Preparation of solid titanium trichloride
Assignee: Mitsubishi Chemical Corp
•
Filing: 1977-08-01
•
Granted: 1978-09-19
•
Expires: 1997-08-01
Abstract
Abstract Solid titanium trichloride in the form of fine granules having low aluminum compound content, which is suitable as a catalyst for polymerization of alpha -olefins, especially, propylene is obtained as a precipitate by heating liquefied titanium trichloride in the presence of a liberating agent, and separating the thus formed precipitate. The liquified titanium trichloride is preferably prepared with an reducing titanium tetrachloride by organic aluminum compound in the presence of ether and hydrocarbon.
Inventors
- 👤 Kazuo Yamaguchi
- 👤 Genjiro Kakogawa
- 👤 Masayoshi Hasuo
- 👤 Nobuaki Goko
- 👤 Yasuo Maruyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:16
CPC Classifications
C; C08; C08F; C08F10/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
186 words
A process for the production of solid purple titanium trichloride suitable for use as a catalyst for polymerization of an α-olefin, which comprises: forming a homogeneous solution or mixture comprising titanium trichloride by treating titanium tetrachloride with an organoaluminum compound represented by the generic formula, AlR 3 n X 3-n , wherein R 3 denotes a hydrocarbon radical of 1 to 20 carbon atoms, n is a number of the value of 1 to 3 and X a halogen atom, in the presence of an ether and a hydrocarbon solvent selected from the group consisting of alicyclic and aromatic hydrocarbon solvents; said ether having the generic formula, R 1 --O--R 2 , wherein R 1 and R 2 are individually an alkyl or alkenyl group and at least one of R 1 and R 2 is an alkyl or alkenyl group having five or less carbon atoms; heating the thus obtained homogeneous solution or mixture in the presence of a Lewis acid at a temperature in the range of 20°-150° C to cause precipitation of a finely granulated purple solid titanium trichloride; and separating the precipitate.
Claim 2
Dependent Claim
186 words
A process for the production of solid purple titanium trichloride suitable for use as a catalyst for polymerization of an α-olefin, which comprises: forming a homogeneous solution or mixture comprising titanium trichloride by treating titanium tetrachloride with an organoaluminum compound represented by the generic formula, AlR 3 n X 3-n , wherein R 3 denotes a hydrocarbon radical of 1 to 20 carbon atoms, n is a number of the value of 1 to 3 and X a halogen atom, in the presence of an ether and a hydrocarbon solvent selected from the group consisting of alicyclic and aromatic hydrocarbon solvents; said ether having the generic formula, R 1 --O--R 2 , wherein R 1 and R 2 are individually an alkyl or alkenyl group and at least one of R 1 and R 2 is an alkyl or alkenyl group having five or less carbon atoms; heating the thus obtained homogeneous solution or mixture in the presence of a Lewis acid at a temperature in the range of 20°-150° C to cause precipitation of a finely granulated purple solid titanium trichloride; and separating the precipitate.
Claim 3
Dependent Claim
13 words
The process of claim 1, wherein said organoaluminum compound is dialkyl aluminum halide.
Claim 4
Dependent Claim
22 words
The process of claim 1, wherein said ether is dibutylether, said hydrocarbon solvent is toluene, and said organoaluminum compound is diethylaluminum chloride.
Claim 5
Dependent Claim
31 words
The process of claim 1, wherein said ether is added in an amount so that the molar ratio of ether to titanium tetrachloride is within the range of 1:0.05 to 1:5.
Claim 6
Dependent Claim
16 words
The process of claim 4, wherein said ratio is within the range of 1:0.25 to 1:2.5.
Claim 7
Dependent Claim
42 words
The process of claim 1, wherein said organoaluminum compound is used in an amount so that the molar ratio of titanium in the titanium tetrachloride to the residue R 3 in organoaluminum compound is within the range of from 1:0.1 to 1:50.
Claim 8
Dependent Claim
31 words
The process of claim 6, wherein said ratio of titanium in the titanium tetrachloride to the residue R 3 in organoaluminum compound is within the range of from 1:0.3 to 1:10.
References Cited (Backward Citations)
GB960232A
Cited
US3492281A
Cited
US3681256A
Cited
ZA721245B
Cited
US4008175A
Cited
US4007133A
Cited
US3984350A
Cited
US4060593A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-18 | 1982-03-20 | 1982-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-18 | 1986-03-20 | 1986-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-18 | 1990-03-20 | 1990-09-19 | $7700.00 | Window Closed / Lapsed |