Method for effecting reverse shape memory phenomena in Cu-Zn-Si brass alloy
Assignee: Essex Solutions USA LLC
•
Filing: 1976-10-04
•
Granted: 1978-07-11
•
Expires: 1996-10-04
Abstract
Abstract A method for making an integrated circuit package includes the steps of fabricating lead frames from a copper-zinc-silicon beta brass alloy and soldering the leads thereof to semi-conductor chips by use of the shape memory and reverse shape memory characteristic of the alloy. The composition of the lead frame material and the choice and sequence of fabrication steps may be varied.
Inventors
- 👤 Horace Pops
- 👤 Barry C. Johnson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:43
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/006; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49121
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
127 words
A method of heat treating a brass composition of about 62-65% by weight copper, 35-38% by weight zinc and 0.3-0.5% by weight silicon to provide a reverse shape memory effect comprising the steps of: betatizing said material; deforming said material up to 10% by bending at a temperature below the martensite transformation temperature of said material or just slightly above said temperature; heating said deformed material to a temperature of less than 400° C. and above the martensite transformation temperature and maintaining said material isothermally whereby shape memory effect returns said material substantially toward the original undeformed condition; and subsequently heating said material to a temperature in the range of 230° to 550° C. whereby said material reforms to the deformed condition by reverse shape memory effect.
Claim 2
Independent Claim
127 words
A method of heat treating a brass composition of about 62-65% by weight copper, 35-38% by weight zinc and 0.3-0.5% by weight silicon to provide a reverse shape memory effect comprising the steps of: betatizing said material; deforming said material up to 10% by bending at a temperature below the martensite transformation temperature of said material or just slightly above said temperature; heating said deformed material to a temperature of less than 400° C. and above the martensite transformation temperature and maintaining said material isothermally whereby shape memory effect returns said material substantially toward the original undeformed condition; and subsequently heating said material to a temperature in the range of 230° to 550° C. whereby said material reforms to the deformed condition by reverse shape memory effect.
Claim 3
Dependent Claim
48 words
The method of claim 1 wherein the step of heating the deformed material comprises heating to about 200° C. and the subsequent heating step comprises heating the material to about 450° C. and maintaining the material at a temperature of about 450° C. for less than 2 minutes.
References Cited (Backward Citations)
US3783037A
Cited
US4014716A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-10 | 1982-01-09 | 1982-07-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-10 | 1986-01-09 | 1986-07-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-10 | 1990-01-09 | 1990-07-11 | $7700.00 | Window Closed / Lapsed |