Process for producing phosphazene fire retardant
Assignee: Albemarle Corp
•
Filing: 1976-01-26
•
Granted: 1978-03-28
•
Expires: 1996-01-26
Abstract
Abstract A process for producing fire retardant phosphonitrilate polymers by reacting phosphonitrilic halide with a hydroxyl compound such as an aliphatic or aromatic alcohol at not more than about 40° C in the presence of an acid acceptor, such as pyridine, under conditions such that a relatively low concentration of the hydroxyl compound is present during the initial 1/2 to 3 hours of the reaction and the reaction conditions are maintained at from 20°-50° C for a period of 1/2 to 120 hours and, optionally, further heating the reaction mixture to a temperature of 40°-80° C for 1/2 to 81/2 hours. The phosphonitrilate polymers are suitable for fire retarding cellulosic materials such as regenerated cellulose, rayon and the like.
Inventors
- 👤 Carroll W. Lanier
- 👤 James T. F. Kao
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 12:08
CPC Classifications
C; C08; C08G; C08G79/00; C08G79/02; C08G79/025; C08L; C08L1/00; C08L1/02; C08L1/06; Y; Y10; Y10S; Y10S260/00; Y10S260/24
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
207 words
Regenerated cellulose filaments and articles having dispersed therein a flame retardant amount of a phosphonitrilate polymer prepared according to the process comprising reacting, in the presence of an amount of an acid acceptor sufficient to complex with at least twice the molar amount of hydrogen halide formed, a phosphonitrilic halide with a hydroxyl compound selected from aliphatic alcohols having from one to about six carbon atoms and aromatic alcohols having from six to about ten carbon atoms according to the steps of (a) contacting a mixture of said phosphonitrilic halide and said acid acceptor with at least about 85 to about 180 weight percent of the theoretical amount based on said phosphonitrilic halide of said hydroxyl compound at a temperature of not more than about 40° C, whereby a relatively low concentration of said hydroxyl compound is present during the initial 1/2 to about 3 hours of the reaction and whereby condensation occurs between intermediate phosphonitrilate alkoxy or aryloxy ester species and phosphonitrilic halides or partially esterified phosphonitrilates with the evolution of an alkyl or aryl halide compound, and (b) thereafter, maintaining the reaction mixture at a temperature of from about 20° to about 50° C for a period of from about 1/2 to about 120 hours.
Claim 2
Dependent Claim
207 words
Regenerated cellulose filaments and articles having dispersed therein a flame retardant amount of a phosphonitrilate polymer prepared according to the process comprising reacting, in the presence of an amount of an acid acceptor sufficient to complex with at least twice the molar amount of hydrogen halide formed, a phosphonitrilic halide with a hydroxyl compound selected from aliphatic alcohols having from one to about six carbon atoms and aromatic alcohols having from six to about ten carbon atoms according to the steps of (a) contacting a mixture of said phosphonitrilic halide and said acid acceptor with at least about 85 to about 180 weight percent of the theoretical amount based on said phosphonitrilic halide of said hydroxyl compound at a temperature of not more than about 40° C, whereby a relatively low concentration of said hydroxyl compound is present during the initial 1/2 to about 3 hours of the reaction and whereby condensation occurs between intermediate phosphonitrilate alkoxy or aryloxy ester species and phosphonitrilic halides or partially esterified phosphonitrilates with the evolution of an alkyl or aryl halide compound, and (b) thereafter, maintaining the reaction mixture at a temperature of from about 20° to about 50° C for a period of from about 1/2 to about 120 hours.
Claim 3
Independent Claim
229 words
A method of preparing a flame retardant regenerated cellulose filament which comprises mixing viscose and a flame retardant amount of a phosphonitrilate polymer, shaping the mixture into a filament, and coagulating and regenerating said filament, said phosphonitrilate polymer being prepared by a process comprising reacting, in the presence of an amount of an acid acceptor sufficient to complex with at least twice the molar amount of hydrogen halide formed, a phosphonitrilic halide with a hydroxyl compound selected from aliphatic alcohols having from one to about six carbon atoms and aromatic alcohols having from six to about ten carbon atoms according to the steps of (a) contacting a mixture of said phosphonitrilic halide and said acid acceptor with at least about 85 to about 180 weight percent of the theoretical amount based on said phosphonitrilic halide of said hydroxyl compound at a temperature of not more than about 40° C, whereby a relatively low concentration of said hydroxyl compound is present during the initial 1/2 to about 3 hours of the reaction and whereby condensation occurs between intermediate phosphonitrilate alkoxy or aryloxy ester species and phosphonitrilic halides or partially esterified phosphonitrilates with the evolution of an alkyl or aryl halide compound, and (b) thereafter, maintaining the reaction mixture at a temperature of from about 20° to about 50° C for a period of from about 1/2 to about 120 hours.
Claim 4
Independent Claim
229 words
A method of preparing a flame retardant regenerated cellulose filament which comprises mixing viscose and a flame retardant amount of a phosphonitrilate polymer, shaping the mixture into a filament, and coagulating and regenerating said filament, said phosphonitrilate polymer being prepared by a process comprising reacting, in the presence of an amount of an acid acceptor sufficient to complex with at least twice the molar amount of hydrogen halide formed, a phosphonitrilic halide with a hydroxyl compound selected from aliphatic alcohols having from one to about six carbon atoms and aromatic alcohols having from six to about ten carbon atoms according to the steps of (a) contacting a mixture of said phosphonitrilic halide and said acid acceptor with at least about 85 to about 180 weight percent of the theoretical amount based on said phosphonitrilic halide of said hydroxyl compound at a temperature of not more than about 40° C, whereby a relatively low concentration of said hydroxyl compound is present during the initial 1/2 to about 3 hours of the reaction and whereby condensation occurs between intermediate phosphonitrilate alkoxy or aryloxy ester species and phosphonitrilic halides or partially esterified phosphonitrilates with the evolution of an alkyl or aryl halide compound, and (b) thereafter, maintaining the reaction mixture at a temperature of from about 20° to about 50° C for a period of from about 1/2 to about 120 hours.
References Cited (Backward Citations)
US2909446A
Cited
US3869294A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-27 | 1981-09-26 | 1982-03-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-27 | 1985-09-26 | 1986-03-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-27 | 1989-09-26 | 1990-03-28 | $7700.00 | Window Closed / Lapsed |