Removal of RTV silicon rubber encapsulants
Assignee: AT&T Inc
•
Filing: 1976-12-27
•
Granted: 1978-05-16
•
Expires: 1996-12-27
Abstract
Abstract Disclosed is a method of removing silicone rubber encapsulating material from micro-electronic circuits. The encapsulant is broken down molecularly and removed by a solution of tetramethyl-ammonium hydroxide which is diluted with an alcohol such as 2-propanol. It was found that this stripping solution causes minimal swelling of the encapsulant and leaves no significant residue which cannot be removed by standard rinsing.
Inventors
- 👤 John Herbert Heiss, Jr.
- 👤 John Robert Wylie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 11:54
CPC Classifications
C; C08; C08J; C08J11/00; C08J11/04; C08J11/10; C08J11/18; C08J11/28; H; H10; H10W; H10W74/00; H10W74/01; C08J2383/00; C08J2383/04; H05; H05K; H05K3/00; H05K3/22; H05K3/28; H05K3/288; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
39 words
In a process for fabricating circuits formed in an insulating substrate, the method of removing silicone rubber encapsulants formed over said circuit comprising the step of applying to said encapsulant a solution consisting of tetramethylammonium hydroxide, methanol and 2-propanol.
Claim 2
Dependent Claim
39 words
In a process for fabricating circuits formed in an insulating substrate, the method of removing silicone rubber encapsulants formed over said circuit comprising the step of applying to said encapsulant a solution consisting of tetramethylammonium hydroxide, methanol and 2-propanol.
Claim 3
Dependent Claim
18 words
The method according to claim 1 wherein the temperature of the solution is within the range 25°-55° C.
Claim 4
Dependent Claim
25 words
The method according to claim 1 wherein the concentration by volume of tetramethylammonium hydroxide and methanol to 2-propanol lies within the range 1:10 to 1:20.
Claim 5
Dependent Claim
18 words
The method according to claim 2 wherein the temperature of the solution is within the range 36°-40° C.
Claim 6
Dependent Claim
29 words
The method according to claim 1 wherein the circuit is successively immersed in different baths of said solution and thereafter rinsed by immersing in a material comprising isopropyl alcohol.
Claim 7
Dependent Claim
154 words
In a process for fabricating circuits formed on an insulating substrate, the method of removing silicone rubber encapsulants comprising siloxanes with methoxy end groups formed on said circuit comprising the steps of: immersing the circuit in a first solution consisting of tetramethylammonium hydroxide, methanol and 2-propanol with a concentration by volume of tetramethylammonium hydroxide and methanol to 2-propanol within the range 1:10 to 1:20 at a temperature within the range 36°-40° C for a period of time within the range 2-6 hours; removing said circuit from said first solution and immersing in a second solution of the same composition at a temperature within the range 36°-40° C for a period of time within the range 1-2 hours in order to remove any residue remaining after immersion in said first solution; and removing said circuit from said second solution and immersing in third and fourth solutions comprising isopropyl alcohol in order to rinse said circuit.
Claim 8
Dependent Claim
154 words
In a process for fabricating circuits formed on an insulating substrate, the method of removing silicone rubber encapsulants comprising siloxanes with methoxy end groups formed on said circuit comprising the steps of: immersing the circuit in a first solution consisting of tetramethylammonium hydroxide, methanol and 2-propanol with a concentration by volume of tetramethylammonium hydroxide and methanol to 2-propanol within the range 1:10 to 1:20 at a temperature within the range 36°-40° C for a period of time within the range 2-6 hours; removing said circuit from said first solution and immersing in a second solution of the same composition at a temperature within the range 36°-40° C for a period of time within the range 1-2 hours in order to remove any residue remaining after immersion in said first solution; and removing said circuit from said second solution and immersing in third and fourth solutions comprising isopropyl alcohol in order to rinse said circuit.
References Cited (Backward Citations)
US2710843A
Cited
US3551204A
Cited
US3673099A
Cited
US3947952A
Cited
US3915769A
Cited
US3969813A
Cited
US4017495A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-15 | 1981-11-14 | 1982-05-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-15 | 1985-11-14 | 1986-05-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-15 | 1989-11-14 | 1990-05-16 | $7700.00 | Window Closed / Lapsed |