Patent US4053976A successfully refreshed from Google Patents.
US4053976A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making Nb3 Sn composite wires and cables
Assignee: General Electric Co
•
Filing: 1975-06-27
•
Granted: 1977-10-18
•
Expires: 1995-06-27
Abstract
Abstract By providing a nickel or copper overcoat to a tin coating on a niobium-copper multifilamentary composite wire, one can avoid the necessity for choosing between poor superconducting properties due to tin droplet formation and substantially increasing production costs by adding a number of special processing steps.
Inventors
- 👤 Ronald M. Scanlan
- 👤 William A. Fietz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 04:11
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0184; Y; Y10; Y10S; Y10S505/00; Y10S505/825; Y10S505/917; Y10S505/918; Y10S505/919; Y10S505/921; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49014
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
95 words
In the method of producing Nb 3 Sn composite wire by forming a niobium-copper composite wire in which the niobium is in the form of elongated filaments in a copper matrix, coating the wire with tin, heating the coated wire and diffusing the tin into the wire and thereafter heating the wire to cause reaction of the tin to form Nb 3 Sn in the wire, the combination of the step of depositing on the tin-coated wire a layer from about 0.1 to 1.0 micron thick of nickel or copper prior to the diffusion-heating step.
Claim 2
Dependent Claim
95 words
In the method of producing Nb 3 Sn composite wire by forming a niobium-copper composite wire in which the niobium is in the form of elongated filaments in a copper matrix, coating the wire with tin, heating the coated wire and diffusing the tin into the wire and thereafter heating the wire to cause reaction of the tin to form Nb 3 Sn in the wire, the combination of the step of depositing on the tin-coated wire a layer from about 0.1 to 1.0 micron thick of nickel or copper prior to the diffusion-heating step.
Claim 3
Dependent Claim
20 words
The method of claim 1 in which the nickel or copper-coated wire is cabled prior to the diffusion heating step.
Claim 4
Dependent Claim
14 words
The method of claim 1 in which the nickel or copper layer is electroplated.
Claim 5
Independent Claim
84 words
The method of making a Nb 3 Sn composite wire which comprises the steps of providing a copper-niobium composite wire in which the niobium is in the form of elongated filaments in a copper matrix and extending lengthwise thereof, coating the wire with tin, depositing a layer of nickel or copper from about 0.1 to 1.0 micron thick over the tin coating, heating the composite coated wire and diffusing the tin into the copper and reacting the tin with the niobium of the filaments.
Claim 6
Independent Claim
84 words
The method of making a Nb 3 Sn composite wire which comprises the steps of providing a copper-niobium composite wire in which the niobium is in the form of elongated filaments in a copper matrix and extending lengthwise thereof, coating the wire with tin, depositing a layer of nickel or copper from about 0.1 to 1.0 micron thick over the tin coating, heating the composite coated wire and diffusing the tin into the copper and reacting the tin with the niobium of the filaments.
Claim 7
Dependent Claim
43 words
The method of claim 4 in which the wire is cabled prior to diffusing the tin into the wire, and in which the diffusion-heating step is carried out at a temperature below the niobium-tin reaction temperature to homogenize the tin throughout the wire.
Claim 8
Dependent Claim
26 words
The method of claim 4 in which the wire is formed around a central strengthening core into a sixstrand cable of about 0.015 inch outside diameter.
Claim 9
Dependent Claim
29 words
The method of claim 4 in which the uncoated wire diameter is between about five and 50 mils and tin coating is between about two and 20 microns thick.
Claim 10
Dependent Claim
16 words
The method of claim 4 in which the nickel or copper layer is formed by electroplating.
Claim 11
Dependent Claim
36 words
The method of claim 4 in which the uncoated wire diameter is about 10 mils, the thickness of the tin coating is about five microns, and the thickness of the nickel layer is about 0.5 micron.
References Cited (Backward Citations)
US3124455A
Cited
US2930106A
Cited
US2995475A
Cited
US3167692A
Cited
US3309179A
Cited
US3429032A
Cited
US3397084A
Cited
US3395040A
Cited
US3525150A
Cited
US3674553A
Cited
US3458293A
Cited
US3595693A
Cited
US3625662A
Cited
US3829963A
Cited
US3838503A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-17 | 1981-04-18 | 1981-10-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-17 | 1985-04-18 | 1985-10-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-17 | 1989-04-18 | 1989-10-18 | $7700.00 | Window Closed / Lapsed |