Reduction of metal halides
Assignee: Amax Specialty Metals Inc
•
Filing: 1974-09-06
•
Granted: 1976-06-29
•
Expires: 1994-09-06
Abstract
Abstract A process for producing zirconium or hafnium metals by the reduction of their tetrachlorides with an excess of molten magnesium is provided with increased reactor capacity, increased yield per run, and improved economy by virtue of withdrawal of magnesium chloride as formed during the reaction, which permits subsequent separation and recovery of excess magnesium from the product by a simple distillation and in a form suitable for direct utilization in a second or subsequent reduction. Apparatus is provided which accommodates both the reduction process and the distillation in convenient fashion.
Inventors
- 👤 Donald R. Spink
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 20:10
CPC Classifications
C; C22; C22B; C22B34/00; C22B34/10; C22B34/14; C22B5/00; C22B5/02; C22B5/04
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
241 words
A process for the production of a metal selected from the group consisting of zirconium and hafnium from its tetrahalide comprising: a. reducing the metal tetrahalide with a stoichiometric excess of magnesium in a inert atmosphere and at an elevated temperature in a first retort having an upper portion and a lower first crucible portion; b. withdrawing magnesium halide from said first retort substantially as formed during the reaction while continuously maintaining a protection cover of magnesium chloride over the reduced metal; c. the said reduced metal being deposited in the first crucible and containing excess magnesium and entrained magnesium chloride; d. a reaction vessel having an upper portion and a lower portion; e. removing said first crucible from the first retort and placing it inverted in the upper portion of said reaction vessel; f. inserting in the lower portion of the reaction vessel a second retort having an upper portion and a lower second crucible portion; g. heating the upper portion of the reaction vessel and vacuum distilling off the excess magnesium and entrained magnesium halide from the reduced metal in the first crucible; h. maintaining the lower portion of the reaction vessel at a lower temperature to condense the vapors of magnesium and magnesium chloride; i. passing the magnesium and magnesium chloride into the second retort from the first crucible; and j. employing said second retort in a subsequent reduction of said metal halides as in step (a) above.
Claim 2
Dependent Claim
241 words
A process for the production of a metal selected from the group consisting of zirconium and hafnium from its tetrahalide comprising: a. reducing the metal tetrahalide with a stoichiometric excess of magnesium in a inert atmosphere and at an elevated temperature in a first retort having an upper portion and a lower first crucible portion; b. withdrawing magnesium halide from said first retort substantially as formed during the reaction while continuously maintaining a protection cover of magnesium chloride over the reduced metal; c. the said reduced metal being deposited in the first crucible and containing excess magnesium and entrained magnesium chloride; d. a reaction vessel having an upper portion and a lower portion; e. removing said first crucible from the first retort and placing it inverted in the upper portion of said reaction vessel; f. inserting in the lower portion of the reaction vessel a second retort having an upper portion and a lower second crucible portion; g. heating the upper portion of the reaction vessel and vacuum distilling off the excess magnesium and entrained magnesium halide from the reduced metal in the first crucible; h. maintaining the lower portion of the reaction vessel at a lower temperature to condense the vapors of magnesium and magnesium chloride; i. passing the magnesium and magnesium chloride into the second retort from the first crucible; and j. employing said second retort in a subsequent reduction of said metal halides as in step (a) above.
Claim 3
Dependent Claim
43 words
The method of claim 1 wherein said second retort contains a quantity of magnesium to provide a heat sink to accelerate the distillation and to provide together with the recovered excess magnesium sufficient magnesium necessary for the subsequent reduction of the metal halides.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-29 | 1979-12-29 | 1980-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-29 | 1983-12-29 | 1984-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-29 | 1987-12-29 | 1988-06-29 | $7700.00 | Window Closed / Lapsed |