Method of preparing high capacity nickel electrode powder
Assignee: Westinghouse Electric Corp
•
Filing: 1975-03-13
•
Granted: 1976-03-02
•
Expires: 1995-03-13
Abstract
Abstract An electrode plate is made by loading a supporting porous metallic plaque with active battery material made by: (1) hydrolyzing the reaction product of a starting material comprising an admixture of Ni oxide and effective amounts of sodium peroxide fused at temperatures between about 800 DEG C-1150 DEG C, the hydrolyzed solid reaction product containing electrochemically active Ni hydrated oxides and hydroxide forms, (2) if desirable, drying the product below about 65 DEG C, and (3) adding, at some step in the method, an amount of cobalt containing additive effective to provide about 2-12 wt% total Co in the active battery material based on Ni oxide plus Co content.
Inventors
- 👤 John F. Jackovitz
- 👤 Earl A. Pantier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:41
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/24; H01M4/32; H01M4/36; H01M4/48; H01M4/52; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
125 words
A method of producing a battery electrode plate containing active battery material, comprising the steps of: a. mixing NiO with Na 2 O 2 in a weight ratio of NiO:Na 2 O 2 of between about 1:1.35 to about 1:2.1; b. heating the mixture of NiO and Na 2 O 2 between about 800°C - 1150°C, for about 1/2 hour to 8 hours, to melt the mixture and to form NaNiO 2 ; c. hydrolyzing the NaNiO 2 in water at between about 20°C-95°C to form active battery material and then washing the active battery material; d. maintaining the activity of the battery material by maintaining the temperature of the material below about 65°C; and e. applying the battery material to a porous metallic plaque.
Claim 2
Independent Claim
125 words
A method of producing a battery electrode plate containing active battery material, comprising the steps of: a. mixing NiO with Na 2 O 2 in a weight ratio of NiO:Na 2 O 2 of between about 1:1.35 to about 1:2.1; b. heating the mixture of NiO and Na 2 O 2 between about 800°C - 1150°C, for about 1/2 hour to 8 hours, to melt the mixture and to form NaNiO 2 ; c. hydrolyzing the NaNiO 2 in water at between about 20°C-95°C to form active battery material and then washing the active battery material; d. maintaining the activity of the battery material by maintaining the temperature of the material below about 65°C; and e. applying the battery material to a porous metallic plaque.
Claim 3
Dependent Claim
39 words
The method of claim 1 wherein the NiO is substantially pure, and cobalt, selected from the group consisting of Co, Co 2 O 3 , Co 3 O 4 and CoO and their mixtures is added to the materials.
Claim 4
Dependent Claim
31 words
The method of claim 1 wherein the NiO is substantially pure, and cobalt additive as substantially pure cobalt hydroxide is added after hydrolysis of the reaction product comprising NaNiO 2 .
Claim 5
Dependent Claim
26 words
The method of claim 1 wherein cobalt additive as a water soluble cobalt salt is added during hydrolysis of the reaction product comprising NaNiO 2 .
Claim 6
Dependent Claim
18 words
The method of claim 1 wherein cobalt additive as a water soluble cobalt salt is added after hydrolysis
Claim 7
Dependent Claim
26 words
The method of claim 1 wherein cobalt additive as a water soluble cobalt salt is added after applying the battery material to the porous metallic plaque.
Claim 8
Independent Claim
179 words
A method of producing a battery electrode plate containing active battery material, comprising the steps of: a. mixing an admixture of NiO and cobalt material selected from the group consisting of Co, Co 2 O 3 , Co 3 O 4 and CoO and their mixtures and Na 2 O 2 , wherein the weight ratio of NiO:Na 2 O 2 is between about 1:1.35 to about 1:2.1 and the amount of Co in the cobalt material is between about 2-12 wt% based on NiO plus Co content; b. heating the admixture at a temperature between about 800°C-1150°C for about one-half hour to 8 hours to melt the admixture and provide a reaction product consisting essentially of NaNiO 2 and then cooling the reaction product NaCoO 2 ; c. hydrolyzing the reaction product, forming an active battery material; d. washing the active battery material; and then maintaining the activity of the battery material by maintaining the temperature of the material below about 65°C.; and e. applying the active battery material to a metallic plaque to provide a battery electrode.
Claim 9
Independent Claim
179 words
A method of producing a battery electrode plate containing active battery material, comprising the steps of: a. mixing an admixture of NiO and cobalt material selected from the group consisting of Co, Co 2 O 3 , Co 3 O 4 and CoO and their mixtures and Na 2 O 2 , wherein the weight ratio of NiO:Na 2 O 2 is between about 1:1.35 to about 1:2.1 and the amount of Co in the cobalt material is between about 2-12 wt% based on NiO plus Co content; b. heating the admixture at a temperature between about 800°C-1150°C for about one-half hour to 8 hours to melt the admixture and provide a reaction product consisting essentially of NaNiO 2 and then cooling the reaction product NaCoO 2 ; c. hydrolyzing the reaction product, forming an active battery material; d. washing the active battery material; and then maintaining the activity of the battery material by maintaining the temperature of the material below about 65°C.; and e. applying the active battery material to a metallic plaque to provide a battery electrode.
Claim 10
Dependent Claim
43 words
The method of claim 7, wherein the reaction product is hydrolyzed in water, the active battery material contains from about 0.5 to 5 wt% unreacted NaNiO 2 and NaCoO 2 and the active battery material is dried between about 15°C-65°C after step (d).
Claim 11
Dependent Claim
44 words
The method of claim 7, wherein the admixture in step (b) is heated at a temperature of between about 850°C-1100°C for between about 1/2-8 hours to melt the mixture and the NiO, cobalt material and Na 2 O 2 are in substantially pure form.
Claim 12
Dependent Claim
35 words
The method of claim 8, wherein the reaction product is cooled to a temperature below about 95°C before step (c), and the water used in the hydrolysis step has a temperature of between about 20°C-95°C.
Claim 13
Dependent Claim
67 words
The method of claim 8, wherein the reaction product is cooled to between about 20°-95°C before step (c), the water used in the hydrolysis step has a temperature of between about 20°C-35°C, the active battery material comprises Ni hydroxide forms which have a weight ratio of Ni (II) hydroxide:Ni (III) hydroxide of over 1:2 and the active battery material is washed after hydrolysis until neutral to litmus.
Claim 14
Dependent Claim
48 words
The method of claim 11, wherein the reaction product is hydrolyzed by immersion in water and the NiO, cobalt material and Na 2 O 2 contain no more than 5% impurities selected from the group consisting of mercury, silver, cadmium, lead, magnesium, chromium, calcium, zirconium and barium compounds.
Claim 15
Dependent Claim
58 words
The method of claim 11, wherein the amount of Co in the mixture of step (a) is between about 4-8 wt%, the active battery material Ni hydroxide forms comprise a material having a stoichimetry of Ni 3 O 4 . 2H 2 O, and the active battery material is applied to the metallic plaque in aqueous slurry form.
Claim 16
Dependent Claim
20 words
The method of claim 13, wherein the metallic plaque is between 90-95% porous and comprises relatively smooth contacting metal fibers.
Claim 17
Dependent Claim
26 words
The method of claim 14, wherein the metal fibers are diffusion bonded before coating, wherein there is only an interdiffusion of atoms across the fibers interface.
References Cited (Backward Citations)
US3600227A
Cited
US3579385A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-02 | 1979-09-01 | 1980-03-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-02 | 1983-09-01 | 1984-03-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-02 | 1987-09-01 | 1988-03-02 | $7700.00 | Window Closed / Lapsed |