Method of preparing a monosize silver halide emulsion involving Ostwald ripening followed by a crystal growth stage
Assignee: Ilford Imaging UK Ltd
•
Filing: 1975-08-04
•
Granted: 1978-01-10
•
Expires: 1995-08-04
Abstract
Abstract A method of preparing a monosize silver halide emulsion of which most of the silver halide crystals are of the twinned octahedral type is provided. An aqueous solution of a silver salt and an aqueous solution of an alkali metal or ammonium halide in an aqueous dispersing medium containing a protective colloid are mixed at such concentration that the silver halide is nucleated, causing the silver halide nuclei to increase in size in the presence of a silver halide solvent by Ostwald ripening to produce a population of twinned octahedral seed crystals. Then the maximum rate of addition of silver salt and alkali metal or ammonium halide which is possible without renucleation occurring and the minimum rate of addition of silver salt and alkali metal or ammonium halide which is possible without Ostwald ripening occurring is determined and the seed crystals are caused to grow by adding to the aqueous dispersing medium aqueous silver salt solution and aqueous alkali metal or ammonium halide solution at a rate between the predetermined maximum and minimum rates and then at intervals the maximum and minimum addition rates are re-determined and the addition rates of silver and halide are adjusted to ensure that at all times during the crystal growth stage neither renucleation nor Ostwald ripening occurs, the p Br of the liquid phase being maintained above 0.15 during the whole crystal growth stage. The silver halide emulsions are useful for preparing photographic material.
Inventors
- 👤 John Derek Lewis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:33
CPC Classifications
G; G03; G03C; G03C1/00; G03C1/005; G03C1/015; G03C1/035; G03C1/0051; G03C2001/0058; G03C2001/0357
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
265 words
A method of preparing a monosize silver halide emulsion of which most of the silver halide crystals are of the twinned octahedral type which comprises a. mixing an aqueous solution of a silver salt and an aqueous solution of an alkali metal or ammonium halide in an aqueous dispersing medium containing a protective colloid at such a concentration that the silver halide is nucleated, b. causing the silver halide nuclei to increase in size in the presence of a silver halide solvent by Ostwald ripening to produce a population of twinned octahedral seed crystals, c. determining the maximum rate of addition of silver salt and alkali metal or ammonium halide which is possible without renucleation occurring and determining the minimum rate of addition of silver salt and alkali metal or ammonium halide which is possible without Ostwald ripening occurring, said determination is carried out by taking samples of the crystals, adding an equal quantity of silver halide at increasing and decreasing rates, respectively, and observing on a microscope when renucleation and Ostwald ripening, respectively, occur, d. causing the seed crystals to grow by adding to the aqueous dispersing medium aqueous silver salt solution and aqueous alkali metal or ammonium halide solution at a rate between the predetermined maximum and minimum rates and then at intervals re-determining the maximum and minimum addition rates and adjusting the addition rates of silver and halides to ensure that at all times during the crystal growth stage neither renucleation nor Ostwald ripening occurs, the p Br of the liquid phase being maintained above 0.15 during the whole crystal growth stage.
Claim 2
Independent Claim
265 words
A method of preparing a monosize silver halide emulsion of which most of the silver halide crystals are of the twinned octahedral type which comprises a. mixing an aqueous solution of a silver salt and an aqueous solution of an alkali metal or ammonium halide in an aqueous dispersing medium containing a protective colloid at such a concentration that the silver halide is nucleated, b. causing the silver halide nuclei to increase in size in the presence of a silver halide solvent by Ostwald ripening to produce a population of twinned octahedral seed crystals, c. determining the maximum rate of addition of silver salt and alkali metal or ammonium halide which is possible without renucleation occurring and determining the minimum rate of addition of silver salt and alkali metal or ammonium halide which is possible without Ostwald ripening occurring, said determination is carried out by taking samples of the crystals, adding an equal quantity of silver halide at increasing and decreasing rates, respectively, and observing on a microscope when renucleation and Ostwald ripening, respectively, occur, d. causing the seed crystals to grow by adding to the aqueous dispersing medium aqueous silver salt solution and aqueous alkali metal or ammonium halide solution at a rate between the predetermined maximum and minimum rates and then at intervals re-determining the maximum and minimum addition rates and adjusting the addition rates of silver and halides to ensure that at all times during the crystal growth stage neither renucleation nor Ostwald ripening occurs, the p Br of the liquid phase being maintained above 0.15 during the whole crystal growth stage.
Claim 3
Dependent Claim
35 words
A method according to claim 1 wherein during crystal growth the pBr of the liquid phase is controlled between 1.00 and 1.30 and the temperature of the liquid phase is between 45° to 55° C.
Claim 4
Dependent Claim
30 words
A method according to claim 2 wherein during crystal growth the pBr of the liquid phase is controlled at 1.15 and the temperature of the liquid phase is 50° C.
Claim 5
Dependent Claim
37 words
A method according to claim 1 wherein the formation of twinned seed crystals takes place at a pAg of over 11.0 and the growth of the twinned octahedral seed crystals takes place at a pAg below 10.1.
Claim 6
Dependent Claim
66 words
A method according to claim 1 wherein the aqueous silver salt solution and the aqueous alkali metal or ammonium halide solution are added at a continuously increasing rate which is approximately proportional to the time from the start of crystal growth after seed formation, the remainder of the conditions in the dispersing medium which affect the solubility of the silver halide in solution being maintained constant.
Claim 7
Dependent Claim
40 words
A method according to claim 1 wherein the rate of addition of the silver salt and the alkali metal or ammonium halide during crystal growth is ninety percent of the maximum rate of addition which is possible without renucleation occuring.
Claim 8
Dependent Claim
73 words
A method according to claim 1 wherein the aqueous silver salt solution and the aqueous alkali-metal or ammonium halide solution are added in step-wise increased amounts, the rates of which are approximately proportional to the time from the start of crystal growth after the formation of the twinned octahedral seed crystals, the remainder of the conditions in the dispersing medium which effect the solubility of the silver halide in solution being maintained constant.
Claim 9
Dependent Claim
16 words
A monosized silver halide emulsion which has been prepared by the method claimed in claim 1.
Claim 10
Dependent Claim
17 words
Photographic material which comprises in a layer thereof at least one emulsion as claimed in claim 8.
References Cited (Backward Citations)
US3655394A
Cited
US3650757A
Cited
US3736144A
Cited
FR2078586A5
Cited
GB1335925A
Cited
US3817756A
Cited
US3773516A
Cited
US3790387A
Cited
US3885970A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-09 | 1981-07-11 | 1982-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-09 | 1985-07-11 | 1986-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-09 | 1989-07-11 | 1990-01-10 | $7700.00 | Window Closed / Lapsed |