Reduction leaching of raw sea nodules with sulfides
Assignee: Huntington Alloys Corp
•
Filing: 1976-03-08
•
Granted: 1978-04-18
•
Expires: 1996-03-08
Abstract
Abstract A process for extracting metal values from sea nodules is provided in which nickel, cobalt and copper values are selectively extracted by leaching raw sea nodules in an aqueous ammoniacal medium in the presence of a reducing agent for tetravalent manganese and carbonate to precipitate the reduced manganese as manganous carbonate.
Inventors
- 👤 Kohur Nagaraja Subramanian
- 👤 Gerald Vernon Glaum
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:27
CPC Classifications
C; C22; C22B; C22B47/00; C22B47/0018; C22B47/0045; C22B47/0054; C22B47/0072; C01; C01G; C01G45/00; C01G45/05; C01P; C01P2006/00; C01P2006/80; Y; Y10; Y10S; Y10S423/00; Y10S423/04
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
211 words
A process for extracting nickel, cobalt, copper and molybdenum values from raw sea nodules containing a major amount of manganese and iron, manganese being present in tetravalent state and a lesser amount of at least one of the nonferrous metals nickel, cobalt, copper and molybdenum comprising leaching said raw nodules in an aqueous ammoniacal medium at a pH of not less than about 8 in the presence of a reducing agent for tetravalent manganese selected from the group consisting of H 2 S, (NH 4 ) 2 S, ammonium polysulfide, and combinations thereof and in the presence of a manganous carbonate precipitant selected from the group consisting of CO 2 , (NH 4 ) 2 CO 3 , and an alkali metal carbonate, at a temperature in the range of about 50° C to about 125° C and pressure of atmospheric to about 100 psig, to convert tetravalent manganese to the divalent state, extract nickel, cobalt, copper and molybdenum values into the leach solution and to separate manganese and iron values into the leach residue, said leaching reaction condition being maintained for a period of time sufficient to maximize said extraction of nickel, cobalt, copper and molybdenum values into solution and separation of manganese and iron values into the leach residue.
Claim 2
Dependent Claim
211 words
A process for extracting nickel, cobalt, copper and molybdenum values from raw sea nodules containing a major amount of manganese and iron, manganese being present in tetravalent state and a lesser amount of at least one of the nonferrous metals nickel, cobalt, copper and molybdenum comprising leaching said raw nodules in an aqueous ammoniacal medium at a pH of not less than about 8 in the presence of a reducing agent for tetravalent manganese selected from the group consisting of H 2 S, (NH 4 ) 2 S, ammonium polysulfide, and combinations thereof and in the presence of a manganous carbonate precipitant selected from the group consisting of CO 2 , (NH 4 ) 2 CO 3 , and an alkali metal carbonate, at a temperature in the range of about 50° C to about 125° C and pressure of atmospheric to about 100 psig, to convert tetravalent manganese to the divalent state, extract nickel, cobalt, copper and molybdenum values into the leach solution and to separate manganese and iron values into the leach residue, said leaching reaction condition being maintained for a period of time sufficient to maximize said extraction of nickel, cobalt, copper and molybdenum values into solution and separation of manganese and iron values into the leach residue.
Claim 3
Dependent Claim
113 words
A process according to claim 1 wherein the sea nodules are provided in the leaching medium in sufficient amount to provide a slurry containing about 10% to 30% solids the carbonate and ammoniacal values are provided to the medium as CO 2 and NH 3 , said CO 2 and NH 3 being supplied in an amount to provide about 60 to 200 gpl NH 3 and about 40 to about 150 gpl CO 2 , and wherein the sea nodules are leached at a temperature of about 100° C to about 125° C at a pressure in the range of about 50 to about 100 psig for about 6 to 10 hours.
Claim 4
Dependent Claim
154 words
A process for extracting nickel, cobalt, copper and molybdenum values from a manganiferous ore containing a major amount of manganese and iron, manganese being present in tetravalent form, and a lesser amount of at least one of the nonferrous metals nickel, cobalt, copper and molybdenum comprising leaching said ore in an aqueous ammoniacal medium at a pH of not less than about 8 in the presence of a reducing agent comprising a sulfide, said sulfide being selected from the group consisting of H 2 S, (NH 4 ) 2 S and ammonium polysulfide, at reaction conditions to convert tetravalent manganese to the divalent state and in the presence of a carbonate capable of forming substantially insoluble manganous carbonate in the ammoniacal medium, whereby at least one of the nonferrous metal values nickel, cobalt, copper and molybdenum is extracted into the leach solution and the manganese and iron values are separated into the leach residue.
Claim 5
Dependent Claim
154 words
A process for extracting nickel, cobalt, copper and molybdenum values from a manganiferous ore containing a major amount of manganese and iron, manganese being present in tetravalent form, and a lesser amount of at least one of the nonferrous metals nickel, cobalt, copper and molybdenum comprising leaching said ore in an aqueous ammoniacal medium at a pH of not less than about 8 in the presence of a reducing agent comprising a sulfide, said sulfide being selected from the group consisting of H 2 S, (NH 4 ) 2 S and ammonium polysulfide, at reaction conditions to convert tetravalent manganese to the divalent state and in the presence of a carbonate capable of forming substantially insoluble manganous carbonate in the ammoniacal medium, whereby at least one of the nonferrous metal values nickel, cobalt, copper and molybdenum is extracted into the leach solution and the manganese and iron values are separated into the leach residue.
Claim 6
Dependent Claim
28 words
A process according to claim 3 wherein the manganiferous ore comprises sea nodules and said nodules are ground and introduced in the raw condition into the leaching medium.
Claim 7
Dependent Claim
35 words
A process according to claim 3 wherein the carbonate is provided by a reagent selected from the group consisting of CO 2 , (NH 4 ) 2 CO 3 , and an alkali metal carbonate.
Claim 8
Dependent Claim
50 words
A process according to claim 3 wherein the leaching reactants are maintained at a temperature of about 25° to about 130° C for a period of time sufficient to maximize said extraction of nickel, cobalt and copper values into solution and separation of manganese and iron values into the residue.
Claim 9
Dependent Claim
21 words
A process according to claim 3 wherein the ammoniacal leaching medium is maintained at a pH between 8 and about 9.
Claim 10
Dependent Claim
23 words
A process according to claim 4 wherein the solids content of the slurry is in the range of about 10% to about 30%.
Claim 11
Dependent Claim
56 words
A process according to claim 4 wherein NH 3 and CO 2 provide the ammoniacal medium and the carbonate reagent, and said NH 3 is supplied to the leaching medium in an amount to provide about 60 to about 200 gpl, and said CO 2 in an amount to provide about 40 to about 150 gpl.
Claim 12
Dependent Claim
18 words
A process according to claim 3 wherein the temperature is maintained at about 100° to about 125° C.
Claim 13
Dependent Claim
139 words
A process for extracting nickel, cobalt, copper and molybdenum values from a manganiferous ore containing a major amount of manganese and iron, maganese being present in tetravalent form and a lesser amount of at least one of the nonferrous metals nickel, cobalt, copper and molybdenum comprising leaching said ore in an aqueous ammoniacal medium at a pH of not less than about 8 in the presence of a reducing agent comprising a sulfide soluble in said ammoniacal medium at reaction conditions to convert tetravalent manganese to the divalent state and in the presence of a carbonate capable of forming substantially insoluble manganous carbonate in the ammoniacal medium, whereby at least one of the nonferrous metal values nickel, cobalt, copper and molybdenum is extracted into the leach solution and the manganese and iron values are separated into the leach residue.
Claim 14
Dependent Claim
139 words
A process for extracting nickel, cobalt, copper and molybdenum values from a manganiferous ore containing a major amount of manganese and iron, maganese being present in tetravalent form and a lesser amount of at least one of the nonferrous metals nickel, cobalt, copper and molybdenum comprising leaching said ore in an aqueous ammoniacal medium at a pH of not less than about 8 in the presence of a reducing agent comprising a sulfide soluble in said ammoniacal medium at reaction conditions to convert tetravalent manganese to the divalent state and in the presence of a carbonate capable of forming substantially insoluble manganous carbonate in the ammoniacal medium, whereby at least one of the nonferrous metal values nickel, cobalt, copper and molybdenum is extracted into the leach solution and the manganese and iron values are separated into the leach residue.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-17 | 1981-10-17 | 1982-04-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-17 | 1985-10-17 | 1986-04-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-17 | 1989-10-17 | 1990-04-18 | $7700.00 | Window Closed / Lapsed |