dispersion with the balance of components necessary to form a foamable polyurethane resin composition; d. thereafter allowing the resin composition to foam in an appropriate mold whereby said foam article has a substantially uniform weight ratio of fiber filaments to foam resin throughout.
References Cited (Backward Citations)
US1952638A
Cited
US2855021A
Cited
US2764566A
Cited
US3099516A
Cited
US3182104A
Cited
US3256218A
Cited
US3443007A
Cited
US3608008A
Cited
DE2218418A1
Cited
US3843100A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-13 | 1981-08-15 | 1982-02-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-13 | 1985-08-15 | 1986-02-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-13 | 1989-08-15 | 1990-02-14 | $7700.00 | Window Closed / Lapsed |