Heat fixing member for electrophotographic copiers
Assignee: Xerox Ltd
•
Filing: 1976-12-17
•
Granted: 1977-12-20
•
Expires: 1996-12-17
Abstract
Abstract Silicone rubber is employed as a coating material on a fuser member and adhered to the base member by means of a novel polysiloxane composition. The novel polysiloxane composition comprises specified quantities of two moieties of organopolysiloxane, an allyl ester of a polybasic acid, an aliphatic salt of a metal, and a silane, and strongly adheres the silicone rubber outer layer to the base member or core even when silicone oil is used as a release agent on the fuser member.
Inventors
- 👤 Koichi Takiguchi
- 👤 Teruhiko Itami
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 18:45
CPC Classifications
G; G03; G03G; G03G15/00; G03G15/20; G03G15/2003; G03G15/2014; G03G15/2053; G03G15/2057; C; C08; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K5/00; C08K5/04; C08K5/09; C08K5/10; C08K5/11; C08K5/54; C08L; C08L83/00; C08L83/04; C09; C09D; C09D183/00; C09D183/04; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
300 words
A fuser member for pressure fusing electrostatic toner images at elevated temperatures comprising a substrate coated with at least one layer of a heat resistant silicone rubber and having a polysiloxane composition intermediate the silicone rubber layer and the substrate, said polysiloxane composition having improved adherence to said substrate and said silicone rubber and having resistance to heat and silicone oil degradation, and comprising: a. 100 parts by weight of an organopolysiloxane of the formula, R 1 n SiO 4-n/2 wherein R 1 is a substituted or unsubstituted monovalent hydrocarbon group, at least 80 mole percent of R 1 being a methyl group and having an aliphatic unsaturated group in an amount not more than 0.2 mole percent, and were n is a positive integer of from 1.98 to 2.01, and having a viscosity greater than 100,000 centistokes at 25° C; b. 5 - 100 parts by weight of an organopolysiloxane of the formula, R 2 SiO 4-m/2 wherein R 2 is a substituted or unsubstituted monovalent hydrocarbon group, about 3 to 25 mole percent of the total R 2 being a vinyl group, and where m is a positive integer from 1.9 to 2.3, and having a viscosity of from about 5 to 10,000 centistokes at 25° C; c. 10 to 80 parts by weight of an allyl ester of a polybasic acid; d. 3 to 20 parts by weight of an aliphatic acid salt of a metal; and e. 0.2 to 20 parts by weight of a silane compound expressed by a general formula, R 3 Si(OR 4 ) 3 wherein R 3 is an unsaturated hydrocarbon group and R 4 is a member selected from the group consisting of a methyl group, an ethyl group, a β-methoxyethyl group and a β-ethoxyethyl group, and partially hydrolyzed products thereof.
Claim 2
Dependent Claim
300 words
A fuser member for pressure fusing electrostatic toner images at elevated temperatures comprising a substrate coated with at least one layer of a heat resistant silicone rubber and having a polysiloxane composition intermediate the silicone rubber layer and the substrate, said polysiloxane composition having improved adherence to said substrate and said silicone rubber and having resistance to heat and silicone oil degradation, and comprising: a. 100 parts by weight of an organopolysiloxane of the formula, R 1 n SiO 4-n/2 wherein R 1 is a substituted or unsubstituted monovalent hydrocarbon group, at least 80 mole percent of R 1 being a methyl group and having an aliphatic unsaturated group in an amount not more than 0.2 mole percent, and were n is a positive integer of from 1.98 to 2.01, and having a viscosity greater than 100,000 centistokes at 25° C; b. 5 - 100 parts by weight of an organopolysiloxane of the formula, R 2 SiO 4-m/2 wherein R 2 is a substituted or unsubstituted monovalent hydrocarbon group, about 3 to 25 mole percent of the total R 2 being a vinyl group, and where m is a positive integer from 1.9 to 2.3, and having a viscosity of from about 5 to 10,000 centistokes at 25° C; c. 10 to 80 parts by weight of an allyl ester of a polybasic acid; d. 3 to 20 parts by weight of an aliphatic acid salt of a metal; and e. 0.2 to 20 parts by weight of a silane compound expressed by a general formula, R 3 Si(OR 4 ) 3 wherein R 3 is an unsaturated hydrocarbon group and R 4 is a member selected from the group consisting of a methyl group, an ethyl group, a β-methoxyethyl group and a β-ethoxyethyl group, and partially hydrolyzed products thereof.
Claim 3
Dependent Claim
14 words
The fuser member of claim 1 wherein the polysiloxane composition further comprises ferric oxide.
Claim 4
Dependent Claim
14 words
The fuser member of claim 1 wherein the polysiloxane composition further comprises cerium oxide.
Claim 5
Dependent Claim
24 words
The fuser member of claim 1 further comprising multiple layers of heat-resistant silicone rubber and having said polysiloxane composition intermediate said silicone rubber layers.
Claim 6
Independent Claim
272 words
A method of adhering a heat-resistant silicone rubber layer to a base member comprising applying at least one layer of a polysiloxane composition intermediate the base member and the silicone rubber layer, said polysiloxane composition comprising: a. 100 parts by weight of an organopolysiloxane of the formula, R 1 n SiO 4-n/2 wherein R 1 is a substituted or unsubstituted monovalent hydrocarbon groups, at least 80 mole percent of R 1 being a methyl group and having an aliphatic unsaturated group in an amount not more than 0.2 mole percent, and where n is a positive integer of from 1.98 to 2.01, and having a viscosity greater than 100,000 centistokes at 25° C; b. 5 - 100 parts by weight of an organopolysiloxane of the formula, R 2 SiO 4-m/2 wherein R 2 is a substituted or unsubstituted monovalent hydrocarbon group, about 3 to 25 mole percent of the total R 2 being a vinyl group, and where m is a positive integer from 1.9 to 2.3, and having a viscosity of from about 5 to 10,000 centistokes at 25° C; c. 10 to 80 parts by weight of an allyl ester of a polybasic acid; d. 3 to 20 parts by weight of an aliphatic acid salt of a metal; and e. 0.2 to 20 parts by weight of a silane compound expressed by a general formula, R 3 Si(OR 4 ) 3 wherein R 3 is an unsaturated hydrocarbon group and R 4 is a member selected from the group consisting of a methyl group, an ethyl group, a β-methoxyethyl group and a β-ethoxyethyl group, and partially hydrolyzed products thereof.
Claim 7
Independent Claim
272 words
A method of adhering a heat-resistant silicone rubber layer to a base member comprising applying at least one layer of a polysiloxane composition intermediate the base member and the silicone rubber layer, said polysiloxane composition comprising: a. 100 parts by weight of an organopolysiloxane of the formula, R 1 n SiO 4-n/2 wherein R 1 is a substituted or unsubstituted monovalent hydrocarbon groups, at least 80 mole percent of R 1 being a methyl group and having an aliphatic unsaturated group in an amount not more than 0.2 mole percent, and where n is a positive integer of from 1.98 to 2.01, and having a viscosity greater than 100,000 centistokes at 25° C; b. 5 - 100 parts by weight of an organopolysiloxane of the formula, R 2 SiO 4-m/2 wherein R 2 is a substituted or unsubstituted monovalent hydrocarbon group, about 3 to 25 mole percent of the total R 2 being a vinyl group, and where m is a positive integer from 1.9 to 2.3, and having a viscosity of from about 5 to 10,000 centistokes at 25° C; c. 10 to 80 parts by weight of an allyl ester of a polybasic acid; d. 3 to 20 parts by weight of an aliphatic acid salt of a metal; and e. 0.2 to 20 parts by weight of a silane compound expressed by a general formula, R 3 Si(OR 4 ) 3 wherein R 3 is an unsaturated hydrocarbon group and R 4 is a member selected from the group consisting of a methyl group, an ethyl group, a β-methoxyethyl group and a β-ethoxyethyl group, and partially hydrolyzed products thereof.
Claim 8
Dependent Claim
13 words
The method of claim 5 wherein the polysiloxane composition further comprises ferric oxide.
Claim 9
Dependent Claim
13 words
The method of claim 5 wherein the polysiloxane composition further comprises cerium oxide.
Claim 10
Dependent Claim
42 words
The method of claim 5 further comprising applying at least one additional silicone rubber layer to the silicone rubber layer on the base member and adhering said additional silicone rubber layer with a layer of polysiloxane composition intermediate the silicone rubber layers.
References Cited (Backward Citations)
GB778348A
Cited
US2860083A
Cited
US3087832A
Cited
US3225419A
Cited
US3511729A
Cited
US3686731A
Cited
US3772122A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-19 | 1981-06-20 | 1981-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-19 | 1985-06-20 | 1985-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-19 | 1989-06-20 | 1989-12-20 | $7700.00 | Window Closed / Lapsed |