Preparation of polyamideimide from diisocyanate with alkali metal lactamate catalyst
Assignee: Pharmacia and Upjohn Co
•
Filing: 1977-02-17
•
Granted: 1978-06-13
•
Expires: 1997-02-17
Abstract
Abstract The use of certain catalysts provide for an improved process for the preparation of soluble polyimides, polyamides, and polyamideimides. The catalysts are compounds of formula <IMAGE> WHEREIN M represents an alkali metal, and n is an integer from 2 to 5 inclusive. The improved process comprises reacting organic diisocyanates with polycarboxylic compounds consisting of tetracarboxylic acids or the intramolecular dianhydrides thereof, tricarboxylic acids or the monoanhydrides thereof, dicarboxylic acids, and mixtures thereof, in the presence of said catalysts. The polymers are obtained in solution at low reaction temperatures and short reaction times thereby avoiding side-reactions which otherwise would be detrimental to polymer molecular weight and ultimate polymer properties.
Inventors
- 👤 Besir K. Onder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 12:48
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/30; C08G18/34; C08G18/341; C08G18/08; C08G18/16; C08G18/22; C08G18/225; C08G18/343; C08G18/345; C08G18/346; C08G69/00; C08G73/00; C08G73/06; C08G73/10; C08G73/1003; C08G73/1035
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
87 words
In a process for preparing an essentially linear, solvent soluble solid polyamideimide by the condensation of an organic diisocyanate with a compound containing one carboxylic acid group and one intramolecular anhydride group or the free carboxylic acids thereof in said solvent, the improvement which comprises adding to the solution of polyamideimide forming reactants a catalytic amount of a compound wherein n is an integer from 2 to 5 inclusive, and M is an alkali metal at a temperature of from about 40° C to about 140° C.
Claim 2
Dependent Claim
87 words
In a process for preparing an essentially linear, solvent soluble solid polyamideimide by the condensation of an organic diisocyanate with a compound containing one carboxylic acid group and one intramolecular anhydride group or the free carboxylic acids thereof in said solvent, the improvement which comprises adding to the solution of polyamideimide forming reactants a catalytic amount of a compound wherein n is an integer from 2 to 5 inclusive, and M is an alkali metal at a temperature of from about 40° C to about 140° C.
Claim 3
Dependent Claim
14 words
The process according to claim 1 wherein the solvent comprises a dipolar aprotic solvent.
Claim 4
Dependent Claim
16 words
The process according to claim 1 wherein the catalyst is an alkali metal salt of pyrrolidone.
Claim 5
Dependent Claim
16 words
The process of claim 1 wherein the polycarboxylic acid derivative comprises an aromatic tricarboxylic acid anhydride.
Claim 6
Dependent Claim
77 words
In a process for preparing an essentially linear, dipolar aprotic solvent soluble solid polyamideimide by the condensation of an organic diisocyanate with a compound containing one carboxylic acid group and one intramolecular anhydride group or the free carboxylic acids thereof in said solvent, the improvement which comprises adding to the solution of polyamideimide forming reactants a catalytic amount of an alkali metal salt of pyrrolidone at a temperature of from about 40° C to about 140° C.
Claim 7
Dependent Claim
77 words
In a process for preparing an essentially linear, dipolar aprotic solvent soluble solid polyamideimide by the condensation of an organic diisocyanate with a compound containing one carboxylic acid group and one intramolecular anhydride group or the free carboxylic acids thereof in said solvent, the improvement which comprises adding to the solution of polyamideimide forming reactants a catalytic amount of an alkali metal salt of pyrrolidone at a temperature of from about 40° C to about 140° C.
Claim 8
Dependent Claim
14 words
The process according to claim 5 wherein the polycarboxylic acid derivative is trimellitic anhydride.
References Cited (Backward Citations)
US3803100A
Cited
US3873503A
Cited
US3658773A
Cited
US3562217A
Cited
US3701756A
Cited
US3682860A
Cited
US3620987A
Cited
US3853813A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-12 | 1981-12-12 | 1982-06-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-12 | 1985-12-12 | 1986-06-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-12 | 1989-12-12 | 1990-06-13 | $7700.00 | Window Closed / Lapsed |