Method of manufacturing semiconductor devices in which oxide regions are formed by an oxidation mask disposed directly on a substrate damaged by ion implantation
Assignee: International Business Machines Corp
•
Filing: 1977-06-03
•
Granted: 1978-07-04
•
Expires: 1997-06-03
Abstract
Abstract A method of manufacturing semiconductor devices of the type wherein regions of oxide such as silicon oxide recessed or inset in a silicon substrate are formed by oxidation of the silicon with the use of a masking layer protecting locally against the oxidation. In order to prevent the formation of a projecting oxide beak under the masking layer a nitride oxidation mask is applied directly to the substrate which has been previously ion-implanted to a controlled depth and then annealed to generate a dense dislocation network array on the substrate surface to prevent mechanical stress defects which normally would occur when a nitride mask is applied directly to a substrate.
Inventors
- 👤 Billy Lee Crowder
- 👤 William Ralph Hunter
- 👤 Douglas William Ormond, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 09:27
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10P14/61; H10P14/65; H10P14/6502; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10P30/208; H10P36/00; H10P36/03; H10P95/00; H10P95/40; H10P95/402; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/0125; H10W10/10; H10W10/13; Y; Y10; Y10S; Y10S438/00; Y10S438/914; Y10S438/924; Y10S438/966
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
87 words
A method of fabricating a semiconductor device comprising the steps of: providing a semiconductor substrate, ion implanting a surface of said semiconductor substrate to damage said surface to produce a dense dislocation network array layer, providing a nitride oxidation mask layer directly on said damaged substrate surface, patterning said nitride mask layer to form openings at the areas where it is desired to inset oxide, oxidizing said semiconductor substrate until an inset oxide is formed in the areas of said openings, and removing said nitride oxidation mask.
Claim 2
Independent Claim
87 words
A method of fabricating a semiconductor device comprising the steps of: providing a semiconductor substrate, ion implanting a surface of said semiconductor substrate to damage said surface to produce a dense dislocation network array layer, providing a nitride oxidation mask layer directly on said damaged substrate surface, patterning said nitride mask layer to form openings at the areas where it is desired to inset oxide, oxidizing said semiconductor substrate until an inset oxide is formed in the areas of said openings, and removing said nitride oxidation mask.
Claim 3
Dependent Claim
32 words
A method according to claim 1 wherein nitride oxidation mask layer is first applied to said semiconductor substrate and said ion implantation of said substrate is performed through said nitride oxidation mask.
Claim 4
Dependent Claim
19 words
A method according to claim 1 further including a final step of removing said damaged silicon layer by etching.
Claim 5
Dependent Claim
13 words
A method according to claim 1 wherein said semiconductor substrate is monocrystalline silicon.
Claim 6
Dependent Claim
32 words
A method according to claim 4 wherein said implanted ion species is not electrically active in said silicon substrate and is selected from the group including argon, germanium, neon, oxygen and silicon.
Claim 7
Dependent Claim
58 words
A method according to claim 5 wherein ion implantation energy controls the depth of said damaged layer and is approximately equal to the critical dose for the formation of a continuous amorphous layer in silicon, said critical dose being in the order of 5 × 10 14 to 10 × 10 14 for argon in said silicon substrate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-03 | 1982-01-02 | 1982-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-03 | 1986-01-02 | 1986-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-03 | 1990-01-02 | 1990-07-04 | $7700.00 | Window Closed / Lapsed |