Four-layer trapatt diode and method for making same
Assignee: RCA Corp
•
Filing: 1975-04-30
•
Granted: 1977-07-26
•
Expires: 1995-04-30
Abstract
Abstract A method for making a four-layer P+PNN+ or N+NPP+ diode, and the diode, wherein the impurity profile about the PN junction is optimally graded for TRAPATT operation throughout the span of the avalanche region by ion implantation of the impurities to a depth of 1000A in a semiconductor wafer and wherein these impurities are subsequently thermally diffused.
Inventors
- 👤 Hirohisa Kawamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 15:41
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/21; H10D; H10D8/00; H10D8/40; H10P30/202; H10P30/204; H10P32/00; H10P32/10; H10P32/14; H10P32/1404; H10P32/1406; H10P32/17; H10P32/171
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
207 words
A method for making a diode for optimum operation in the TRAPATT mode, the diode having several layers of a semiconductor including two innermost layers, the two innermost layers forming a PN junction close to a surface of the diode, the diode having an impurity profile about the PN junction in the two innermost layers, the profile exhibiting the same slope on each side of the PN junction, said method comprising the steps of: (a) implanting impurities of a first conductivity type into a lightly doped original layer of a second conductivity type, the original layer being located on a heavily doped semiconductor wafer having impurities of the second conductivity type, up to a density of the order of 5 × 10 16 atoms-cm - 3 ; (b) depositing on the original layer a means for preventing out-diffusion of the implanted impurities; (c) diffusing the implanted impurities into the original layer; (d) simultaneously diffusing the impurities in the heavily doped wafer into the original layer during the diffusion of the implanted impurities whereby the PN junction is formed in the original layer; (e) thereafter removing said means for preventing out-diffusion from said original layer; and (f) diffusing impurities of the first conductivity type into the original layer.
Claim 2
Independent Claim
207 words
A method for making a diode for optimum operation in the TRAPATT mode, the diode having several layers of a semiconductor including two innermost layers, the two innermost layers forming a PN junction close to a surface of the diode, the diode having an impurity profile about the PN junction in the two innermost layers, the profile exhibiting the same slope on each side of the PN junction, said method comprising the steps of: (a) implanting impurities of a first conductivity type into a lightly doped original layer of a second conductivity type, the original layer being located on a heavily doped semiconductor wafer having impurities of the second conductivity type, up to a density of the order of 5 × 10 16 atoms-cm - 3 ; (b) depositing on the original layer a means for preventing out-diffusion of the implanted impurities; (c) diffusing the implanted impurities into the original layer; (d) simultaneously diffusing the impurities in the heavily doped wafer into the original layer during the diffusion of the implanted impurities whereby the PN junction is formed in the original layer; (e) thereafter removing said means for preventing out-diffusion from said original layer; and (f) diffusing impurities of the first conductivity type into the original layer.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein the means for preventing out-diffusion of the implanted impurities comprises an oxide located adjacent the lightly doped original layer.
Claim 4
Dependent Claim
23 words
The method of claim 2, wherein the implanted impurities of the first conductivity type are created by ionic bombardment of like impurity ions.
Claim 5
Dependent Claim
25 words
The method of claim 3, wherein the impurities of the first conductivity type are implanted in the original layer to depth not exceeding approximately 1000A.
Claim 6
Dependent Claim
40 words
The method of claim 4 further comprising the steps of depositing impurities of a first conductivity type on the original layer up to a density of the order of 10 19 atoms/cm - 3 and thermally diffusing the deposited impurities.
Claim 7
Dependent Claim
27 words
The method of claim 5, wherein the step of diffusing the implanted impurities further includes thermally diffusing the implanted impurities over a period of approximately 8 hours.
Claim 8
Dependent Claim
23 words
The method of claim 4, wherein the ionic bombardment occurs at a flux density of approximately 5 × 10 14 ions/cm 2 .
Claim 9
Dependent Claim
23 words
The method of claim 7, wherein the original layer is approximately 12 μm thick and wherein the wafer is approximately 50 μm thick.
Claim 10
Dependent Claim
26 words
The method of claim 8, wherein in the step of implanting impurities, phosphorus ions are implanted into the original layer, the wafer being doped with boron.
Claim 11
Dependent Claim
25 words
The method of claim 8, wherein the step of implanting impurities, boron ions are implanted into the original layer, the wafer being doped with phosphorus.
References Cited (Backward Citations)
US3745070A
Cited
US3660171A
Cited
US3758875A
Cited
US3638300A
Cited
US3891468A
Cited
US3926693A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-25 | 1981-01-24 | 1981-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-25 | 1985-01-24 | 1985-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-25 | 1989-01-24 | 1989-07-26 | $7700.00 | Window Closed / Lapsed |