Carbon-containing molecular sieves
Assignee: Bergwerksverband GmbH
•
Filing: 1974-02-21
•
Granted: 1976-06-01
•
Expires: 1994-02-21
Abstract
Abstract Process for preparing carbon-containing molecular sieves adapted for separating small molecular gases, in particular oxygen, from nitrogen, which comprises treating coke having a content of volatile components of up to 5% at 600° - 900°C with a hydrocabon which splits off carbon whereby the split-off carbon is deposited in the carbon framework of the coke thereby narrowing the existing pores.
Inventors
- 👤 Heinrich Munzner
- 👤 Heinrich Heimbach
- 👤 Werner Korbacher
- 👤 Werner Peters
- 👤 Harald Juntgen
- 👤 Karl Knoblauch
- 👤 Dieter Zundorf
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:52
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/02; C; C01; C01B; C01B32/00; C01B32/30; C01B32/306; C01B2210/00; C01B2210/0043; C01B2210/0045
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
130 words
A molecular sieve which adsorbs a gas of a first atomic or molecular size more readily than a gas of a larger second atomic or molecular size, said molecular sieve comprising coke having carbon deposited in the pores to reduce the pore size to an effective size less than about 0.3 millimicrons, and said molecular sieve being capable of adsorbing oxygen so much more readily than nitrogen that when air is passed through a confining space, having a volume of substantially 1 liter and substantially filled with said molecular sieve, for a period of about 1 minute and at a velocity of about 30 centimeters per second, subsequent desorption of the thus-adsorbed gas from said molecular sieve yields a gas containing a minimum of about 35 volume percent of oxygen.
Claim 2
Dependent Claim
130 words
A molecular sieve which adsorbs a gas of a first atomic or molecular size more readily than a gas of a larger second atomic or molecular size, said molecular sieve comprising coke having carbon deposited in the pores to reduce the pore size to an effective size less than about 0.3 millimicrons, and said molecular sieve being capable of adsorbing oxygen so much more readily than nitrogen that when air is passed through a confining space, having a volume of substantially 1 liter and substantially filled with said molecular sieve, for a period of about 1 minute and at a velocity of about 30 centimeters per second, subsequent desorption of the thus-adsorbed gas from said molecular sieve yields a gas containing a minimum of about 35 volume percent of oxygen.
Claim 3
Dependent Claim
36 words
A molecular sieve as defined in claim 1, wherein said coke is impregnated with finely dispersed carbon deposited in said pores, said carbon being effective for reducing the effective size of said openings of said pores.
Claim 4
Dependent Claim
13 words
A molecular sieve as defined in claim 1, wherein said coke is particulate.
Claim 5
Dependent Claim
23 words
A molecular sieve as defined in claim 3, wherein said coke comprises particles having a particle size between substantially 0.1 and 20 millimeters.
Claim 6
Dependent Claim
23 words
A molecular sieve as defined in claim 2, wherein said coke comprises particles having a particle size between substantially 0.1 and 20 millimeters.
Claim 7
Dependent Claim
105 words
A molecular sieve comprising interconnected coke particles having particle sizes between substantially 0.1 and 20 millimeters and constituting a porous lattice; and finely dispersed carbon deposited in the pores of said lattice and reducing the average effective size of the pores to less than 0.3 millimicrons so that, when air is passed through the pores of the molecular sieve, oxygen having a molecular diameter of less than 0.3 millimicrons is more readily adsorbed by the molecular sieve than other components of air having larger atomic or molecular diameters whereby the gas desorbed from a saturated molecular sieve contains at least 35 volume percent of oxygen.
Claim 8
Dependent Claim
105 words
A molecular sieve comprising interconnected coke particles having particle sizes between substantially 0.1 and 20 millimeters and constituting a porous lattice; and finely dispersed carbon deposited in the pores of said lattice and reducing the average effective size of the pores to less than 0.3 millimicrons so that, when air is passed through the pores of the molecular sieve, oxygen having a molecular diameter of less than 0.3 millimicrons is more readily adsorbed by the molecular sieve than other components of air having larger atomic or molecular diameters whereby the gas desorbed from a saturated molecular sieve contains at least 35 volume percent of oxygen.
Claim 9
Dependent Claim
105 words
A molecular sieve produced by heating coke particles having a size between substantially 0.1 and 20 millimeters and a volatile components content of at most about 5 percent in an inert atmosphere at a temperature between substantially 600° and 900°C while a gaseous stream of a carbonaceous substance which splits off carbon at said temperature is passed into contact with said coke particles for such a period between about 1 and 60 minutes that the carbon that is thus split off is deposited in the pores of said coke particles and reduces the effective average size of said pores to less than about 0.3 millimicrons.
Claim 10
Dependent Claim
105 words
A molecular sieve produced by heating coke particles having a size between substantially 0.1 and 20 millimeters and a volatile components content of at most about 5 percent in an inert atmosphere at a temperature between substantially 600° and 900°C while a gaseous stream of a carbonaceous substance which splits off carbon at said temperature is passed into contact with said coke particles for such a period between about 1 and 60 minutes that the carbon that is thus split off is deposited in the pores of said coke particles and reduces the effective average size of said pores to less than about 0.3 millimicrons.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-01 | 1979-12-01 | 1980-06-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-01 | 1983-12-01 | 1984-06-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-01 | 1987-12-01 | 1988-06-01 | $7700.00 | Window Closed / Lapsed |