US4028223A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Guard beds in hydrocarbon conversion with an acidic multimetallic catalytic composite
Assignee: Honeywell UOP LLC
•
Filing: 1975-08-11
•
Granted: 1977-06-07
•
Expires: 1995-08-11
Abstract
Abstract Hydrocarbons are converted by contacting a hydrocarbon charge stock and a hydrogen stream at hydrocarbon conversion conditions, in a reaction zone maintained in a substantially sulfur- and water-free condition by the use of at least one guard bed, with an acidic multimetallic catalytic composite comprising a combination of catalytically effective amounts of a platinum group component, a tin component, a cobalt component, and a halogen component with a porous carrier material. The platinum group component, tin component, cobalt component, and halogen component are present in the multimetallic catalyst in amounts respectively, calculated on an elemental basis, corresponding to about 0.01 to about 2 wt. % platinum group metal, about 0.01 to about 5 wt. % tin, about 0.5 to about 5 wt. % cobalt, and about 0.1 to about 3.5 wt. % halogen. Moreover, these metallic components are uniformly dispersed throughout the porous carrier material in carefully controlled oxidation states such that substantially all of the platinum group metal is present therein in the elemental metallic state, substantially all of the catalytically available cobalt component is present in the elemental metallic state or in a state which is reducible to the elemental metallic state under hydrocarbon conversion conditions or in a mixture of these states, while substantially all of the tin is present therein an oxidation state above that of the elemental metal. A specific example of the type of hydrocarbon conversion process disclosed is a process for the catalytic reforming of a low-octane gasoline fraction wherein the gasoline fraction and a hydrogen stream are contacted under a substantially sulfur- and water-free condition with the acidic multimetallic catalyst disclosed herein at reforming conditions. The sulfur- and water-selective guard bed can be used exclusively on the hydrocarbon charge stock when the hydrocarbon stream is autogenously produced or it can be used to treat a mixture of the hydrocarbon charge stock and the hydrogen stream. In another mode of operation, separate guard beds can be used on the input hydrocarbon charge stock and on the input hydrogen stream.
Inventors
- 👤 John C. Hayes
- 👤 Ernest L. Pollitzer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:14
CPC Classifications
B; B01; B01J; B01J27/00; B01J27/06; B01J27/08; B01J23/00; B01J23/70; B01J23/89; B01J23/8933; B01J23/8966; C; C10; C10G; C10G35/00; C10G35/04; C10G35/06; C10G35/085; C10G35/09; C10G47/00; C10G47/02; C10G47/10; C10G47/12; C10G47/14; C07; C07C; C07C2521/00; C07C2521/02; C07C2521/04; C07C2523/00; C07C2523/02; C07C2523/04; C07C2523/14; C07C2523/38; C07C2523/40; C07C2523/42; C07C2523/44; C07C2523/46; C07C2523/70; C07C2523/74; C07C2523/75; C07C2523/89
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
190 words
A process for converting a hydrocarbon charge stock which comprises contacting the hydrocarbon charge stock and a hydrogen stream at hydrocarbon conversion conditions, in a reaction zone maintained in a substantially sulfur- and water-free condition, with an acidic catalytic composite comprising a porous carrier material containing, on an elemental basis, about 0.01 to about 2 wt. % platinum group metal, about 0.5 to about 5 wt. % cobalt, about 0.01 to about 5 wt. % tin, and about 0.1 to about 3.5 wt. % halogen, wherein the platinum group metal, catalytically available cobalt, and tin are uniformly dispersed throughout the porous carrier material, wherein substantially all of the platinum group metal is present in the elemental metallic state, wherein substantially all of the tin is present in an oxidation state above that of the elemental metal wherein the average crystalline size of said tin is less than 100 Angstroms in maximum dimension, and wherein substantially all of the catalytically available cobalt is present in the elemental metallic state or in a state which is reducible to the elemental metallic under hydrocarbon conversion conditions or in a mixture of these states.
Claim 2
Dependent Claim
190 words
A process for converting a hydrocarbon charge stock which comprises contacting the hydrocarbon charge stock and a hydrogen stream at hydrocarbon conversion conditions, in a reaction zone maintained in a substantially sulfur- and water-free condition, with an acidic catalytic composite comprising a porous carrier material containing, on an elemental basis, about 0.01 to about 2 wt. % platinum group metal, about 0.5 to about 5 wt. % cobalt, about 0.01 to about 5 wt. % tin, and about 0.1 to about 3.5 wt. % halogen, wherein the platinum group metal, catalytically available cobalt, and tin are uniformly dispersed throughout the porous carrier material, wherein substantially all of the platinum group metal is present in the elemental metallic state, wherein substantially all of the tin is present in an oxidation state above that of the elemental metal wherein the average crystalline size of said tin is less than 100 Angstroms in maximum dimension, and wherein substantially all of the catalytically available cobalt is present in the elemental metallic state or in a state which is reducible to the elemental metallic under hydrocarbon conversion conditions or in a mixture of these states.
Claim 3
Dependent Claim
122 words
A process as defined in claim 1 wherein the sulfur- and water-free condition is achieved and maintained by treating the hydrocarbon charge stock, prior to passage of same into the reaction zone, with a first guard bed containing a sulfur- and water-selective adsorbent at first adsorption conditions effective to produce a treated charge stock containing less than 1 wt. ppm. sulfur and less than 1 wt. ppm. of water, and by treating the hydrogen stream, prior to passage of same into the reaction zone, with a second guard bed containing a sulfur- and water-selective adsorbent at second adsorption conditions effective to form a treated hydrogen stream containing less than 1 vol. ppm. of sulfur and less than 1 vol. ppm. of water.
Claim 4
Dependent Claim
35 words
A process as defined in claim 2 wherein at least one of said guard beds contains an adsorbent comprising high surface area particles of a reactive metal having a high affinity for water and sulfur.
Claim 5
Dependent Claim
30 words
A process as defined in claim 3 wherein the reactive metal is selected from the group consisting of potassium, sodium, magnesium, aluminum, zinc, iron, nickel, cobalt, copper, and mixtures thereof.
Claim 6
Dependent Claim
26 words
A process as defined in claim 2 wherein at least one of said guard beds contains an adsorbent comprising particles of a sulfur- and water-selective clay.
Claim 7
Dependent Claim
30 words
A process as defined in claim 2 wherein at least one of said guard beds comprises a mixture of particles of a sulfur-accepting reactive metal oxide and of a desiccant.
Claim 8
Dependent Claim
28 words
A process as defined in claim 2 wherein at least one of said guard beds comprises particles of a sulfur-accepting reactive metal oxide followed by particles of desiccant.
Claim 9
Dependent Claim
36 words
A process as defined in claim 6 wherein the sulfur-accepting reactive metal oxide is selected from the group consisting of alumina, zinc oxide, copper oxide, magnesium oxide, iron oxide, cobalt oxide, nickel oxide, and mixtures thereof.
Claim 10
Dependent Claim
89 words
A process as defined in claim 1 wherein substantially all of the hydrogen stream is obtained by recycling a portion of the effluent from the reaction zone and wherein the sulfur- and water-free condition is achieved and maintained by treating the hydrocarbon charge stock, prior to passage of same into the reaction zone, with a guard bed containing a sulfur- and water-selective adsorbent at adsorption conditions effective to produce a treated charge stock containing less than 1 wt. ppm. of sulfur and less than 1 wt. ppm. of water.
Claim 11
Dependent Claim
27 words
A process as defined in claim 9 wherein the adsorbent comprises high surface area particles of a reactive metal having a high affinity for water and sulfur.
Claim 12
Dependent Claim
24 words
A process as defined in claim 9 wherein the adsorbent comprises particles of a sulfur-accepting reactive metal oxide followed by particles of a desiccant.
Claim 13
Dependent Claim
86 words
A process as defined in claim 1 wherein a mixture of the hydrocarbon charge stock and the hydrogen stream is formed outside of the reaction zone and the mixture is thereafter passed into the reaction zone and wherein the sulfur- and water-free condition is achieved and maintained by treating the mixture with a guard bed containing a sulfur- and water-selective adsorbent at adsorption conditions effective to produce a treated mixture containing less than 1 wt. ppm. of sulfur and less than 1 wt. ppm. of water.
Claim 14
Dependent Claim
26 words
A process as defined in claim 1 wherein substantially all of the catalytically available cobalt contained in the composite is present in the elemental metallic state.
Claim 15
Dependent Claim
22 words
A process as defined in claim 1 wherein substantially all of the tin is present in the catalytic composite as tin oxide.
Claim 16
Dependent Claim
44 words
A process as defined in claim 1 wherein the composite contains about 0.05 to about 1 wt. % platinum, about 0.5 to about 2 wt. % cobalt, about 0.05 to about 1 wt. % tin, and about 0.5 to about 1.5 wt. % halogen.
Claim 17
Dependent Claim
44 words
A process as defined in claim 1 wherein the type of hydrocarbon conversion is catalytic reforming of a gasoline fraction to produce a high octane reformate, wherein the hydrocarbon is contained in the gasoline fraction, and wherein the hydrocarbon conversion conditions are reforming conditions.
Claim 18
Dependent Claim
58 words
A process as defined in claim 16 wherein the reforming conditions include a temperature of about 800° to about 1100° F., a pressure of about 0 to about 1000 psig., a liquid hourly space velocity of about 0.1 to about 10 hr..sup. -1 , and a mole ratio of hydrogen to hydrocarbon of about 1:1 to about 20:1.
Claim 19
Dependent Claim
21 words
A process as defined in claim 16 wherein the reforming conditions include a pressure of about 100 to about 450 psig.
References Cited (Backward Citations)
US2911357A
Cited
US3063933A
Cited
US3189539A
Cited
US3576766A
Cited
US3830727A
Cited
US3644198A
Cited
US3844938A
Cited
US3847794A
Cited
US3775300A
Cited
US3881696A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-06 | 1980-12-06 | 1981-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-06 | 1984-12-06 | 1985-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-06 | 1988-12-06 | 1989-06-07 | $7700.00 | Window Closed / Lapsed |