Hydrocarbon conversion with modified solid catalyst materials
Assignee: Mobil Oil AS
•
Filing: 1976-12-22
•
Granted: 1978-03-21
•
Expires: 1996-12-22
Abstract
Abstract Organic compound conversion in the presence of refractory metal oxide solid materials, characterized by the presence of surface hydroxyl groups, which have undergone modification by being subjected to the sequential steps of (1) silylating, (2) calcining and (3) steaming is provided. The silylating step in the modification of the refractory materials is accomplished by contacting the solid material with an organic- or halogen-substituted silane at a temperature of between about 25 DEG C and about 500 DEG C to effect bonding between the silane and the surface hydroxyl groups of the solid. The calcining step in the modification of the refractory materials is accomplished by heating the resulting silylated solid at a temperature and for a time sufficient to remove substantially all of any introduced organic or halogen substituent. The steaming step in the modification of the refractory materials is accomplished by contacting the resulting calcined solid with an atmosphere containing at least 2 percent by volume of steam at a temperature of between about 900 DEG F and about 1600 DEG F for at least about 1/2 hour.
Inventors
- 👤 Thomas Owen Mitchell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:35
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/08; B01J37/082; C; C10; C10G; C10G11/00; C10G11/02; C10G11/04; C10G47/00; C10G47/02; C10G47/10; C10G47/12; C10G47/16
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
210 words
The method of hydrocarbon compound catalytic conversion which comprises contacting said hydrocarbon compound with a refractory metal oxide solid material selected from the group consisting of alumina, silica-alumina and alumino-silicates under hydrocarbon compound conversion conditions, said refractory metal oxide solid material being characterized by the presence of surface hydroxyl groups and having been modified by being subjected to the sequential steps of silylating said solid material, calcining the product solid material of said silylating step and steaming the product solid material of said calcining step; said silylating step comprising contacting said solid material with an organic- or halogen-substituted silane at a temperature of between about 25° C and about 500° C to effect bonding between said silane and the surface hydroxyl groups of said solid material; said calcining step comprising heating the resulting solid material from said silylating step at a temperature of greater than about 350° C to about 700° C in an inert atmosphere or oxygen-containing atmosphere for from about 30 minutes to about 20 hours; and said steaming step comprising contacting the resulting solid material from said calcining step with an atmosphere containing at least 2 volume percent steam at a temperature of between about 900° F and about 1600° F for at least about one-half hour.
Claim 2
Independent Claim
210 words
The method of hydrocarbon compound catalytic conversion which comprises contacting said hydrocarbon compound with a refractory metal oxide solid material selected from the group consisting of alumina, silica-alumina and alumino-silicates under hydrocarbon compound conversion conditions, said refractory metal oxide solid material being characterized by the presence of surface hydroxyl groups and having been modified by being subjected to the sequential steps of silylating said solid material, calcining the product solid material of said silylating step and steaming the product solid material of said calcining step; said silylating step comprising contacting said solid material with an organic- or halogen-substituted silane at a temperature of between about 25° C and about 500° C to effect bonding between said silane and the surface hydroxyl groups of said solid material; said calcining step comprising heating the resulting solid material from said silylating step at a temperature of greater than about 350° C to about 700° C in an inert atmosphere or oxygen-containing atmosphere for from about 30 minutes to about 20 hours; and said steaming step comprising contacting the resulting solid material from said calcining step with an atmosphere containing at least 2 volume percent steam at a temperature of between about 900° F and about 1600° F for at least about one-half hour.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein said refractory metal oxide solid material is alumina.
Claim 4
Dependent Claim
14 words
The method of claim 1 wherein said refractory metal oxide solid material is silica-alumina.
Claim 5
Dependent Claim
14 words
The method of claim 1 wherein said refractory metal oxide solid material is aluminosilicate.
Claim 6
Dependent Claim
23 words
The method of claim 4 wherein said aluminosilicate is zeolite X, zeolite Y, zeolite L, zeolite ZSM-4, zeolite ZSM-5, faujasite, erionite or mordenite.
Claim 7
Dependent Claim
345 words
The method of claim 1 wherein the silylating step in the modification of the refractory metal oxide solid material comprises contacting said solid material with an organic- or halogen-substituted silane having the general formula: ##STR2## wherein n is 1 or 2; and when n is 2, R is a reactive member selected from the group consisting of amino and alkylamido of from 1 to about 30 carbon atoms, and R 1 , R 2 and R 3 are members selected from the group consisting of R, hydrogen, hydroxy, halogen, alkoxy, of from 1 to about 30 carbon atoms, aryloxy, an organic radical which may include alkyl of from 1 to about 40 carbon atoms, alkyl or aryl carboxylic acid wherein the organic portion of the alkyl group contains from 1 to about 30 carbon atoms and the aryl group contains from 6 to 24 carbon atoms, aryl of from 6 to about 24 carbon atoms and which may be further substituted, alkaryl and aralkyl of from 7 to about 30 carbon atoms and which may be further substituted; and when n is 1, R is a reactive member selected from the group consisting of hydrogen, hydroxy, halogen, alkoxy of from 1 to 30 carbon atoms, methyl, aryloxy, alkyl-substituted aryloxy wherein the alkyl portion thereof may have from 1 to about 30 carbon atoms and carboxy, and R 1 , R 2 and R 3 are members selected from the group consisting of hydrogen, hydroxy, halogen, alkoxy of from 1 to about 30 carbon atoms, aryloxy, alkyl-substituted aryloxy wherein the alkyl portion thereof may have from 1 to about 30 carbon atoms, alkyl of from 1 to about 40 carbon atoms, alkyl or aryl carboxylic acid wherein the organic portion of the alkyl group contains from 1 to about 30 carbon atoms and the aryl group contains from 6 to about 24 carbon atoms, aryl of from 6 to about 24 carbon atoms and which may be further substituted, alkaryl and aralkyl of from 7 to about 30 carbon atoms and which may be further substituted.
Claim 8
Dependent Claim
59 words
The method of claim 6 wherein the silylating step in the modification of the refractory metal oxide solid material comprises contacting said solid material with a silane having the general formula as in claim 6 wherein n is 1 and R is hydrogen or methyl, at a temperature of from greater than about 300° C to about 500° C.
Claim 9
Dependent Claim
46 words
The method of claim 6 wherein the calcining step in the modification of the refractory metal oxide solid material comprises heating the resulting solid material from said silylating step in an inert atmosphere or an oxygen-containing atmosphere for from about 30 minutes to about 20 hours.
Claim 10
Dependent Claim
36 words
The method of claim 8 wherein the calcining step in the modification of the refractory metal oxide solid material comprises heating to a temperature in the range of from about 450° C to about 550° C.
Claim 11
Dependent Claim
45 words
The method of claim 6 wherein the steaming step in the modification of the refractory metal oxide solid material is continued for from about 1/2 hour to about 5 hours at a temperature in the range of from about 1000° F to about 1400° F.
Claim 12
Dependent Claim
59 words
The method of claim 1 wherein said hydrocarbon compound conversion is conducted in a flow apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a liquid hourly spaced velocity of from about 0.1 hr -1 to about 20 hr -1 .
Claim 13
Dependent Claim
54 words
The method of claim 1 wherein said hydrocarbon compound conversion is conducted in a batch apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a contact time of from about 0.05 hour to about 10 hours.
Claim 14
Dependent Claim
59 words
The method of claim 2 wherein said hydrocarbon compound conversion is conducted in a flow apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a liquid hourly spaced velocity of from about 0.1 hr -1 to about 20 hr -1 .
Claim 15
Dependent Claim
54 words
The method of claim 2 wherein said hydrocarbon compound conversion is conducted in a batch apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a contact time of from about 0.05 hour to about 10 hours.
Claim 16
Dependent Claim
59 words
The method of claim 3 wherein said hydrocarbon compound conversion is conducted in a flow apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a liquid hourly spaced velocity of from about 0.1 hr -1 to about 20 hr -1 .
Claim 17
Dependent Claim
54 words
The method of claim 3 wherein said hydrocarbon compound conversion is conducted in a batch apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a contact time of from about 0.05 hour to about 10 hours.
Claim 18
Dependent Claim
59 words
The method of claim 4 wherein said hydrocarbon compound conversion is conducted in a flow apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a liquid hourly spaced velocity of from about 0.1 hr -1 to about 20 hr -1 .
Claim 19
Dependent Claim
54 words
The method of claim 4 wherein said hydrocarbon compound conversion is conducted in a batch apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a contact time of from about 0.05 hour to about 10 hours.
Claim 20
Dependent Claim
59 words
The method of claim 5 wherein said hydrocarbon compound conversion is conducted in a flow apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a liquid hourly space velocity of from about 0.1 hr -1 to about 20 hr -1 .
Claim 21
Dependent Claim
54 words
The method of claim 5 wherein said hydrocarbon compound conversion is conducted in a batch apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a contact time of from about 0.05 hour to about 10 hours.
Claim 22
Dependent Claim
59 words
The method of claim 6 wherein said hydrocarbon compound conversion is conducted in a flow apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a liquid hourly space velocity of from about 0.1 hr -1 to about 20 hr -1 .
Claim 23
Dependent Claim
54 words
The method of claim 6 wherein said hydrocarbon compound conversion is conducted in a batch apparatus under conditions, which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a contact time of from about 0.05 hour to about 10 hours.
Claim 24
Dependent Claim
59 words
The method of claim 8 wherein said hydrocarbon compound conversion is conducted in a flow apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a liquid hourly space velocity of from about 0.1 hr -1 to about 20 hr -1 .
Claim 25
Dependent Claim
54 words
The method of claim 8 wherein said hydrocarbon compound conversion is conducted in a batch apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a contact time of from about 0.05 hour to about 10 hours.
Claim 26
Dependent Claim
59 words
The method of claim 10 wherein said hyrocarbon compound conversion is conducted in a flow apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a liquid hourly spaced velocity of from about 0.1 hr -1 to about 20 hr -1 .
Claim 27
Dependent Claim
54 words
The method of claim 10 wherein said hydrocarbon compound conversion is conducted in a batch apparatus under conditions which include a temperature of from about 70° F to about 1200° F, a pressure of from about atmospheric to about 4000 psig and a contact time of from about 0.05 hour to about 10 hours.
Claim 28
Dependent Claim
52 words
The method of claim 11 wherein said conversion is cracking under conditions which include a temperature of from about 500° F to about 1200° F, a pressure of from atmospheric to about 500 psig and a liquid hourly space velocity of from about 0.1 hr -1 to about 20 hr -1 .
Claim 29
Dependent Claim
47 words
The method of claim 12 wherein said conversion is cracking under conditions which include a temperature of from about 500° F to about 1200° F, a pressure of from atmospheric to about 500 psig and a contact time of from about 0.05 hour to about 10 hours.
Claim 30
Dependent Claim
56 words
The method of claim 11 wherein said conversion is hydrocracking under conditions which include a temperature of from about 450° F to about 1000° F, a pressure of from about 200 psig to about 4000 psig, a liquid hourly space velocity of from about 0.2 hr -1 to about 10 hr -1 to about 12,000 scf/bbl.
Claim 31
Dependent Claim
61 words
The method of claim 12 wherein said conversion is hydrocracking under conditions which include a temperature of from about 450° F to about 1000° F, a pressure of from about 200 psig to about 4000 psig, a contact time of from about 0.1 hour to about 10 hours and a hydrogen/hydrocarbon ratio of from about 500 scf/bbl to about 12,000 scf/bbl.
References Cited (Backward Citations)
US2722504A
Cited
US3437587A
Cited
US3140253A
Cited
US3682996A
Cited
US3661770A
Cited
US3698157A
Cited
US4013589A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-20 | 1981-09-19 | 1982-03-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-20 | 1985-09-19 | 1986-03-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-20 | 1989-09-19 | 1990-03-21 | $7700.00 | Window Closed / Lapsed |