Process for manufacturing a solar cell from a reject semiconductor wafer
Assignee: Silicon Materials Inc
•
Filing: 1975-12-31
•
Granted: 1977-12-13
•
Expires: 1995-12-31
Abstract
Abstract A process for manufacturing a solar cell from a reject semiconductor wafer comprising stripping all external layers from the wafer, etching the surfaces of the wafer so as to effectively remove all P/N junctions without pitting the wafer surface, introducing a layer of dopant to form a P/N junction in the front wafer surface, forming a first patterned conductive electrode over the dopant layer, and forming a second conductive electrode on the back surface of the wafer. In the preferred embodiment a sputtering operation is used to form the conductive electrodes.
Inventors
- 👤 John E. Lawrence
- 👤 Icheng Wu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:00
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/121; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/547; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
105 words
A process for manufacturing a solar cell from a reject semiconductor wafer containing process induced contaminants in the silicon bulk latice, comprising: stripping all external layers from said wafer; etching the surfaces of said wafer so as to effectively remove all P/N junctions; introducing a layer of dopant to form a P/N junction in a first of said wafer surfaces; forming a first conductive electrode over said layer of dopant; and forming a second conductive electrode on a second surface of said wafer opposed to said first surface, said solar cell being produced from the reject wafer without gettering to eliminate the process induced contaminants.
Claim 2
Dependent Claim
105 words
A process for manufacturing a solar cell from a reject semiconductor wafer containing process induced contaminants in the silicon bulk latice, comprising: stripping all external layers from said wafer; etching the surfaces of said wafer so as to effectively remove all P/N junctions; introducing a layer of dopant to form a P/N junction in a first of said wafer surfaces; forming a first conductive electrode over said layer of dopant; and forming a second conductive electrode on a second surface of said wafer opposed to said first surface, said solar cell being produced from the reject wafer without gettering to eliminate the process induced contaminants.
Claim 3
Dependent Claim
65 words
A process for manufacturing a solar cell from a reject semiconductor wafer as recited in claim 1 wherein the step of forming a first conductive electrode includes providing an external metal mask having a preselected pattern of slots therethrough; laying the mask in a covering relationship on said layer of dopant; and sputtering a first conductive material on said layer of dopant through said pattern.
Claim 4
Dependent Claim
38 words
A process for manufacturing a solar cell from a reject semiconductor wafer as recited in claim 2 wherein the substep of sputtering is followed by the step of sputtering a second conductive material on said first conductive material.
Claim 5
Dependent Claim
31 words
A process for manufacturing a solar cell from a reject semiconductor wafer as recited in claim 3 wherein said first conductive material is titanium and said second conductive material is silver.
Claim 6
Dependent Claim
38 words
A process for manufacturing a solar cell from a reject semiconductor wafer as recited in claim 4 wherein said titanium has a depth of about 1500 Anstroms and wherein said silver has a depth of about 50,000 Angstroms.
Claim 7
Dependent Claim
40 words
A process for manufacturing a solar cell from a reject semiconductor wafer as recited in claim 2 wherein the top surface of said layer is bombarded with ions prior to the step of sputtering to remove contaminants from said wafer.
Claim 8
Dependent Claim
52 words
A process for manufacturing a solar cell from a reject semiconductor wafer as recited in claim 1 wherein the step of etching includes immersing said wafer in an etchant having a constant etching rate, and agitating the etchant relative to said wafer so as to produce a nonpreferential removal of said surfaces.
Claim 9
Dependent Claim
39 words
A process for manufacturing a solar cell from a reject semiconductor wafer as recited in claim 1 wherein the step of introducing a layer of dopant includes heating said wafer, and forming a layer of boron over said surfaces.
Claim 10
Dependent Claim
41 words
A process for manufacturing a solar cell from a reject semiconductor wafer as recited in claim 8 wherein said boron is diffused into said wafer to a depth corresponding to a sheet resistivity of about 60 ± 30 ohms per square.
Claim 11
Dependent Claim
76 words
A process for manufacturing a solar cell from a reject semiconductor wafer as recited in claim 8 wherein the step of forming a layer of boron is followed by the steps of forming an etchant-resistant coating over at least a portion of said boron layer, etching the surfaces of said boron layer so as to effectively remove said boron layer from those surfaces not covered with said coating, and removing said coating from said boron layer.
Claim 12
Dependent Claim
52 words
A process for manufacturing a solar cell from a reject semiconductor wafer as recited in claim 1 wherein the step of introducing a layer of dopant includes bombarding said first surface with boron ions, followed by step of annealing said wafer so as to allow the boron to stabilize within said wafer.
Claim 13
Dependent Claim
32 words
A process for manufacturing a solar cell from a reject semiconductor wafer as described in claim 1 wherein said solar cell is made without polishing any surface of the reject semiconductor wafer.
Claim 14
Dependent Claim
115 words
A process for manufacturing a solar cell from a reject semiconductor wafer having one type conductivity and containing process induced contaminants in the silicon bulk latice, comprising: stripping all external layers from said wafer; etching the surfaces of said wafer so as to effectively remove the P/N junctions; forming a layer of material having an opposed type conductivity on a first of said wafer surfaces, said first surface providing a P/N junction; forming a first conductive electrode over said layer; and forming a second conductive electrode on a second surface of said wafer opposed to said first surface, said solar cell being produced from the reject wafer without gettering to eliminate the process induced contaminants
Claim 15
Dependent Claim
115 words
A process for manufacturing a solar cell from a reject semiconductor wafer having one type conductivity and containing process induced contaminants in the silicon bulk latice, comprising: stripping all external layers from said wafer; etching the surfaces of said wafer so as to effectively remove the P/N junctions; forming a layer of material having an opposed type conductivity on a first of said wafer surfaces, said first surface providing a P/N junction; forming a first conductive electrode over said layer; and forming a second conductive electrode on a second surface of said wafer opposed to said first surface, said solar cell being produced from the reject wafer without gettering to eliminate the process induced contaminants
Claim 16
Dependent Claim
32 words
A process for manufacturing a solar cell from a reject semiconductor wafer as described in claim 13, wherein said solar cell is made without polishing any surface of the reject semiconductor wafer.
References Cited (Backward Citations)
US3151004A
Cited
US3533850A
Cited
US3600797A
Cited
US3617373A
Cited
US3772768A
Cited
US3783050A
Cited
US3923567A
Cited
US3985597A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-12 | 1981-06-13 | 1981-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-12 | 1985-06-13 | 1985-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-12 | 1989-06-13 | 1989-12-13 | $7700.00 | Window Closed / Lapsed |