Method of manufacturing apertured aluminum oxide substrates
Assignee: RCA Corp
•
Filing: 1976-12-30
•
Granted: 1978-01-17
•
Expires: 1996-12-30
Abstract
Abstract A method for making an apertured aluminum oxide substrate by selectively masking a sapphire wafer, depositing aluminum oxide adjacent the wafer and the mask, and removing the aluminum oxide deposited adjacent the mask and the mask, whereby an aperture is formed in the aluminum oxide. A composite is thus formed of an insulating substrate of monocrystalline sapphire with an insulating epitaxial layer of aluminum oxide apposed thereto, the epitaxial layer having an aperture therein which may be filled with an island of epitaxial silicon.
Inventors
- 👤 Joseph Michael Shaw
- 👤 Karl Heinz Zaininger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 06:26
CPC Classifications
H; H10; H10W; H10W99/00; H10P; H10P14/00; H10P14/20; H10P14/27; H10P14/271; H10P14/29; H10P14/2901; H10P14/2921; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; Y; Y10; Y10S; Y10S438/00; Y10S438/967; Y10S438/969
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
152 words
A method for making a planar composite of a monocrystalline silicon island imbedded in aluminum oxide comprising the steps of: selectively masking a sapphire wafer with a mask of silicon dioxide or a physico-chemical equivalent material, depositing substantially monocrystalline aluminum oxide on said wafer, simultaneously depositing polycrystalline aluminum oxide on said mask, contacting the aluminum oxide deposited on said mask and said wafer with hot phosphoric acid (H 3 PO 4 ), whereby said polycrystalline aluminum oxide is removed by etching but said substantially monocrystalline aluminum oxide remains intact, removing the mask, whereby the wafer is selectively exposed by an aperture in the aluminum oxide deposited on the wafer, depositing monocrystalline silicon into the aperture and on a non-contiguous surface of the deposited aluminum oxide, and removing a portion of said deposited silicon which extends above the deposited aluminum oxide whereby a monocrystalline silicon island remains imbedded in the deposited aluminum oxide.
Claim 2
Independent Claim
152 words
A method for making a planar composite of a monocrystalline silicon island imbedded in aluminum oxide comprising the steps of: selectively masking a sapphire wafer with a mask of silicon dioxide or a physico-chemical equivalent material, depositing substantially monocrystalline aluminum oxide on said wafer, simultaneously depositing polycrystalline aluminum oxide on said mask, contacting the aluminum oxide deposited on said mask and said wafer with hot phosphoric acid (H 3 PO 4 ), whereby said polycrystalline aluminum oxide is removed by etching but said substantially monocrystalline aluminum oxide remains intact, removing the mask, whereby the wafer is selectively exposed by an aperture in the aluminum oxide deposited on the wafer, depositing monocrystalline silicon into the aperture and on a non-contiguous surface of the deposited aluminum oxide, and removing a portion of said deposited silicon which extends above the deposited aluminum oxide whereby a monocrystalline silicon island remains imbedded in the deposited aluminum oxide.
Claim 3
Independent Claim
118 words
A method for making an apertured aluminum oxide layer on a substrate comprising the steps of: selectively masking a portion of a surface of a sapphire wafer with a mask of silicon dioxide or a physico-chemical equivalent material, depositing polycrystalline aluminum oxide on said mask and substantially monocrystalline aluminum oxide on the unmasked portion of said wafer, contacting the aluminum oxide deposited on said mask and said wafer with hot phosphoric acid (H 3 PO 4 ), whereby said polycrystalline aluminum oxide is removed by etching but said substantially monocrystalline aluminum oxide remains intact, and removing the mask, whereby the surface of the wafer is selectively exposed by an aperture in the aluminum oxide deposited on the wafer.
Claim 4
Independent Claim
118 words
A method for making an apertured aluminum oxide layer on a substrate comprising the steps of: selectively masking a portion of a surface of a sapphire wafer with a mask of silicon dioxide or a physico-chemical equivalent material, depositing polycrystalline aluminum oxide on said mask and substantially monocrystalline aluminum oxide on the unmasked portion of said wafer, contacting the aluminum oxide deposited on said mask and said wafer with hot phosphoric acid (H 3 PO 4 ), whereby said polycrystalline aluminum oxide is removed by etching but said substantially monocrystalline aluminum oxide remains intact, and removing the mask, whereby the surface of the wafer is selectively exposed by an aperture in the aluminum oxide deposited on the wafer.
Claim 5
Dependent Claim
19 words
A method according to claim 1, wherein the hot phosphoric acid is at a temperature of approximately 180° C.
Claim 6
Dependent Claim
20 words
A method according to claim 3, wherein the aluminum oxides are grown at a temperature between 875° and 990° C.
Claim 7
Dependent Claim
22 words
A method according to claim 4, wherein the aluminum oxide depositions occur at a rate between 50 and 400 Angstroms per minute.
Claim 8
Dependent Claim
21 words
A method according to claim 5, wherein the aluminum oxides are deposited from pyrohydrolysis of aluminum trichloride, hydrogen and carbon dioxide.
Claim 9
Dependent Claim
51 words
A method according to claim 6, wherein the deposited aluminum oxides are annealed at growth temperatures in hydrogen or a physico-chemically equivalent material for at least 10 minutes, and the annealed oxides are then slow-cooled in said hydrogen or said material until the temperature decreases to about 300° to 400° C.
Claim 10
Dependent Claim
20 words
A method according to claim 7, in which said slow cooling is at a rate of 20°-25° C per minute.
References Cited (Backward Citations)
US3272670A
Cited
US3496037A
Cited
US3661676A
Cited
US3698947A
Cited
US3740280A
Cited
US3766637A
Cited
US3861968A
Cited
US3878005A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-16 | 1981-07-18 | 1982-01-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-16 | 1985-07-18 | 1986-01-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-16 | 1989-07-18 | 1990-01-17 | $7700.00 | Window Closed / Lapsed |