Abstract This invention relates to a process for producing a tetra-silicic mica having the formula Na 0 .6 - 0.8 Mg 2 .6 - 2.7 (Si 4 O 10 )F 2 which comprises mixing components selected from the group of sodium fluoride (NaF, sodium silicofluoride (Na 2 SiF 6 ), magnesium fluoride (MgF 2 ), magnesia (MgO) and silica (SiO 2 ) in a mole ratio of (a) 1 - 1.2 NaF : 0.5 - 1.2 MgF 2 : 2 MgO : 4 SiO 2 or (b) 0.5 - 0.8 Na 2 SiF 6 : 0.5 - 1.2 MgF 2 : 2 MgO : 4 SiO 2 , melting the mixture at a temperature of 1300° C to 1500° C and cooling the melt to obtain a crystal. This invention further relates to a water sol of flake-like ultra-fine particles of tetra-silicic mica produced in accordance with claim 1, wherein most of the flake-like particles dispersed in water have a thickness of less than 50 A and an average diameter of the flat plane of between 500 A and 3000 A.
Synthetic tetra-silicic mica having the formula Na 0 .6-0.8 Mg 2 .6-2.7 (Si 4 O 10 )F 2 which is swellable and cleavable in water without heating, thus producing particles having a thickness of less than 50 A and an average diameter of the flat plane of between 500 A and 3000 A.
Claim 2
Dependent Claim
53 words
Synthetic tetra-silicic mica having the formula Na 0 .6-0.8 Mg 2 .6-2.7 (Si 4 O 10 )F 2 which is swellable and cleavable in water without heating, thus producing particles having a thickness of less than 50 A and an average diameter of the flat plane of between 500 A and 3000 A.
Claim 3
Dependent Claim
61 words
Water sol of flake-like ultra-fine particles of tetra-silicic mica having the formula Na 0 .6-0.8 Mg 2 .6-2.7 (Si 4 O 10 )F 2 , prepared by swelling and cleaving the tetra-silicic mica in water without heating and having a thickness of less than 50 A and an average diameter of the flat plane of between 500 A and 3000 A.
Claim 4
Dependent Claim
61 words
Water sol of flake-like ultra-fine particles of tetra-silicic mica having the formula Na 0 .6-0.8 Mg 2 .6-2.7 (Si 4 O 10 )F 2 , prepared by swelling and cleaving the tetra-silicic mica in water without heating and having a thickness of less than 50 A and an average diameter of the flat plane of between 500 A and 3000 A.
Claim 5
Dependent Claim
77 words
A synthetic tetra-silicic mica according to claim 1 produced by the process which comprises preparing a mixture on a molar basis of (a) 1-1.2 NaF : 0.15-1.2 MgF 2 : 2 MgO : 4 SiO 2 or (b) 0.5-0.8 Na 2 SiF 6 : 0.5-1.2 MgF 2 : 2 MgO : 4 SiO 2 , melting the mixture at a temperature of 1300° C to 1500° C and cooling the melt to obtain said mica crystalline form.