Process of manufacturing terminals of a heat-proof metallic thin film resistor
Assignee: Individual
•
Filing: 1976-06-02
•
Granted: 1978-02-14
•
Expires: 1996-06-02
Abstract
Abstract A process for making thin film resistor terminals is described. Terminal fabrication is accomplished by the steps of chemical plating onto the terminal forming surfaces of the resistor and thereafter heat treating between 300° and 800° C in the vacuum, non-oxidation gas or non-oxidation atmosphere or in the air, oxidation gas or oxidation atmosphere. The chemical plating is of nickel, cobalt or nickel-cobalt alloy.
Inventors
- 👤 Nobuo Yasujima
- 👤 Juichiro Arai
- 👤 Natsuo Itokawa
- 👤 Katsumoto Okino
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 12:03
CPC Classifications
H; H01; H01C; H01C17/00; H01C17/28; H01C17/288; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9265; Y10S428/929; Y10S428/9335; Y10S428/936; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082; Y10T29/49101; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12806; Y10T428/12819; Y10T428/12826; Y10T428/31504; Y10T428/31678
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
115 words
A process of manufacturing terminals of a resistor consisting essentially of the steps: (a) depositing a resistive metallic thin film heat proof between 300° and 800° C onto a substrate, (b) chemical plating a metallic layer selected from the group consisting of nickel, cobalt and nickel-cobalt alloy onto terminal portions of said resistor of said resistive metallic thin film to make metallic terminal layers, and (c) heat treating the resultant resistor at a temperature between 300° and 800° C in a non-oxidation atmosphere whereby said terminal layers which contact with said resistive metallic thin film reduce contact resistance therebetween to substantially zero and thereby produce an electrical current noise of the resultant resistor below -20(db).
Claim 2
Dependent Claim
115 words
A process of manufacturing terminals of a resistor consisting essentially of the steps: (a) depositing a resistive metallic thin film heat proof between 300° and 800° C onto a substrate, (b) chemical plating a metallic layer selected from the group consisting of nickel, cobalt and nickel-cobalt alloy onto terminal portions of said resistor of said resistive metallic thin film to make metallic terminal layers, and (c) heat treating the resultant resistor at a temperature between 300° and 800° C in a non-oxidation atmosphere whereby said terminal layers which contact with said resistive metallic thin film reduce contact resistance therebetween to substantially zero and thereby produce an electrical current noise of the resultant resistor below -20(db).
Claim 3
Dependent Claim
19 words
A heat-proof metallic thin film resistor with terminals manufactured according to the process as set forth in claim 1.
Claim 4
Dependent Claim
114 words
A process of manufacturing terminals of resistor consisting essentially of the steps: (a) depositing a resistive metallic thin film heat proof between 300° and 800° C onto a substrate, (b) chemical plating a metallic layer selected from the group consisting of nickel, cobalt and nickel-cobalt alloy onto terminal portions of said resistor of said resistive metallic thin film to make metallic terminal layers, and (c) heat treating the resultant resistor at a temperature between 300° and 800° C in an oxidation atmosphere whereby said terminal layers which contact with said resistive metallic thin film reduce contact resistance therebetween to substantially zero and thereby produce an electrical current noise of the resultant resistor below -20(db).
Claim 5
Dependent Claim
114 words
A process of manufacturing terminals of resistor consisting essentially of the steps: (a) depositing a resistive metallic thin film heat proof between 300° and 800° C onto a substrate, (b) chemical plating a metallic layer selected from the group consisting of nickel, cobalt and nickel-cobalt alloy onto terminal portions of said resistor of said resistive metallic thin film to make metallic terminal layers, and (c) heat treating the resultant resistor at a temperature between 300° and 800° C in an oxidation atmosphere whereby said terminal layers which contact with said resistive metallic thin film reduce contact resistance therebetween to substantially zero and thereby produce an electrical current noise of the resultant resistor below -20(db).
Claim 6
Dependent Claim
19 words
A heat-proof metallic thin film resistor with terminals manufactured according to the process as set forth in claim 3.
Claim 7
Dependent Claim
174 words
A process of manufacturing terminals of a resistor consisting essentially of the steps: (a) despositing a resistive metallic thin film heat proof between 300° and 800° C onto a substrate, (b) chemical plating a metallic layer selected from the group consisting of nickel, cobalt and nickel-cobalt alloy onto said resistive metallic thin film (c) coating a resistive coating material onto the metallic layer, (d) removing the resistive coating material except terminal portions of said resistor to expose said metallic layer, (e) etching the exposed metallic layer to expose the resistive metallic thin film, (f) removing the resistive coating material which has been coated onto said terminal portions of the resistor to expose the metallic layer which acts as terminal layers of said resistor, and (g) heat treating the resultant resistor at a temperature between 300° and 800° C in a non-oxidation atmosphere whereby said terminal layers which contact with said resistive metallic thin film reduce contact resistance therebetween to substantially zero and thereby produce an electrical current noise of the resultant resistor below -20(db).
Claim 8
Dependent Claim
174 words
A process of manufacturing terminals of a resistor consisting essentially of the steps: (a) despositing a resistive metallic thin film heat proof between 300° and 800° C onto a substrate, (b) chemical plating a metallic layer selected from the group consisting of nickel, cobalt and nickel-cobalt alloy onto said resistive metallic thin film (c) coating a resistive coating material onto the metallic layer, (d) removing the resistive coating material except terminal portions of said resistor to expose said metallic layer, (e) etching the exposed metallic layer to expose the resistive metallic thin film, (f) removing the resistive coating material which has been coated onto said terminal portions of the resistor to expose the metallic layer which acts as terminal layers of said resistor, and (g) heat treating the resultant resistor at a temperature between 300° and 800° C in a non-oxidation atmosphere whereby said terminal layers which contact with said resistive metallic thin film reduce contact resistance therebetween to substantially zero and thereby produce an electrical current noise of the resultant resistor below -20(db).
Claim 9
Dependent Claim
19 words
A process as set forth in claim 5, wherein the heat-proof resistive metallic thin film essentially consists of tantalum-silicon.
Claim 10
Dependent Claim
175 words
A process of manufacturing terminals of a resistor consisting essentially of the steps: (a) depositing a resistive metallic thin film heat proof between 300° and 800° C onto a substrate, (b) chemical plating a metallic layer selected from the group consisting of nickel, cobalt and nickel-cobalt alloy onto said resistive metallic thin film, (c) coating a resistive coating material onto the metallic layer, (d) removing the resistive coating material except terminal portions of said resistor to expose said metallic layer, f (e) etching the exposed metallic layer to expose the resistive metallic thin film, (f) removing the resistive coating material which has been coated onto said terminal portions of the resistor to expose the metallic layer which acts as terminal layers of said resistor, and (g) heat treating the resultant resistor at a temperature between 300° and 800° C in an oxidation atmosphere whereby said terminal layers which contact with said resistive metallic thin film reduce contact resistance therebetween to substantially zero and thereby produce an electrical current noise of the resultant resistor below -20(db).
Claim 11
Dependent Claim
175 words
A process of manufacturing terminals of a resistor consisting essentially of the steps: (a) depositing a resistive metallic thin film heat proof between 300° and 800° C onto a substrate, (b) chemical plating a metallic layer selected from the group consisting of nickel, cobalt and nickel-cobalt alloy onto said resistive metallic thin film, (c) coating a resistive coating material onto the metallic layer, (d) removing the resistive coating material except terminal portions of said resistor to expose said metallic layer, f (e) etching the exposed metallic layer to expose the resistive metallic thin film, (f) removing the resistive coating material which has been coated onto said terminal portions of the resistor to expose the metallic layer which acts as terminal layers of said resistor, and (g) heat treating the resultant resistor at a temperature between 300° and 800° C in an oxidation atmosphere whereby said terminal layers which contact with said resistive metallic thin film reduce contact resistance therebetween to substantially zero and thereby produce an electrical current noise of the resultant resistor below -20(db).
Claim 12
Dependent Claim
19 words
A process as set forth in claim 7, wherein the heat-proof resistive metallic thin film essentially consists of tantalum-silicon.
References Cited (Backward Citations)
US3172074A
Cited
US3496512A
Cited
US3546015A
Cited
US3607386A
Cited
US3904461A
Cited
US3930896A
Cited
US3934058A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-13 | 1981-08-15 | 1982-02-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-13 | 1985-08-15 | 1986-02-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-13 | 1989-08-15 | 1990-02-14 | $7700.00 | Window Closed / Lapsed |