Process for the preparation of materials having improved mechanical properties and materials obtained thereby
Assignee: SnamProgetti SpA
•
Filing: 1974-10-31
•
Granted: 1977-03-22
•
Expires: 1994-10-31
Abstract
Abstract The mechanical and thermal properties of aluminum oxide, such as γ alumina, adapted for use as a catalyst or catalyst carrier are improved through a treatment thereof with a silicon compound containing hydrolyzable radicals, such as methyl orthosilicate, in which the aluminum compound is impregnated with the silicon compound or a solution thereof in a compatible organic solvent whose boiling point is lower than the boiling point of the silicon compound. The impregnated aluminum oxide is slowly brought to the boiling temperature of the silicon compound in an inert atmosphere so as to cause silicon compound to react with the aluminum oxide and to distill off reaction products and excess silicon compound. The hydrolyzable groups bound to the silicon compound on the aluminum oxide are then reacted with water and distilled off.
Inventors
- 👤 Franco Buonomo
- 👤 Vittorio Fattore
- 👤 Bruno Notari
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:40
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; B; B01; B01J; B01J21/00; B01J21/12; B01J23/00; B01J23/02; B01J23/04; B01J37/00; B01J37/08; B01J37/10; C01; C01B; C01B13/00; C01B13/14; C01B13/145; C04B41/45; C04B41/46; C04B41/49; C01P; C01P2004/00; C01P2004/30; C01P2004/32; C01P2006/00; C01P2006/12; C01P2006/14; Y; Y10; Y10S; Y10S502/00; Y10S502/50
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
143 words
The process of improving the mechanical and thermal properties of aluminum oxide adapted for use as a catalyst or catalytic carrier which comprises impregnating said aluminum oxide with a silicon compound containing hydrolyzable radicals selected from the group consisting of the tetraesters of silicic acid, the halogen containing esters of orthosilicic acid and the organic silicon salts, slowly heating said impregnated aluminum oxide to the boiling temperature of said silicon compound in an inert atmosphere so as to react the silicon compound with the aluminum oxide and to distill off reaction products and excess silicon compound, and then reacting the hydrolyzable radicals bound to the silicon compound on said aluminum oxide with water in a closed vessel so as to hydrolyze said hydrolyzable radicals and distilling off vapors from said vessel and condensing said vapors outside the vessel until only water is condensed.
Claim 2
Dependent Claim
143 words
The process of improving the mechanical and thermal properties of aluminum oxide adapted for use as a catalyst or catalytic carrier which comprises impregnating said aluminum oxide with a silicon compound containing hydrolyzable radicals selected from the group consisting of the tetraesters of silicic acid, the halogen containing esters of orthosilicic acid and the organic silicon salts, slowly heating said impregnated aluminum oxide to the boiling temperature of said silicon compound in an inert atmosphere so as to react the silicon compound with the aluminum oxide and to distill off reaction products and excess silicon compound, and then reacting the hydrolyzable radicals bound to the silicon compound on said aluminum oxide with water in a closed vessel so as to hydrolyze said hydrolyzable radicals and distilling off vapors from said vessel and condensing said vapors outside the vessel until only water is condensed.
Claim 3
Dependent Claim
26 words
Process according to claim 1, wherein the hydrolysis of the silicon compound is carried out in the temperature range of from room temperature to 500° C.
Claim 4
Dependent Claim
20 words
Process according to claim 1, wherein the hydrolysis is carried out under pressure and/or in the presence of superheated steam.
Claim 5
Dependent Claim
20 words
Process according to claim 1 wherein the hydrolysis is carried out in the presence of an acid or a base.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-21 | 1980-09-20 | 1981-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-21 | 1984-09-20 | 1985-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-21 | 1988-09-20 | 1989-03-22 | $7700.00 | Window Closed / Lapsed |