Process of treating polyester yarn to provide a pattern of portions that differ in dyeability
Assignee: EIDP Inc
•
Filing: 1976-04-19
•
Granted: 1978-06-20
•
Expires: 1996-04-19
Abstract
Abstract Polyester yarn having portions which differ in dye uptake, arranged along its length in a predetermined pattern, is produced by treating portions of a spin-oriented yarn with a fluid to induce crystallization and then drawing the yarn to provide a product having a break elongation appropriate for the intended use. The spin-oriented yarn is preferably prepared by melt-spinning polyethylene terephthalate into yarn while withdrawing the yarn from the spinneret at a take-off speed of 3000 to 4000 yards per minute. Suitable treating fluids include acetone or methylene chloride at room temperature and water or air at elevated temperatures. The treated yarn can be draw-textured on false-twist texturing machines having heaters at temperatures above 200° C. The treated portions of the yarn dye deeper than the untreated portions to provide attractive effects in dyed fabrics.
Inventors
- 👤 David Emerson Bosley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:41
CPC Classifications
D; D01; D01D; D01D5/00; D01D5/20; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2922; Y10T428/2973; Y10T428/2976
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
123 words
In a process for producing polyester yarn having alternating thick and thin portions along the yarn that differ in dyeability, wherein the yarn is drawn at a lower draw ratio than would be used to produce a fully-drawn yarn, the improvement which comprises treating as-spun spin-oriented polyester yarn by contacting the yarn at intervals along its length with a fluid to induce crystallization in the contacted portions of the yarn, the treatment being sufficient to provide in the contacted portions a force-to-draw value of at least 1.12 times the value for untreated portions and a density difference of more than 0.005, and then drawing the yarn to have 4 to 20 percent greater denier in the contacted portions than in the untreated portions.
Claim 2
Dependent Claim
123 words
In a process for producing polyester yarn having alternating thick and thin portions along the yarn that differ in dyeability, wherein the yarn is drawn at a lower draw ratio than would be used to produce a fully-drawn yarn, the improvement which comprises treating as-spun spin-oriented polyester yarn by contacting the yarn at intervals along its length with a fluid to induce crystallization in the contacted portions of the yarn, the treatment being sufficient to provide in the contacted portions a force-to-draw value of at least 1.12 times the value for untreated portions and a density difference of more than 0.005, and then drawing the yarn to have 4 to 20 percent greater denier in the contacted portions than in the untreated portions.
Claim 3
Dependent Claim
30 words
A process as defined in claim 1 wherein the treated yarn is drawn and false-twist textured at a heater temperature of over 200° C for setting twist in the yarn.
Claim 4
Dependent Claim
20 words
A process as defined in claim 1 wherein the yarn is drawn and false-twist textured by a simultaneous draw-texturing process.
Claim 5
Dependent Claim
56 words
A process as defined in claim 1 wherein as-spun spin-oriented yarn of polyethylene terephthalate is contacted at intervals along its length with acetone for at least five minutes and is then draw-textured, using a draw ratio which provides 4 to 20 percent greater denier in the contacted portions than in the untreated portions of the yarn.
Claim 6
Dependent Claim
57 words
A process as defined in claim 1 wherein as-spun spin-oriented yarn of polyethylene terephthalate is contacted at intervals along its length with methylene chloride for at least five minutes and is then draw-textured, using a draw ratio which provides 4 to 20 percent greater denier in the contacted portions than in the untreated portions of the yarn.
Claim 7
Dependent Claim
57 words
A process as defined in claim 1 wherein as-spun spin-oriented yarn of polyethylene terephthalate is contacted at intervals along its length with boiling water for at least five minutes and is then draw-textured, using a draw ratio which provides 4 to 20 percent greater denier in the contacted portions than in the untreated portions of the yarn.
Claim 8
Dependent Claim
60 words
A process as defined in claim 1 wherein as-spun spin-oriented yarn of polyethylene terephthalate is contacted at intervals along its length with hot air at about 160° C for at least five minutes and is then drawtextured, using a draw ratio which provides 4 to 20 percent greater denier in the contacted portions than the untreated portions of the yarn.
References Cited (Backward Citations)
US3363295A
Cited
US3478143A
Cited
US3591672A
Cited
US3771307A
Cited
US3949041A
Cited
US3979496A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-19 | 1981-12-19 | 1982-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-19 | 1985-12-19 | 1986-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-19 | 1989-12-19 | 1990-06-20 | $7700.00 | Window Closed / Lapsed |