Expired / Lapsed
US
⏱️ 0.0 years remaining
Wrought brass alloy having a low spring back coefficient and shape memory effect
Assignee: Essex International Inc
•
Filing: 1974-09-20
•
Granted: 1977-03-29
•
Expires: 1994-09-20
Abstract
Abstract An improved ternary brass alloy includes silicon as the additive material. The composition limits of the constituents of the brass are fixed by two factors: (1) the M s or Martensite transformation temperature, and (2) the brass must be a totally beta phase above 454° C. The composition may be betatized, that is, heated at approximately 800° C. and quenched at a fast rate so that the beta phase is retained in order to provide material having a shape memory effect, a low spring back coefficient and super elastic properties. A continuous betatizing and quenching process may be utilized in the manufacture of strip and sheet products. Alternatively, the composition may be hot worked between 600° and 700° C. and then cold worked to provide a material having a low spring back coefficient.
Inventors
- 👤 Amado Cabo
- 👤 Horace Pops
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 13:40
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/006
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
185 words
An improved method of manufacture for a wrought, polycrystalline brass alloy having a shape memory characteristic and a low spring back coefficient comprising the steps of providing a mixture of constituents consisting essentially of about 0.56 to 6.6, atomic % silicon, 23.5 to 40.5, atomic % zinc and the balance copper, combining said constituents in a substantially homogeneous alloy composition to provide an alloy having a stable beta phase above 454° C. and having a Martensite transformation temperature defined approximately by the formula M s (° K) +3280-80Zn-120Si where M s (° K) is the Martensite transformation temperature in ° K, Zn is atomic percent zinc, and Si is atomic percent silicon, and where the Martensite transformation temperature is substantially at or below the temperature of normal use of said alloy, fabrication of said alloy by working said alloy to insure a polycrystalline structure, heating to effect betatizing wherein essentially all of said alloy is in the beta phase and subsequently quenching said alloy to a temperature at or below the temperature of normal use of said alloy to retain beta phase in said alloy.
Claim 2
Dependent Claim
185 words
An improved method of manufacture for a wrought, polycrystalline brass alloy having a shape memory characteristic and a low spring back coefficient comprising the steps of providing a mixture of constituents consisting essentially of about 0.56 to 6.6, atomic % silicon, 23.5 to 40.5, atomic % zinc and the balance copper, combining said constituents in a substantially homogeneous alloy composition to provide an alloy having a stable beta phase above 454° C. and having a Martensite transformation temperature defined approximately by the formula M s (° K) +3280-80Zn-120Si where M s (° K) is the Martensite transformation temperature in ° K, Zn is atomic percent zinc, and Si is atomic percent silicon, and where the Martensite transformation temperature is substantially at or below the temperature of normal use of said alloy, fabrication of said alloy by working said alloy to insure a polycrystalline structure, heating to effect betatizing wherein essentially all of said alloy is in the beta phase and subsequently quenching said alloy to a temperature at or below the temperature of normal use of said alloy to retain beta phase in said alloy.
Claim 3
Dependent Claim
15 words
The process of claim 1 including the additional step of working said alloy after quenching.
Claim 4
Dependent Claim
28 words
The process of claim 1 wherein said quench is at a rate of more than 500° C. per second to prevent substantially all decomposition of the beta phase.
Claim 5
Dependent Claim
27 words
The process of claim 1 wherein the step of working said alloy includes the step of fabricating said alloy into a manufactured component shape prior to betatizing.
Claim 6
Dependent Claim
20 words
The process of claim 1 including the step of working said alloy below the Martensite transformation temperature subsequent to quenching.
Claim 7
Dependent Claim
19 words
The process of claim 5 including the step of heating said alloy subsequent to working below said Martensite temperature.
References Cited (Backward Citations)
US3783037A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-28 | 1980-09-27 | 1981-03-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-28 | 1984-09-27 | 1985-03-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-28 | 1988-09-27 | 1989-03-29 | $7700.00 | Window Closed / Lapsed |