Abstract Significantly higher productivity of polyester feed yarn is achieved when the polymer from which the feed yarn is melt spun is chain-branched with multifunctional chain branchers having 1-15 microequivalents of reactive branching sites based on one gram of the polymer. This productivity increase (over conventional production employing the same spinnerette in accordance with teachings of the prior art as applied generally to unbranched polymers) may be achieved specifically by spinning a feed yarn (of the same filament denier and draw ratio) at a higher throughput rate at a higher windup speed followed by draw-texturing (at the same draw ratio to the same drawn denier); or by spinning at a higher throughput rate employing the same windup speed a feed yarn of higher denier and draw-ratio followed by draw-texturing at the higher draw ratio to the same drawn denier; or by any combination thereof.
A melt spun partially oriented polyester multifilament feed yarn made from a polyester polymer containing a tri or tetrafunctional chain brancher in such an amount that the polymer has 2-14 microequivalents of reactive branching sites per gram of polymer, said feed yarn having a tenacity of about 1.2-3.0, a spun denier of at least about 5 dpf, an elongation of about 60-220%, and a draw ratio (DR) in accordance with the following: DR ≦ 5593.7/S where S is 3107-4022 meters per minute and is the melt spinning take-up speed of the multifilament feed yarn.
Claim 2
Dependent Claim
94 words
A melt spun partially oriented polyester multifilament feed yarn made from a polyester polymer containing a tri or tetrafunctional chain brancher in such an amount that the polymer has 2-14 microequivalents of reactive branching sites per gram of polymer, said feed yarn having a tenacity of about 1.2-3.0, a spun denier of at least about 5 dpf, an elongation of about 60-220%, and a draw ratio (DR) in accordance with the following: DR ≦ 5593.7/S where S is 3107-4022 meters per minute and is the melt spinning take-up speed of the multifilament feed yarn.
Claim 3
Dependent Claim
11 words
The multifilament feed yarn of claim 1 wherein DR ≦ 5904.4/S
Claim 4
Dependent Claim
32 words
The process of claim 2 wherein the polymer contains such an amount of the chain brancher that the polymer has 5 to 12 microequivalents of reactive branching sites per gram of polymer.