Method of making sensitized polyimide polymers, having catalyst and electroless metal, metal deposits thereon and circuit patterns of various metallization schemes
Assignee: TE Connectivity Corp
•
Filing: 1976-09-20
•
Granted: 1978-03-07
•
Expires: 1996-09-20
Abstract
Abstract A method is disclosed for the generation of circuit patterns on a polyimide type of substrate by preconditioning the substrate's surface with a hydrazine/caustic solution, depositing a catalyst on the surface treated polymer, and exposing the polymer with the catalyst thereon to a bath having a metal therein capable of deposition electrolessly on the polymer surface containing catalyst.
Inventors
- 👤 John Peter Redmond
- 👤 Albert Shirk
- 👤 Elmer John Bottiglier
- 👤 Richard Henry Zimmerman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:57
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/38; H05K3/381; C; C09; C09K; C09K13/00; C09K13/02; C23; C23C; C23C18/00; C23C18/16; C23C18/1601; C23C18/1603; C23C18/1607; C23C18/1608; C23C18/1612; C23C18/18; C23C18/20; C23C18/2006; C23C18/2046; C23C18/2073; C23C18/2086; C23C18/28; C23C18/285; C23C18/30
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
111 words
A method for electrolessly plating a pattern of metal on a polyimide film with good adhesion therebetween comprising the steps of: preconditioning said polyimide film by immersion in a hydrazine-alkali metal hydroxide solution to at least partially etch a surface of said film; neutralizing said surface by rinsing in a dilute hydrochloric acid solution; immersing said film thus preconditioned in tin-palladium solutions separately in sequential steps or in a mixture of these solutios; rinsing said film to wash off loosely held catalyst, immersing said film in an electroless metal plating bath; and depositing on said film a metal from said electroless metal plating bath on areas exposed to said catalytic material.
Claim 2
Independent Claim
111 words
A method for electrolessly plating a pattern of metal on a polyimide film with good adhesion therebetween comprising the steps of: preconditioning said polyimide film by immersion in a hydrazine-alkali metal hydroxide solution to at least partially etch a surface of said film; neutralizing said surface by rinsing in a dilute hydrochloric acid solution; immersing said film thus preconditioned in tin-palladium solutions separately in sequential steps or in a mixture of these solutios; rinsing said film to wash off loosely held catalyst, immersing said film in an electroless metal plating bath; and depositing on said film a metal from said electroless metal plating bath on areas exposed to said catalytic material.
Claim 3
Dependent Claim
27 words
The method as defined in claim 1 wherein the hydrazine alkali metal hydroxide solution has triethanolamine added thereof in order to improve the wettabilithy of the film.
Claim 4
Dependent Claim
19 words
The method as defined in claim 1 wherein said palladium catalyzed film is immersed in an electroless copper bath.
Claim 5
Dependent Claim
19 words
The method as defined in claim 1 wherein said palladium catalyzed film is immersed in an electroless cobalt bath.
Claim 6
Dependent Claim
19 words
The method as defined in claim 1 wherein said palladium catalyzed film is immersed in an electroless gold bath.
Claim 7
Dependent Claim
26 words
The method as defined in claim 1 wherein the said palladium catalyzed film immersed in an electroless nickel bath containing sodium hypophosphite as a reducing agent.
Claim 8
Dependent Claim
21 words
The method as defined in claim 6 wherein said immersion in the electroless nickel bath is for 5 to 20 seconds.
Claim 9
Dependent Claim
26 words
The method as defined in claim 7 wherein said polyimide film with nickel deposited thereon is immersed in an electroless copper bath to deposit copper thereon.
Claim 10
Dependent Claim
117 words
A process for chemically preconditioning a polyimide film in order to electrolessly metal plate on said film with high adhesion which comprises the steps of: a. at least partially etching the surface of said polyimide film by immersion in a solution of hydrazine, unsymmetrical dimethyl hydrazine, monomethyl hydrazine, or phenyl hydrazine, or mixtures of same in admixture with an alkali metal hydroxide solution; b. rinsing and neutralizing the thus treated film; c. immersing said film in a catalyst solution known to initiate metal plating on said etchedareas in an electroless metal plating bath; and d. immersing said catalyzed, preconditioned film in an electroless metal plating bath to deposit a metal catalytically from said bath onto the film.
Claim 11
Dependent Claim
117 words
A process for chemically preconditioning a polyimide film in order to electrolessly metal plate on said film with high adhesion which comprises the steps of: a. at least partially etching the surface of said polyimide film by immersion in a solution of hydrazine, unsymmetrical dimethyl hydrazine, monomethyl hydrazine, or phenyl hydrazine, or mixtures of same in admixture with an alkali metal hydroxide solution; b. rinsing and neutralizing the thus treated film; c. immersing said film in a catalyst solution known to initiate metal plating on said etchedareas in an electroless metal plating bath; and d. immersing said catalyzed, preconditioned film in an electroless metal plating bath to deposit a metal catalytically from said bath onto the film.
Claim 12
Dependent Claim
33 words
The process as defined in claim 9 wherein said catalyst solution comprises a catalyst metal salt in an acidic solution, said metal salt being capable of being rendered catalytically active on said surface.
Claim 13
Dependent Claim
13 words
The process as defined in claim 10, wherein the catalyst is palladium chloride.
Claim 14
Dependent Claim
16 words
The process as defined in claim 10. further comprising a catalyst sensitizer of a tin salt.
Claim 15
Dependent Claim
23 words
The process as defined in claim 10 wherein the catalyst is palladous dichloride and a catalyst sensitizer therefor is a stannous chloride. /
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-06 | 1981-09-05 | 1982-03-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-06 | 1985-09-05 | 1986-03-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-06 | 1989-09-05 | 1990-03-07 | $7700.00 | Window Closed / Lapsed |