Patent US4042730A successfully refreshed from Google Patents.
US4042730A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for electroless plating using separate sensitization and activation steps
Assignee: AT&T Inc
•
Filing: 1976-03-29
•
Granted: 1977-08-16
•
Expires: 1996-03-29
Abstract
Abstract A process is described for the electroless deposition of metals on nonmetallic surfaces. After pretreatment of the nonmetallic surface so as to obtain a finish suitable for deposition of sensitizers and activators, the nonmetallic surface is exposed to a sensitizing solution and thereafter in a separate step to an activation solution. The surface is then washed with an aqueous alkaline solution prior to immersion in the electroless plating solution. The separate sensitization and activation steps are particularly suitable where the sensitizing step is also used for pattern generation. The inclusion of the aqueous alkaline wash after the activation step both protects the electroless plating bath from contamination with sensitizer and activator, and also insures a short initition time. Short initiation times are highly desirable especially in the production of electronic circuits because highly uniform metal platings are insured, manufacturing time is considerably reduced and reliability is increased.
Inventors
- 👤 Richard Lewis Cohen
- 👤 Ronald Lee Meek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 04:51
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/28; H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
134 words
A process for electroless deposition of copper on nonmetallic surfaces comprising the steps of: a. preconditioning the nonmetallic surface so as to prepare the surface for a sensitizing and activating procedure; b. exposing the preconditioned surface to a sensitizing solution consisting essentially of an acidified aqueous solution of tin ions; c. activating the sensitized surface by exposing the surface to an acidified solution of palladium ions so as to produce a catalytically active surface; d. exposing the catalytically active surface to an aqueous post-activation solution; and e. exposing said surface to an alkaline electroless copper plating solution; characterized in that the aqueous post activation solution consists essentially of a nonreducing alkaline agent with dissociation constant for the liberation of one hydroxyl ion greater than 10.sup. -5 and concentration range from 0.07 to 0.2 molar.
Claim 2
Dependent Claim
134 words
A process for electroless deposition of copper on nonmetallic surfaces comprising the steps of: a. preconditioning the nonmetallic surface so as to prepare the surface for a sensitizing and activating procedure; b. exposing the preconditioned surface to a sensitizing solution consisting essentially of an acidified aqueous solution of tin ions; c. activating the sensitized surface by exposing the surface to an acidified solution of palladium ions so as to produce a catalytically active surface; d. exposing the catalytically active surface to an aqueous post-activation solution; and e. exposing said surface to an alkaline electroless copper plating solution; characterized in that the aqueous post activation solution consists essentially of a nonreducing alkaline agent with dissociation constant for the liberation of one hydroxyl ion greater than 10.sup. -5 and concentration range from 0.07 to 0.2 molar.
Claim 3
Dependent Claim
11 words
The process of claim 1 where the alkaline agent is NaOH.
Claim 4
Dependent Claim
11 words
The process of claim 1 where the alkaline agent is ammonia.
Claim 5
Dependent Claim
18 words
The process of claim 1 where the concentration of alkaline agent is from 0.1 M to 0.2 M.
Claim 6
Dependent Claim
21 words
The process of claim 1 where the catalytically prepared surface is exposed to the aqueous post-activation solution for approximately 5 minutes.
Claim 7
Dependent Claim
22 words
The process of claim 1 where the sensitizing solution consists essentially of an aqueous solution of stannous chloride acidified with hydrochloric acid.
Claim 8
Dependent Claim
28 words
The process of claim 6 where the concentration of stannous chloride is from 1 to 20 gm/l and of concentrated hydrochloric acid is from 10 to 60 gm/l.
Claim 9
Dependent Claim
22 words
The process of claim 1 where the activating solution consists essentially of an aqueous solution of palladium dichloride acidified with hydrochloric acid.
Claim 10
Dependent Claim
31 words
The process of claim 8 in which the concentration of palladium dichloride is from 0.02 to 2 gm/l and the concentration of concentrated hydrochloric acid is from 0.02 to 20 ml/l.
Claim 11
Dependent Claim
18 words
The process of claim 1 in which the surface is electroplated with copper subsequent to electroless copper plating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-15 | 1981-02-14 | 1981-08-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-15 | 1985-02-14 | 1985-08-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-15 | 1989-02-14 | 1989-08-16 | $7700.00 | Window Closed / Lapsed |