Process for the manufacture of oriented sheets of thermoplastic resin which are protected against the action of ultraviolet rays
Assignee: Solvay SA
•
Filing: 1977-07-08
•
Granted: 1978-11-21
•
Expires: 1997-07-08
Abstract
Abstract Process for the manufacture of oriented sheets of thermoplastic resin which are protected against the action of ultraviolet rays by applying, to at least one of the faces of the sheet, a solution comprising at least a solvent exerting a swelling action on the resin and at least one anti-UV agent which is soluble in the solvent and causing the solvent to evaporate. The treatment is applied before the orienting step by stretching, the sheets being at a temperature favoring orientation by stretching.
Inventors
- 👤 Axel Lempkowicz
- 👤 Jean Nanoux
- 👤 Jean-Francois Bequet
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 16:41
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/04; C08J7/06; C08J7/065
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
159 words
Process for the manufacture of an oriented sheet of thermoplastic resin which is protected against the action of ultraviolet rays, which comprises extruding a sheet from the resin, conditioning this sheet to a temperature favoring orientation by stretching, stretching the conditioned sheet in at least one direction so as to induce molecular orientation tensions in the sheet, and cooling the stretched sheet under tension to a temperature below the second order transition temperature of the resin, comprising: before stretching the conditioned sheet, applying to at least one of the faces of the sheet a solution comprising at least one solvent exerting a swelling action on the resin and between 5 and 40% weight of at least one anti-UV agent which is soluble in the solvent, the amount of solution deposited per square metre of surface of the sheet being between 20 and 200 g, and evaporating the solvent less than 60 seconds after applying the solution to the sheet.
Claim 2
Dependent Claim
159 words
Process for the manufacture of an oriented sheet of thermoplastic resin which is protected against the action of ultraviolet rays, which comprises extruding a sheet from the resin, conditioning this sheet to a temperature favoring orientation by stretching, stretching the conditioned sheet in at least one direction so as to induce molecular orientation tensions in the sheet, and cooling the stretched sheet under tension to a temperature below the second order transition temperature of the resin, comprising: before stretching the conditioned sheet, applying to at least one of the faces of the sheet a solution comprising at least one solvent exerting a swelling action on the resin and between 5 and 40% weight of at least one anti-UV agent which is soluble in the solvent, the amount of solution deposited per square metre of surface of the sheet being between 20 and 200 g, and evaporating the solvent less than 60 seconds after applying the solution to the sheet.
Claim 3
Dependent Claim
38 words
Process according to claim 1, wherein the amount of solution deposited by coating on one face is such that the amount of anti-UV agent deposited per square metre of sheet before stretching varies between 2 and 50 g.
Claim 4
Dependent Claim
28 words
Process according to claim 1, wherein the solvent is selected from the group consisting of the chlorinated solvents derived from hydrocarbons containing from 1 to 3 carbon atoms.
Claim 5
Dependent Claim
19 words
Process according to claim 1, wherein the sheet to be treated consists of a resin based on polyvinyl chloride.
Claim 6
Dependent Claim
40 words
Process according to claim 4, wherein the solution consists of a mixture of 1,1,2-trichloroethane and tetrachloroethylene in a weight ratio of between 1.5 and 3, containing from 10 to 40 g of an anti-UV agent per 100 g of solution.
Claim 7
Dependent Claim
13 words
Process according to claim 4, wherein the anti-UV agent is a benzophenone derivative.
Claim 8
Dependent Claim
31 words
Process according to claim 1, wherein the faces of the sheet to which the solution is applied are, at the time of application, at a temperature which favors orientation by stretching.
Claim 9
Dependent Claim
33 words
Process according to claim 1, wherein the solvent is evaporated by passing through a chamber under reduced pressure, the chamber being maintained at the temperature chosen for the treatment of orientation by stretching.
References Cited (Backward Citations)
US2919259A
Cited
US3254146A
Cited
US3446886A
Cited
US3582398A
Cited
US3744952A
Cited
US3834853A
Cited
US3892889A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-20 | 1982-05-22 | 1982-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-20 | 1986-05-22 | 1986-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-20 | 1990-05-22 | 1990-11-21 | $7700.00 | Window Closed / Lapsed |