Etching method for flattening a silicon substrate utilizing an anisotropic alkali etchant
Assignee: Hitachi Ltd
•
Filing: 1976-10-05
•
Granted: 1977-11-01
•
Expires: 1996-10-05
Abstract
Abstract An epitaxial silicon layer is grown on a principal surface of the (100) crystal face of a silicon single crystal having a depressed portion in the principal surface. The epitaxial silicon layer is flattened by etching, the epitaxial silicon layer being formed to a sufficient thickness so that the side surfaces of the crystal face (111) of a new depressed portion as viewed in a vertical section (the new depressed portion being formed in a surface of the epitaxial silicon layer in correspondence with the first-mentioned depressed portion) intersect at a level which is, at the lowest, the final plane of the etching. The etching is anisotropic etching with an alkali etchant, by which the epitaxial silicon layer is etched down to the final plane.
Inventors
- 👤 Masayoshi Yoshimura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:50
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/60; H10P50/64; H10P50/642; H10P50/644; H10W; H10W10/00; H10W10/01; H10W10/031; H10W10/30; H10W15/00; H10W15/01
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
123 words
An etching method for flattening a silicon substrate wherein an epitaxial silicon layer is grown on the (100) crystal face of the silicon single-crystal substrate, the silicon single-crystal substrate having a depressed portion in its principal face, and etching for flattening the epitaxial silicon layer is carried out; said method comprising the steps of forming said epitaxial silicon layer to such a sufficient thickness that a position at which side surfaces of a new depressed portion to be formed in a surface of said epitaxial silicon layer, said side surface having a crystal face (111), intersect becomes at least a final surface of the etching, and subjecting said epitaxial silicon layer to anisotripic etching with an alkali etchant down to said final surface.
Claim 2
Dependent Claim
123 words
An etching method for flattening a silicon substrate wherein an epitaxial silicon layer is grown on the (100) crystal face of the silicon single-crystal substrate, the silicon single-crystal substrate having a depressed portion in its principal face, and etching for flattening the epitaxial silicon layer is carried out; said method comprising the steps of forming said epitaxial silicon layer to such a sufficient thickness that a position at which side surfaces of a new depressed portion to be formed in a surface of said epitaxial silicon layer, said side surface having a crystal face (111), intersect becomes at least a final surface of the etching, and subjecting said epitaxial silicon layer to anisotripic etching with an alkali etchant down to said final surface.
Claim 3
Independent Claim
163 words
A method of manufacturing a semiconductor device wherein an epitaxial silicon layer is grown on a principal face of a silicon single-crystal substrate which is the (100) crystal face, the silicon single-crystal substrate having depressed portions in its principal face, and etching for flattening the epitaxial silicon layer is carried out; comprising the steps of forming said epitaxial silicon layer to such a sufficient thickness that a position at which side surfaces of each of new depressed portions to be formed in a surface of said epitaxial silicon layer, said side surface having a crystal face (111), intersect becomes at least a final surface of the etching, subjecting said epitaxial silicon layer to anisotropic etching with an alkali etchant, and subsequently doping selected parts of said epitaxial silicon layer outside a surface of said depressed portion of said substrate with an impurity of the same conductivity type as that of said substrate to the extent that the impurity-doped layers extend to said substrate.
Claim 4
Independent Claim
163 words
A method of manufacturing a semiconductor device wherein an epitaxial silicon layer is grown on a principal face of a silicon single-crystal substrate which is the (100) crystal face, the silicon single-crystal substrate having depressed portions in its principal face, and etching for flattening the epitaxial silicon layer is carried out; comprising the steps of forming said epitaxial silicon layer to such a sufficient thickness that a position at which side surfaces of each of new depressed portions to be formed in a surface of said epitaxial silicon layer, said side surface having a crystal face (111), intersect becomes at least a final surface of the etching, subjecting said epitaxial silicon layer to anisotropic etching with an alkali etchant, and subsequently doping selected parts of said epitaxial silicon layer outside a surface of said depressed portion of said substrate with an impurity of the same conductivity type as that of said substrate to the extent that the impurity-doped layers extend to said substrate.
Claim 5
Dependent Claim
40 words
The method of manufacturing a semiconductor device as defined in claim 2, further comprising the step of forming a desired circuit element in each of the large number of epitaxial silicon layers which are electrically isolated by said impurity-doped layers.
Claim 6
Dependent Claim
38 words
The method of manufacturing a semiconductor device as defined in claim 3, wherein an element for power is formed within the deep epitaxial silicon layer, while an element for a small signal is formed within the shallow portion.
Claim 7
Independent Claim
168 words
A method of manufacturing a semiconductor device comprising the steps of: a. removing a prescribed portion of semiconductor material from the (100) crystal face of a silicon single crystal substrate so as to form a depression in said substrate; b. epitaxially growing a silicon layer on said (100) crystal face and in the depression of said substrate so as to fill said depression and so that said layer extends above the original (100) crystal face of said substrate while leaving a depression in said silicon layer above the depression in said substrate; and c. subjecting said epitaxially grown silicon layer to anisotropic etching with an alkali etchant; and wherein step (b) comprises epitaxially growing said silicon layer to a thickness such that lines extending along the side surfaces of the depression in said silicon layer, as said silicon layer is etched by said alkali etchant, intersect at a point no deeper from the surface of said silicon layer than the extent to which said silicon layer is etched.
Claim 8
Independent Claim
168 words
A method of manufacturing a semiconductor device comprising the steps of: a. removing a prescribed portion of semiconductor material from the (100) crystal face of a silicon single crystal substrate so as to form a depression in said substrate; b. epitaxially growing a silicon layer on said (100) crystal face and in the depression of said substrate so as to fill said depression and so that said layer extends above the original (100) crystal face of said substrate while leaving a depression in said silicon layer above the depression in said substrate; and c. subjecting said epitaxially grown silicon layer to anisotropic etching with an alkali etchant; and wherein step (b) comprises epitaxially growing said silicon layer to a thickness such that lines extending along the side surfaces of the depression in said silicon layer, as said silicon layer is etched by said alkali etchant, intersect at a point no deeper from the surface of said silicon layer than the extent to which said silicon layer is etched.
Claim 9
Dependent Claim
50 words
A method according to claim 5, wherein said silicon single crystal substrate has a first conductivity type, and further comprising the step (d) of forming, prior to step (b), a high impurity concentration layer of a second conductivity type, opposite said first conductivity type, in the depression in said substrate.
Claim 10
Dependent Claim
30 words
A method according to claim 6, wherein step (d) comprises introducing an impurity of said second conductivity type into the bottom and side walls of the depression in said substrate.
Claim 11
Dependent Claim
45 words
A method according to claim 7, wherein said silicon layer has said second conductivity type and further comprising the step (e) of forming a prescribed circuit element in that portion of the etched silicon layer overlying the depression on said substrate, subsequent to step (c).
Claim 12
Dependent Claim
42 words
A method according to claim 8, further comprising the step (f) of introducing an impurity of said first conductivity type into a portion of said silicon layer surrounding said circuit element so as to provide PN junction isolation for said circuit element.
Claim 13
Dependent Claim
26 words
A method according to claim 5, wherein the side walls of the depression in said silicon substrate lie in the (111) crystal face of said substrate.
References Cited (Backward Citations)
US3486953A
Cited
US3426254A
Cited
US3486892A
Cited
US3728166A
Cited
US3664894A
Cited
US3755012A
Cited
US3990925A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-31 | 1981-05-02 | 1981-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-31 | 1985-05-02 | 1985-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-31 | 1989-05-02 | 1989-11-01 | $7700.00 | Window Closed / Lapsed |