Method of preparing high capacity nickel electrode powder
Assignee: Westinghouse Electric Corp
•
Filing: 1976-05-24
•
Granted: 1977-06-14
•
Expires: 1996-05-24
Abstract
Abstract A battery electrode plate is made by loading a supporting porous metallic plaque with active battery material made by: (1) hydrolyzing the reaction product of a fuse-melted starting material comprising an admixture of nickel oxide, sodium peroxide and an amount of an oxide containing, alkali metal, non-reactive flux material effective to allow a melt-fusion reaction of the starting material at temperatures of between about 650° C to about 925° C, the hydrolyzed solid reaction product containing electrochemically active nickel hydrated oxides and hydroxide forms, (2) if desirable, drying the product below about 65° C, and (3) preferably adding, at some step in the method, an amount of cobalt containing additive effective to provide about 2 wt.% to about 10 wt.% cobalt in the active battery material based on nickel oxide plus cobalt content.
Inventors
- 👤 John F. Jackovitz
- 👤 Earl A. Pantier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 05:23
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/36; H01M4/48; H01M4/52; H01M4/24; H01M4/32; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
180 words
A method of producing a battery electrode plate containing active battery material, comprising the steps of: a. mixing NiO and Na 2 O 2 in a weight ratio of NiO:Na 2 O 2 of between about 1:1.20 to about 1:1.60 with an amount of an oxygen containing alkali metal fluxing material selected from the group consisting of alkali metal molybdates, alkali metal tungstates, alkali metal vanadates, alkali metal carbonates, alkali metal nitrates and mixtures thereof, effective to allow fuse-melting of the NiO and Na 2 O 2 at temperatures of between about 650° C to about 925° C; b. heating the mixture of NiO, Na 2 O 2 and fluxing material between about 650° C to about 925° C to melt-fuse the mixture and to form NaNiO 2 ; c. hydrolyzing the NaNiO 2 in water at between about 20° C to about 95° C to form active battery material; d. maintaining the activity of the battery material by maintaining the temperature of the material below about 65° C; and e. applying the battery material to a porous metallic plaque.
Claim 2
Independent Claim
180 words
A method of producing a battery electrode plate containing active battery material, comprising the steps of: a. mixing NiO and Na 2 O 2 in a weight ratio of NiO:Na 2 O 2 of between about 1:1.20 to about 1:1.60 with an amount of an oxygen containing alkali metal fluxing material selected from the group consisting of alkali metal molybdates, alkali metal tungstates, alkali metal vanadates, alkali metal carbonates, alkali metal nitrates and mixtures thereof, effective to allow fuse-melting of the NiO and Na 2 O 2 at temperatures of between about 650° C to about 925° C; b. heating the mixture of NiO, Na 2 O 2 and fluxing material between about 650° C to about 925° C to melt-fuse the mixture and to form NaNiO 2 ; c. hydrolyzing the NaNiO 2 in water at between about 20° C to about 95° C to form active battery material; d. maintaining the activity of the battery material by maintaining the temperature of the material below about 65° C; and e. applying the battery material to a porous metallic plaque.
Claim 3
Dependent Claim
103 words
The method of claim 1 wherein the fluxing material is selected from the group consisting of Na 2 MoO 4 , K 2 MoO 4 , Li 2 MoO 4 , Na 2 WO 4 , K 2 WO 4 , Li 2 WO 4 , Na 3 VO 4 , K 3 VO 4 , Li 3 VO 4 , Na 2 CO 3 , K 2 CO 3 , Li 2 CO 3 , NaNO 3 , KNO 3 , LiNO 3 and mixtures thereof, cobalt is added to the materials, and as a last step the fluxing material is recovered.
Claim 4
Dependent Claim
48 words
The method of claim 2 wherein cobalt additive selected from the group consisting of Co, Co 2 O 3 , Co 3 O 4 , CoO and mixtures thereof is added in step (a) and the weight ratio of NiO:fluxing material is between about 1:0.5 to about 1:3.0.
Claim 5
Dependent Claim
23 words
The method of claim 2 wherein cobalt additive as cobalt hydroxide is added after hydrolysis of the reaction product comprising NaNiO 2 .
Claim 6
Dependent Claim
26 words
The method of claim 2 wherein cobalt additive as a water soluble cobalt salt is added during hydrolysis of the reaction product comprising NaNiO 2 .
Claim 7
Dependent Claim
18 words
The method of claim 2 wherein cobalt additive as a water soluble cobalt salt is added after hydrolysis.
Claim 8
Dependent Claim
26 words
The method of claim 2 wherein cobalt additive as a water soluble cobalt salt is added after applying the battery material to the porous metallic plaque.
Claim 9
Dependent Claim
38 words
The method of claim 2 wherein the active battery material contains from about 0.5 to about 3 wt.% unreacted NaNiO 2 and the active battery material is dried between about 15° C to 65° C in step (d).
Claim 10
Dependent Claim
32 words
The method of claim 8, wherein the mixture in step (b) is heated at a temperature of between about 700° C to about 900° C for between about 1/2 to 5 hours.
Claim 11
Dependent Claim
21 words
The method of claim 8, wherein the reaction product is cooled to a temperature below about 95° C before step (c).
Claim 12
Dependent Claim
27 words
The method of claim 8, wherein the active battery material comprises Ni hydroxide forms and the active battery material is washed after hydrolysis until neutral to litmus.
Claim 13
Dependent Claim
43 words
The method of claim 11, wherein the active battery material Ni hydroxide forms comprise a material having a stoichimetry of Ni 3 O 4 .sup.. 2H 2 O, and the active battery material is applied to the metallic plaque in aqueous slurry form.
Claim 14
Dependent Claim
23 words
The method of claim 12, wherein the metallic plaque is between about 90% to 95% porous and comprises relatively smooth contacting metal fibers.
Claim 15
Dependent Claim
24 words
The method of claim 13, wherein the metal fibers are diffusion bonded, wherein there is only an interdiffusion of atoms across the fibers interface.
Claim 16
Independent Claim
158 words
A method of making an active battery electrode powder, comprising the steps of: a. mixing an admixture of nickel oxide and Na 2 O 2 , in a weight ratio of nickel oxide:Na 2 O 2 of between about 1:1.20 to about 1:1.60 with an amount of an oxygen containing, alkali metal fluxing material selected from the group consisting of alkali metal molybdates, alkali metal tungstates, alkali metal vanadates, alkali metal carbonates, alkali metal nitrates and mixtures thereof, effective to allow fuse-melting of the nickel oxide and Na 2 O 2 at temperatures between about 650° C to about 925° C; b. heating the admixture at a reaction temperature of between about 650° C to about 925° C, to melt-fuse the admixture and form a reaction product comprising NaNiO 2 ; and c. hydrolyzing the reaction product comprising NaNiO 2 in water at between 20° C to about 95° C, forming a battery material comprising Ni hydroxide forms.
Claim 17
Independent Claim
158 words
A method of making an active battery electrode powder, comprising the steps of: a. mixing an admixture of nickel oxide and Na 2 O 2 , in a weight ratio of nickel oxide:Na 2 O 2 of between about 1:1.20 to about 1:1.60 with an amount of an oxygen containing, alkali metal fluxing material selected from the group consisting of alkali metal molybdates, alkali metal tungstates, alkali metal vanadates, alkali metal carbonates, alkali metal nitrates and mixtures thereof, effective to allow fuse-melting of the nickel oxide and Na 2 O 2 at temperatures between about 650° C to about 925° C; b. heating the admixture at a reaction temperature of between about 650° C to about 925° C, to melt-fuse the admixture and form a reaction product comprising NaNiO 2 ; and c. hydrolyzing the reaction product comprising NaNiO 2 in water at between 20° C to about 95° C, forming a battery material comprising Ni hydroxide forms.
Claim 18
Dependent Claim
165 words
The method of claim 15 wherein the fluxing material is selected from the group consisting of Na 2 MoO 4 , K 2 MoO 4 , Li 2 MoO 4 , Na 2 WO 4 , K 2 WO 4 , Li 2 WO 4 , Na 3 VO 4 , K 3 VO 4 , Li 3 VO 4 , Na 2 CO 3 , K 2 CO 3 , Li 2 CO 3 , NaNO 3 , KNO 3 , LiNO 3 and mixtures thereof, cobalt additive, selected from the group consisting of Co, Co 2 O 3 , Co 3 O 4 and CoO and their mixtures is mixed with the nickel oxide and Na 2 O 2 in step (a) providing a battery material with about 2 wt.% to about 10 wt.% Co based on NiO plus Co content, the battery material is dried between about 15° C to about 65° C after step (c), and the fluxing material is recovered.
Claim 19
Dependent Claim
39 words
The method of claim 16 wherein the mixture of nickel oxide, cobalt additive and Na 2 O 2 is heated at a temperature of between about 700° C to about 900° C for between about 1/2 to 5 hours.
Claim 20
Dependent Claim
37 words
The method of claim 16 wherein the Ni hydroxide forms comprise a material having a stoichiometry of Ni 3 O 4 .sup.. 2H 2 O, said material after drying being in crystalline layer form with interlaminar water.
Claim 21
Dependent Claim
31 words
The method of claim 18 wherein the crystalline structure of the material after drying has a center of symmetry and layer like --O--Ni--O-- structure with water molecules dispersed in interlaminar positions.
Claim 22
Dependent Claim
44 words
The method of claim 18 wherein the fluxing material is selected from the group consisting of Na 2 MoO 4 , K 2 MoO 4 , Na 2 CO 3 , K 2 CO 3 , NaNO 3 , KNO 3 and mixtures thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-13 | 1980-12-13 | 1981-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-13 | 1984-12-13 | 1985-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-13 | 1988-12-13 | 1989-06-14 | $7700.00 | Window Closed / Lapsed |